Submerged Arc Welding Wire

Submerged Arc Welding Wire
Brand: "M&R"

Submerged Arc Welding Wire of Carbon Steel and Low-alloy Steel
Features:stable electric arc, low splashing, high deposition
Submerged Arc Welding Wire of Carbon Steel and Low-alloy Steel
Application:
H08A
For general sheet metal, boilers and tube plate and angle butt joint welding
H08MnA
For general sheet metal, boilers and tube plate and angle butt joint welding
H10Mn2
Plate for a single wire, double wire and multi-layer multi-wire welding as well as girth
H10MnSi
welding important low carbon steel and low alloy steel structures
H08Mn2SiA
welding important low carbon steel and low steel structures
H08MnMoA H08Mn2MoA
Welding intensity level corresponding low-alloy steel such as transportation equipment used for lifting vessels, vehicles, construction machinery, power plants, petrochemical industry, bridges, boilers and pressure vessels, steel frame
Standards:GB/T 8110-2008;AWS A5. 28M: 2005

Submerged Arc Welding Wire

Submerged Arc Welding Wire
1) Wire Diameter: 0.8-1.6mm;
2) ER70S-6, ER49-1 and etc;
3) ISO9001-2000, ABS, SG ;
4) OEM welcom
Submerged Arc Welding Wire,

Thanks a lot in advance for you reading mail from New Keyrun.
We are one of China suppliers. We are manufacture in field of welding material more than 15 years. Ovens of welding, Welding electrodes and welding wire are our main products. For instance, carbon steel welding electrode, stainless steel electrode, special electrode, co2 gas shield welding wire, flux wire, submerged arc wire and so on.
Now our monthly output of electrode is more than 1200 tons, also the welding wire is more than 2500 tons.
We have some certificates, for example: ISO9001-2000, ABS, SGS, DNV and so on.
It is very important for us to have some clients from your country, we know now our products are good taste in your market.
We would like to find more importers to help us developing market. So I send this e-mail to you.
If we have a chance, I think the result is win-win.
Thanks a lot again for your read our mail.

Submerged Arc Welding Wire

Submerged Arc Welding Wire
1.AWS EL-8 EM12 EM12K EH14
2.size :2.0-5.0mm
3.ISO BV IEI SGS
Submerged Arc Welding Wire

1.AWS EL-8 EM12 EH14
2.Size :2.0-5.0mm
3.ISO BV IEI SGS
4.GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi

Model:
EL8(H08A) EM12K(H08MnA) EH14(H10Mn2)
Wire specification:
Φ2.0mm, Φ2.4mm, Φ2.5mm, Φ3.0mm, Φ3.2mm, Φ4.0mm, Φ5.0mm Φ5.5mm
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%) & Mechanical properties of deposited metal


The type of packages

AWS ER70S-6 welded wire

welded wire SO9001,CE,TUV
AWS A5.18 ER70S-6
0.8,0.9,1.0,1.2,1.6mm
for welding of carbon steel and low alloy steel
Detailed Product Description
welded wire
ISO9001,CE,TUV
AWS A5.18 ER70S-6
0.8,0.9,1.0,1.2,1.6mm
for welding of carbon steel and low alloy steel
welded wire

Model:
AWS A5.18 ER70S-6

Specification:

1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.

Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.

Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
5. suitable for all position

Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03

Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2

Submerged Arc Welding Wire

welding wire
excellent welding performance and mechanical performancde
Welding wire
With excellent welding performance and mechanical performancde such as stable arc,strong removability of slag,good welding seam and high depositing efficiency,the series of submerged are welding wires manufactured by our company are suitable for the welding of thick boards.

This series of welding wires have a wide range of specification and are suitable for the welding of various kinds of products with different requirements in industries including steel strutrue, pressure wessel, bridge, shipmaking heavy duty machinery and pipes etc.

Submerged Arc Welding Wires (H08MnA)EM12

Submerged arc welding wires
EM12
AWS A 5.17
Size:1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Submerged Arc Welding Wires
EM12
AWS A 5.17
Size: 1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Packing: 25kgs/spool
Based on sutomers' size requirements
Min. Order Quantity: 2T

Submerged Arc Welding Wires (em12)

Sub Merged Arc Welding Wire.They are suitable for the welding of thick boards,with excellet welding performance.
Welding method
Brand name
GB
AWS
Chemical Composition
Impact Value()
C
Mn
Si
Cr
Ni
Cu
P
S
Relevant welding flux
Submerged arc welding
HTM08A
H08A
EL 12
41(-20)
0.057
0.4
0.018
0.018
0.025
0.05
0.012
0.019
F43A2
HTM08MnA
H08MnA
EM 12
42(-20)
0.062
1.77
0.048
0.022
0.026
0.03
0.014
0.015
F43A2
HTM08Mn2SiA
H08Mn2SiA

