CO2 Gas shielded arc welding wire(stone bridge brand with SGS)

AWS ER70S-6 co2 welding wire
1CO2/Mig gas welding wire ER70S-6
2Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS
Supplier:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand and Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice




Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
Features:
1) Our wire is copper coated solid wire for CO2 welding for general engineering and structural application
2) Gives spatter-free welding with CO2 gas and Ar + CO2gas mixtures
3) The weld deposit is free from porosities with very smooth and uniform weld bead
4) Size (diameter): 0.6 - 2.0mm
Packing:
1) 5kg / 12.5kg / 13.5kg / 15kg precision layer wound plastic spools
2) Sealed in moisture-proof air tight plastic bag and cartons with silica
gel drying agent to prevent corrosion and rust, increase shelf life of
wires and cartons on the pallet

co2 Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20