51(0)
0.076
1.81
0.62
0.026
0.029
0.04
0.02
0.012
F48A0
HTM10Mn2
H10Mn2
EH 14
65(-20)
0.079
1.56
0.058
0.048
0.035
0.05
0.018
0.017
F48A2
EM12K

EM 12K
45(-20)
0.068
1.54
0.25
0.027
0.018
0.05
0.019
0.017
F43A2
HTM-55( III )
H10MnCuNi( III)

75(-40)
0.09
1.32
0.3
0.44
0.27
0.23
0.01
0.012
F48A4

COIL SIZES FOR SUBMERGED ARC WELDING WIRE
wire Size(mm)
Weigth (kg)
Bore Diameter (mm)
Axial Size (mm)
2.0, 3.0, 3.2, 4.0, 4.5, 5.0
25
300
82-85
100 250 350
550
162-165
250 350
630
162-165
200
380
175

Submerged Arc Welding Wires EH14

Submerged Arc Welding Wires EH14:
1. Strong removability of slag
2. Good welding seam
3. High depositing efficiency
Submerged Arc Welding Wires EH14:
1. Strong removability of slag
2. Good welding seam
3. High depositing efficiency
Welding method
Brand name
GB
AWS
Chemical Composition
Impact Value()
C
Mn
Si
Cr
Ni
Cu
P
S
Relevant welding flux
Submerged arc welding
HTM08A
H08A
EL 12
41(-20)
0.057
0.4
0.018
0.018
0.025
0.05
0.012
0.019
F43A2
HTM08MnA
H08MnA
EM 12
42(-20)
0.062
1.77
0.048
0.022
0.026
0.03
0.014
0.015
F43A2
HTM08Mn2SiA
H08Mn2SiA

51(0)
0.076
1.81
0.62
0.026
0.029
0.04
0.02
0.012
F48A0
HTM10Mn2
H10Mn2
EH 14
65(-20)
0.079
1.56
0.058
0.048
0.035
0.05
0.018
0.017
F48A2
EM12K

EM 12K
45(-20)
0.068
1.54
0.25
0.027
0.018
0.05
0.019
0.017
F43A2
HTM-55( III )
H10MnCuNi( III)

75(-40)
0.09
1.32
0.3
0.44
0.27
0.23
0.01
0.012
F48A4

COIL SIZES FOR SUBMERGED ARC WELDING WIRE
wire Size(mm)
Weigth (kg)
Bore Diameter (mm)
Axial Size (mm)
2.0, 3.0, 3.2, 4.0, 4.5, 5.0
25
300
82-85
100 250 350
550
162-165
250 350
630
162-165
200
380
175

Submerged Arc Welding Wires EM12

Submerged Arc Welding Wires
EM12
AWS A5.17: EM12
Size: 1.2/1.6/2.0/2.4/2.5/3.0/3.2/4.0/5.0mm
Submerged Arc Welding Wires
EM12
AWS A5.17: EM12
Size: 1.2/1.6/2.0/2.4/2.5/3.0/3.2/4.0/5.0mm
Packing: 15kgs/coil; 25kgs/spool

Submerged Arc Welding Wires

Submerged Arc Flux Cored Welding Wire DY-YD430(M) containing 17%Cr is ferrite type flux cored wire.
Submerged Arc Flux Cored Welding Wire:

DESCRIPTION

DY-YD420(M), designed for surfacing is ferrite type flux-cored wire,it has good corrosion resistance under high temperature.

APPLICATION

For hard facing corrosion resisting parts;underlying base metals for continuous casting roll, strightened roll,and other rolls, with welding flux SJ414 or HJ107.

Typical Chemical Composition of Deposition Metal (%)

C
Mn
Si
Cr
S
P
0.05
0.90
0.50
17.50
0.016
0.018

Typical Mechanical Properties of Deposited Metal

HRC
Remarks
23
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
4.0
Current Range(A)
350-450
450-550
Voltage Range (V)
25-32
28-34

AWS ER70S-6 welding wire

CO2 welding wire, AWS ER70S-6
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg
Suitable for low carbon steel and low alloy steel

CO2 welding wire ER70S-6

CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
It is suitable for welding in all position like Vertical/Horizontal.
Co2 welding wire will produce Low Hydrogen Weld
Compatibility: CO2 gas shielded welding wire can be used for welding mild steel, high strength steel & low alloyed steel, co2 welding wire may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.

Applications: Co2 welding wire is suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.

Submerged Arc Welding Wires

Submerged Arc Welding Wires:
1. Strong removability of slag
2. Good welding seam
3. High depositing efficiency
Welding method
Brand name
GB
AWS
Chemical Composition
Impact Value()
C
Mn
Si
Cr
Ni
Cu
P
S
Relevant welding flux
Submerged arc welding
HTM08A
H08A
EL 12
41(-20)
0.057
0.4
0.018
0.018
0.025
0.05
0.012
0.019
F43A2
HTM08MnA
H08MnA
EM 12
42(-20)
0.062
1.77
0.048
0.022
0.026
0.03
0.014
0.015
F43A2
HTM08Mn2SiA
H08Mn2SiA

51(0)
0.076
1.81
0.62
0.026
0.029
0.04
0.02
0.012
F48A0
HTM10Mn2
H10Mn2
EH 14
65(-20)
0.079
1.56
0.058
0.048
0.035
0.05
0.018
0.017
F48A2
EM12K

EM 12K
45(-20)
0.068
1.54
0.25
0.027
0.018
0.05
0.019
0.017
F43A2
HTM-55( III )
H10MnCuNi( III)

75(-40)
0.09
1.32
0.3
0.44
0.27
0.23
0.01
0.012
F48A4

COIL SIZES FOR SUBMERGED ARC WELDING WIRE
wire Size(mm)
Weigth (kg)
Bore Diameter (mm)
Axial Size (mm)
2.0, 3.0, 3.2, 4.0, 4.5, 5.0
25
300
82-85
100 250 350
550
162-165
250 350
630
162-165
200
380
175

Submerged Arc Welding Wires

Submerged Arc Welding Wire AWS A5.17 EM13K
Application:welding high tensile strength steel structures
Size:2.4mm/3.2mm/4.0mm
Submerged Arc Welding Wire AWS A5.17 EM13K

1.Classification:
AWS A5.17 EM13K ; GB H10MnSi ; EN 756 S1

2.Application:
Welding of important low carbon steel /medium carbon steel structures with suitable fluxes,to obtain target metal compostion.
Such as Boilers , nuclear stations , chemical / pressure containers , bridges ,ships etc.

3.Excellent Welding Proformance:
can get good mechanical seam with corresponding flux ; high fusion / depositing efficiency , stable welding quality , works / manipulates smoothly etc.

4.Welding Process:
Sumbermarged-Arc -- SAW Welding Process ,recommended flux SFA/AWS 5.17 ,
please refer to specification Guide of Lincoln / Esab Manual Instructions .

5.Packing: 25kg per roll , one roll per cartons , then on pallet.


We are a factory-based exporting business office of Precision Welding Material Group.We specialized in producing welding consumables.With strong techincal capacity and higher
researching level , product quality keeps ahead in the professional welding domain.

Our products mainly have:
1. Mild Steel Steel Electrode Series: AWS E6013 / E6011 / E7018 / E7024
2. Low Alloy Steel Electrode Series: AWS E8018-G / E9016-G / E7015-G
3. Gas-Shielded Welding Wire: AWS ER70S-6 /ER70S-3 / ER80S-G etc
4. Submerged Arc Welding Wire Series: AWS EL12 / EM12K / EH14 etc
5. Stainless Steel Welding Electrodes: AWS E308L-16 / E308-16 etc
6. Cast Iron Welding Electrode Series: AWS EZNi-C1 / ENiFe-C1 etc
7. Flux-Cored Welding Wire Series: AWS E71T-1 / ER308LT1-1 etc
8. Brazing Material / Nonferrous Metals:Copper / Aluminium Alloys
Approvals: GL ; ABS ; DNV ; TUV etc


Update Date:2011-5-13 0:37:29

Submerged Arc Welding Wires

Submerged arc welding wires
EM12
AWS A 5.17
Size:1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Submerged Arc Welding Wires
EM12
AWS A 5.17
Size: 1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Packing: 25kgs/spool
Based on sutomers' size requirements
Min. Order Quantity: 2T

Submerged Arc Welding wires

Applicable for the submerged arc automatic weld of low carbon steel and low alloy steel such as boiler,bridge,boat.
Product Model:H08Mn2SiA
Brand
Model
Sodler wire spec
Chemical components of solder wire(%)
Mechanical properties of deposited metal
C
Mn
Si
S
P
Cu
Cr
Ni
σ
0.2
(MPa)
σ
b
(MPa)
δ
5
(%)
kv
(J)
UN49-1
H08Mn2SiA
Φ2.0mm
Φ2.4mm
Φ2.5mm
Φ3.0mm
Φ3.2mm
Φ4.0mm
Φ5.0mm
Φ5.5mm
≤0.11
1.802.10
0.650.95
≤0.030
≤0.030
≤0.50
≤0.20
≤0.30
≥400
480650
≥22
≥27
(-20)
Packing form
1.20Kg plastic spool packing(for only Φ2.0mm)
2.25Kg, 50Kg, 150Kg, 250Kg, 350Kg transverse wind without core
3.30Kg, 50Kg dundle
4.250Kg wiid drum packing
Characterisitcis and application
Applicable for the submerged arc automatic weld of low carbon steel and low alloy steel such as boiler,bridge,boat.

Submerged Arc Welding wires

Submerged Arc Welding wires
a.Diameter:2.0;3.0;3.2;4.0;5.0 mm
Submerged Arc Welding wires


NO GB/T14957 AWS
1 H08A EL8
2 H08MnA EM12
3 H10Mn2 EH14
4 H10MnSi EM13K
Sizes Of Wire:diameter
mm:2.0;3.0;3.2;4.0;5.0

Submerged Arc welding Wire EB2

Submerged Arc welding Wire EB2
For welding heat-resistant pressure vessels and pipes, such as 12CrMoA, ASTMA387Cr11, A387Cr12.
1,Submerged Arc welding Wire EB2 For welding heat-resistant pressure vessels and pipes, such as 12CrMoA, ASTMA387Cr11, A387Cr12.
2,
Wire Type
Size
inner diameter
outer diameter
Net Weight
Coil Packaging
φ1.6~5.0(mm)
300mm 620mm
400mm 820mm
25kg 250kg
TIG Wire
1 meter
5kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Mo
V
Cu
0.11~0.16
0.40~0.70
0.15~0.35
≤0.030
≤0.030
0.80~1.10
≤0.30
0.40~0.60
-
≤0.20
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
470~510
550~580
≥22
130(10)

Submerged Arc welding Wire

Submerged Arc welding Wire EM12
Certificate:ABS,DNV,CCS,GL,NK,BV,LR,RINA,KR...
Application: welding sheet metal
Submerged Arc welding Wire EM12
1,20kg plastic spool packing(for only Φ2.0mm)
2,25kg, 50kg, 150kg, 250kg, 350kg transverse wind without core
3,30kg, 50kg dundle
4,250kg wiid drum packing
5,Applicable for the sumberged arc automatic weld of the boiler and pressure container made of low carbon steel and low alloy steel.
6,
Brand
Model
Sodler wire spec
Chemical components of solder wire(%)
Mechanical properties of deposited metal
C
Mn
Si
S
P
Cu
Cr
Ni
σ
0.2
(MPa)
σ
b
(MPa)
δ
5
(%)
Α
kv
(J)
JY-08MnA
H08MnA
(EM12)
Φ2.0mm
Φ2.4mm
Φ2.5mm
Φ3.0mm
Φ3.2mm
Φ4.0mm
Φ5.0mm
Φ5.5mm
≤0.10
0.80~1.10
≤0.07
≤0.030
≤0.030
≤0.35
≤0.20
≤0.30
≥330
415~550
≥22
≥27
(-20°C)

Submerged Arc-welding Wire -EH14

Submerged Arc-welding Wire -EH14. With flux SJ101,HJ150,HJ330,HJ350,the welding seam has excellent mechanical prope.
Submerged Arc-welding Wire -EH14

1,EH14 is a kind of submerged arc welding wire. With flux SJ101,HJ150,HJ330,HJ350, the welding seam has excellent mechanical properties.
2,Used to automatically submerged arc welding for mild steel and low alloy steel like 16Mn, 14MnNb steel structrures.
3,
Wire Type
Size
inner diameter
outer diameter
Net Weight
Coil Packaging
φ1.6~5.0(mm)
300mm 620mm
400mm 820mm
25kg 250kg
TIG Wire
1 meter
5kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
≤0.12
1.50~1.90
≤0.07
≤0.035
≤0.035
≤0.20
≤0.30
≤0.20
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
410~550
≥22
≥34(-20)
Wire Size(mm)
Welding position
Eletricity Polarity
φ2.0
φ2.5
φ3.0

DC+ or AC
φ3.2
φ4.0
φ5.0

Submerged Welding Wire and suitable Welding Flux

Excellent welding and mechanical performances,stable arc,easily removable residue,good seam forming highly efficient deposition
Submerged Welding Wire
The feature: excellent welding and mechanical performances,stable arc, easily removable residue,good seam forming and highly efficient deposition. Wire melting doesn’t lead to spashing or strong flashing. The seam surface is smooth and welding quality is guaranteed.
Specification:
Dia.2.0mm,2.5mm,3.2mm,4.0mm,5.0mm
Packing: 15-30kg/coil, then on pallet
Technical Data:
Products
Chemical compositions of one sample wire (%)
Mechanical properties of one sample deposited metal
C
Mn
Si
Cr
Ni
Mo
Cu
Ti
S
P
Yield strength (Mpa)
Tensile Strength (Mpa)
Elongation (%)
Impact Energy (–20°C) (J)
H08A
0.06
0.43
0.025
0.020
0.010
-
0.120
-
0.015
0.014
455
545
30
80
H08C
0.07
0.41
0.027
0.019
0.017
-
0.120
-
0.012
0.011
460
555
31
87
H08E
0.08
0.50
0.026
0.021
0.016
-
0.130
-
0.010
0.011
470
560
31
90
H08MnA
0.06
0.94
0.024
0.025
0.015
-
0.130
-
0.014
0.017
469
578
28
87
H10Mn2
0.07
1.85
0.021
0.021
0.016
-
0.160
-
0.017
0.015
460
570
29
85
H10MnSi
0.08
0.96
0.850
0.015
0.018
-
0.160
-
0.018
0.020
455
550
30
75
H08MnMoA
0.08
1.45
0.180
0.018
0.015
0.38
0.150
0.12
0.020
0.019
490
650
27
85
H08Mn2MoA
0.07
1.78
0.210
0.021
0.018
0.60
0.150
0.11
0.022
0.017
510
657
26
90
H08Mn2SiA
0.07
1.85
0.750
0.015
0.018
-
0.150
-
0.018
0.020
455
560
27
89

Submerged Welding Wire

Submerged Welding Wire
1. Size: 2.0MM, 3.0MM,4.0MM
2. High efficiency, little splash and smog.
Submerged Welding Wire



4. The content is as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030


5. Mechnical Properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5



6. Welding Current:
Wire Size (mm)
0.8
1.0
1.2
1.6


Welding position
Welding Current (A)
40~140
50~220
80~350
120~550

Note
Wire shall be stocked in dry.Open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts.


7. Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.

1.
Size: 2.0MM, 3.0MM,4.0MM,5.0MM
2.
High efficiency, little splash and smog.
3.
Certificate: ISO 9001:2000

0.8mm CO2 GAS SHIELD MIG WELDING WIRE ER70S-6

CO2 gas shield welding wire
ABS/LR/GL/DNV/CCS/NK/KR CERTIFICATE
packing: 15kg spool on pallet
copper coated
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
Tensile Num KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
Packing: 15kg per spool with pallet
spool size: D270

TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheet metal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable

AWS ER70S-6 welding wire

1.AWS ER70S-6 welding wire
2.Dia.0.8mm,1.0mm,1.2mm,1.6mm
3.Weight:1kg,5kg,15kg,18kg,20kg
Welding Wire ER70S-6 ,
WELDING WIRE

Description:
ER70S-6 is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:

Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts

Submerged Welding Wire

Submerged Welding Wire
1. Size: 2.0MM, 3.0MM,4.0MM
2. High efficiency, little splash and smog.
Submerged Welding Wire



4. The content is as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030


5. Mechnical Properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5



6. Welding Current:
Wire Size (mm)
0.8
1.0
1.2
1.6


Welding position
Welding Current (A)
40~140
50~220
80~350
120~550

Note
Wire shall be stocked in dry.Open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts.


7. Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.

1.
Size: 2.0MM, 3.0MM,4.0MM,5.0MM
2.
High efficiency, little splash and smog.
3.
Certificate: ISO 9001:2000

Submerged Welding Wire

Submerged Welding Wire
1. Size: 2.0MM, 3.0MM,4.0MM
2. High efficiency, little splash and smog.
Submerged Welding Wire



4. The content is as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030


5. Mechnical Properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5



6. Welding Current:
Wire Size (mm)
0.8
1.0
1.2
1.6


Welding position
Welding Current (A)
40~140
50~220
80~350
120~550

Note
Wire shall be stocked in dry.Open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts.


7. Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company

1.
Size: 2.0MM, 3.0MM,4.0MM,5.0MM
2.
High efficiency, little splash and smog.
3.
Certificate: ISO 9001:2000

Submerged Welding Wires EL8

1.Submerged Welding Wires EL8
2.Size:2.0mm/2.5mm/3.2mm/4.0mm/5.0mm
3.Welding flux:HJ431,SJ301
Submerged Welding Wires EL8

1.Size:2.0mm/2.5mm/3.2mm/4.0mm/5.0mm
2.Welding flux:HJ431,SJ301
3.Good quality.
4.Competive price.
5.Professional.


ITEM

C

Si

Mn

S

P
EL8

0.081

0.02


0.45

0.008

0.012

EM12

0.007

0.03

0.95

0.010

0.012

EM13K

0.080

0.72

0.9

0.009

0.011
EH14

0.070

0.03

1.72

0.010

0.010

Submerged arc Welding Wire

Submerged Arc Flux Cored Welding WireDY-YD430(M) containing 17%Cr is ferrite type flux cored wire.
Submerged Arc Flux Cored Welding Wire:

DESCRIPTION

DY-YD420(M), designed for surfacing is ferrite type flux-cored wire,it has good corrosion resistance under high temperature.

APPLICATION

For hard facing corrosion resisting parts;underlying base metals for continuous casting roll, strightened roll,and other rolls, with welding flux SJ414 or HJ107.

Typical Chemical Composition of Deposition Metal (%)

C
Mn
Si
Cr
S
P
0.05
0.90
0.50
17.50
0.016
0.018

Typical Mechanical Properties of Deposited Metal

HRC
Remarks
23
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
4.0
Current Range(A)
350-450
450-550
Voltage Range (V)
25-32
28-34

Submerged arc Welding Wire

Submerged arc Welding Wire
for welding low carbon steel and some low-alloy steel structures
We supply AWSEL8 AWSEM12 AWSEH14
Submerged arc Welding Wire


AWSEL8
for welding low carbon steel and some low-alloy steel (16Mn) structures with flux HJ430,HJ431,HJ433. for excellent mechanical property. Approved by CCS.
C≤0.10 Mn0.30-0.60 Si≤0.0
Dia.:2.0 2.5 3.2 4.0 5.0mm


AWSEM12
for welding low carbon steel and some low-alloy steel (16Mn) structures with flux HJ430,HJ431,HJ433. for excellent mechanical property. Approved by CCS.
C≤0.10 Mn0.08-1.10 Si≤0.07
Dia.:2.0 2.5 3.2 4.0 5.0mm

AWSEH14
for welding low carbonfor excellent mechanical property steel or high strength steel structures like boat, heavy-machunes, pressure container and bridges. for excellent mechanical property.
C≤0.12 Mn1.50-1.90 Si≤0.07

Dia.:2.0 2.5 3.2 4.0 5.0mm

Also can supply other models.
Welcome send email to enquiry.

Submerged arc welding Wire - EM12

Applicable for the sumberged arc automatic weld of the boiler and pressure container made of low carbon steel and low alloy stee
Submerged arc welding Wire - EM12
1,20kg plastic spool packing(for only Φ2.0mm)
2,25kg, 50kg, 150kg, 250kg, 350kg transverse wind without core
3,30kg, 50kg dundle
4,250kg wiid drum packing
5,Applicable for the sumberged arc automatic weld of the boiler and pressure container made of low carbon steel and low alloy steel.
6,
Brand
Model
Sodler wire spec
Chemical components of solder wire(%)
Mechanical properties of deposited metal
C
Mn
Si
S
P
Cu
Cr
Ni
σ
0.2
(MPa)
σ
b
(MPa)
δ
5
(%)
Α
kv
(J)
TFM-08MnA
H08MnA
(EM12)
Φ2.0mm
Φ2.4mm
Φ2.5mm
Φ3.0mm
Φ3.2mm
Φ4.0mm
Φ5.0mm
Φ5.5mm
≤0.10
0.80~1.10
≤0.07
≤0.030
≤0.030
≤0.35
≤0.20
≤0.30
≥330
415~550
≥22
≥27
(-20°C)

Submerged arc welding wire (EL-8,EM12)

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.



The submerged arc welding wire is proved by ISO9001:2000.

Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

Submerged arc welding wire EL8.,EM12

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.





The submerged arc welding wire is proved by ISO9001:2000.

Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

Submerged arc welding wire EM12 EM12K

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.





The submerged arc welding wire is proved by ISO9001:2000.

Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

Submerged arc welding wire EM12K

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.





The submerged arc welding wire is proved by ISO9001:2000.

Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

AWS ER70S-6 welding wire

CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating
Features Specifications: WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
STANDARD:GB,AWS JIS
Chemical Composition of Welding Wire(%)
Type:ER50-6
C: <0.093
Mn: <1.13
Si: <0.83
S: <0.012
P:< 0.010
Cu:<0.063
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength Mpa
Elogation(%)
Temperature
Tensile Num Kav
550
450
30
66(-29)
27
Specifications/Reference Electric Current/ Voltage/ Packing/ Weight
Diameter
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
40-140A
50-200A
70-260A
80-350A
170-550A
Voltage
16-24
16-27
16-27
17.5-30
18-35
Packaging
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM

Submerged arc welding wire H08A,H08MnA

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.




The submerged arc welding wire is proved by ISO9001:2000.

Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

Submerged arc welding wire H08A,H08MnA

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

Submerged arc welding wire H08MnA (EM12)

Submerged arc welding wire H08MnA (EM12) is used together with fused flux 431 for welding carbon steel and low-allay steel.
1. Product Information
Chemical Composition of the Welding Wires(%)
C
Mn
Si
Cr
Ni
S
P
≤0.10
0.8~1.1
≤0.07
≤0.20
≤0.30
≤0.030
≤0.030

Mechanical Properties of Welding Wires
σ b
σs
δ5
Akv
415~550MPa
≥330MPa
≥22%
≥27J

2. Detail Picture
Feature:
(1) Submerged arc welding wire H08MnA (EM12) is used together with fused flux 431.

(2) It is used for both high speed welding and filling welding on 50kg class base metals.

3. Picture of Factory

Submerged arc welding wire SQ EL-8

Submerged arc welding wire
1carbon steel and low-alloy steel.
2Stable electric arc,low splashing,high depsition
3size:2.4-5.0

S
ubmerged-buried Arc Welding Wire

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----



Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged arc welding wire SQ EM-12

Submerged arc welding wire
1carbon steel and low-alloy steel.
2Stable electric arc,low splashing,high depsition
3size:2.4-5.0

S
ubmerged-buried Arc Welding Wire

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----



Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged arc welding wire and Flux

Submerged arc welding wire and Flux
Well and High Quality Control
Prompt Delivery
New Product
Free Sample.

1 Submerged arc welding wire ( SAW WIRE) H08A .H08MnA/ H10Mn
2



2. Specifications: 2.0 mm, 2.4 mm, 3.2 mm, 4.0 mm
3. Type of packing: 25 kg, 50 kg, 100 kg, 200 kg, 300 kg
4. Packing material: carton, knitting bag, wooden spool
5. Advantage/
. Well and High Quality Control
. Prompt Delivery
. New Product
. Customer's Designs and Logos are Welcome
. Competitive Prices
. Small Order Acceptable

Submerged arc welding wireH08A

GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.





The submerged arc welding wire is proved by ISO9001:2000.

Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.

Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01

Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78

Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650

Submerged arc welding wire

Submerged arc welding wire:
Quick Details
Place of Origin: Jiangsu China (Mainland) Brand Name: Model Number: EM12
Mater
Submerged arc welding wire:Quick Details
Place of Origin:
zhejiang China (Mainland)
Brand Name:
Da Yunhe
Model Number:
EM12
Material:
welding steel
Diameter:
1.6mm-5.0mm
Weight:
25 kg per coil
Application:
steel stucture
Certification:
ISO9001, CCS,ISO14000
Packaging & Delivery
Packaging Detail:
Packing: 25kg/bag, then on wooden pallets
Delivery Detail
within 15 days after confirming the purchase orders
Specifications
SAW wire EL12
-Suitable for welding low carbon steels and some low-alloy tructure
-Size: 1,2mm to 5.0mm

EM12 submerged arc welding wire

1-Sizes:
1.6 - 5.0mm

2-
Applications
:
welding low carbon steels and some low-alloy steel structures,high-Mn welding flux
3-Packing:
precious layer wire self incto coils,every coils packed in plastic bag,every 25kg per coil,every coil in one carton then on wooden pallets

4-Approvals:
ABS,CCS,LR

5-Making capacity:500 metric tons
MOQ:1000kg(one pallet)
:

Submerged arc welding wire

Submerged arc welding wire
We gained good reputation for our low price but high quality among our customers.
Sunmeged arc Welding Wire

1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

Submerged arc welding wire

Submerged welding wire
1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog
Sunmeged arc Welding Wire

1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

AWS ER70S-6 welding wire

AWS ER70S-6 welding wire
1)melting fast
2)efficient cladding
3)low splash
4)high reliability ISO9001
AWS ER70S-6 welding wireMODEL:GB/T ER50-6 AWS ER70S-6 DIN SG2
Features Specifications:

use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures

Material:
AWS ER70S-6 welding wire is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
AWS ER70S-6 welding wire
Introduction
: Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Chemical Composition of Welding Wire(%)
C
Mn
Si
P
S
Cu
0.06-0.15
0.80-0.15
0.80-1.15
≤0.025
≤0.035
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
15/18
15/18
15/20
15/20
15/20

Submerged arc welding wire

Submerged welding wire
It is applied in the welding.
Diameter is 0.8mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm
Sunmeged arc Welding Wire

It is applied in the welding.
Diameter is 0.8mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm.
It is smooth space, and in apple-pie order.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5





Uses:

Our products are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.


We are manufacture and exporter of the products, we always do best for customers. If you in need of our products, pls feel free to contact us, welcome to here!

Best regards,
Tina
Tel: 86-312-5922853

Submerged arc welding wire

Submerged welding wire ER70s-6
1. AWS ER70s-6
2. Smooth face,in apple -pie order.
3.Small splash and smog.
Sunmeged arc Welding Wire (ER70s-6)

1. AWS ER70s-6
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5





Uses:

Our products are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.


We are manufacture and exporter of the products, we always do best for customers. If you in need of our products, pls feel free to contact us, welcome to here!

Best regards,
Tina
Tel: 86-312-5922853

Submerged arc welding wire

We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with
Sunmeged arc Welding Wire

1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

Submerged arc welding wire

Submerged welding wire
1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog
Sunmeged arc Welding Wire

1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5





Uses:

Our products are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.


We are manufacture and exporter of the products, we always do best for customers. If you in need of our products, pls feel free to contact us, welcome to here!

Best regards,
Tina
Tel: 86-312-5922853

Submerged arc welding wire

Submerged welding wire
It is applied in the welding.
Diameter is 0.8mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm
Sunmeged arc Welding Wire

It is applied in the welding.
Diameter is 0.8mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm.
It is smooth space, and in apple-pie order.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5





Uses:

Our products are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.


We are manufacture and exporter of the products, we always do best for customers. If you in need of our products, pls feel free to contact us, welcome to here!

Best regards,
Tina
Tel: 86-312-5922853

Submerged arc welding wire

Submerged welding wire
1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and
Sunmeged arc Welding Wire

1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

AWS ER70S-6

Stable electric arc,.Little splashing,Moderate deflection,Good welding seam,Smooth wire carring,Adapt for automatic Etc.
CO2 Gas Shielded Welding Wire AWS ER70S-6:

Stable electric arc,.Little splashing,Moderate deflection,Good welding seam,Smooth wire carring,Adapt for automatic Etc.

The products take the advanced technology of surface cleaning and copper plating, the surface is smooth, and the copper is well-distributed. The rust inhibitor, which is made of new type composite rusisting materials, brings about good antirust performance. The close package can keep the bright color and nonrust for long time. They adopt the refined rowing and winding technology, has excellent bonding performance.

Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts



Update Date:2011/9/30 10:36:22

Submerged arc welding wire

vehicles, bridge projects, ship building and containers.
Sunmeged arc Welding Wire (ER70s-6)

1. AWS ER70s-6
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

Submerged arc welding wire

We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with
Sunmeged arc Welding Wire (ER70s-6)

1. AWS ER70s-6
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

Submerged arc welding wire

Submerged welding wire
1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.
Sunmeged arc Welding Wire

1. Diameter: 1.0mm, 2.0mm, 3.0mm, 4.0mm
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5





Uses:

Our products are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.


We are manufacture and exporter of the products, we always do best for customers. If you in need of our products, pls feel free to contact us, welcome to here!

Best regards,
Tina
Tel: 86-312-5922853

Submerged arc welding wire

We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations wit
Sunmeged arc Welding Wire (ER70s-6)

1. AWS ER70s-6
2. Smooth face,in apple -pie order.
3.Small splash and smog.

Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5

Submerged arc welding wire

Submerged arc welding wire:
1. AWS EL12
2. Exellent quality
3. Best price
Submerged arc welding wire
The series of submerged arc welding wire manufactured by our company are suitable for the welding of thick boards, with excellent welding performance and mechanical performance such as stable arc, strong removability of slag, good welding seam and high depositing efficiency.

This series of welding wire have a wide range of specification, and are suitable for the welding of various kinds of products with different requirements in industries including steel structure, pressure vessel, bridge, shipmaking ,heavy duty machinery and pipes etc.

AWS ER70S-6

mig/co2 welding wire AWS ER70S-6
Dia:0.6-0.8-1.0-1.2-1.6mm
Packing: 5-15-20kg
ISO certificate!

MIG/CO2 WELDING WIRE AWS ER70S-6

ER70S-6

Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.





TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable

CONFORMANCE
Conforms to ER70S-6 per
AWS A5.18
ABS : 3YSA
CCS : 3YSM
DNV : IIIYMS

DEPOSIT COMPOSITION

Requirements:
AWS E6013(%)
%C
%Mn
%Si
%P
%S
0.06 - 0.15
1.40 - 1.85
0.80 - 1.15
0.025
0.035
Typicle Values(%)
0.080
1.13
0.60
0.010
0.011

Submerged arc welding wire

low price and high quality
diameter :2.0mm-5.5mm

Brand/Model
HJ-08A /H08A
Standards
Confirm to GB H08A, Correspond to AWS EL8
Chemical components of welding wire

C
Mn
Si
S
P
Cu
Cr
Ni
≤0.10
0.30-0.60
≤ 0.030
≤0.030
≤0.030.
≤ 0.350
≤ 0.20
≤ 0.30
Mechanical properties of deposited metal
σ0.2
(MPa)
σb
(MPa)
δ5
(%)

AKV
(J)
≥330
415-550
≥22
≥27-20
Characteristics
Applicable for the submerged arc automatic welding of low carbon steel ,low strength alloy steel and pressure container.
Specification
φ2.0mm-5.0mm
Package
20kg plastic spool packing (only for 2.0mm)
25kg ,50kg,150kg,250kg,350kg packed in winding cordless.
30kg,50kg bundle
250kg wood drum packing
Or as per customers requirements

Submerged arc welding wire

welding wire:
complete specifications for electrode and electric welding wire,
reliable quality,reasonable in price
welding wire
Detailed Product Description

Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

Submerged arc welding wire

Model:HX.M08A
Cert: CCS,ABS,GL,BV,NK,KR,LR
Instruction: low carbon steel wire
Chemical composition of welding wire%
Trademark
C
Si
Mn
S
P
Cr
Ni
Cu
H08A
≤0.10
≤0.03
0.350.60
≤0.030
≤0.030
≤0.20
≤0.30
≤0.20
H08E
≤0.10
≤0.03
0.350.60
≤0.020
≤0.020
≤0.20
≤0.30
≤0.20
Mechanical property of deposited metal
Tensile strengthRm
MPa
Lower yield strength(ReL)
MPa
Elongation(A)
%
AKvAverage absorbed energyJ
0°C
415550
≥330
≥22
≥27


Welding wire specification
Welding wire diameter(mm)
φ2.0
φ2.5
φ3.2
φ4.0
φ5.0

Submerged arc welding wires EM12

Submerged arc welding wires
EM12
AWS A 5.17
Size:1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Submerged Arc Welding Wires
EM12
AWS A 5.17
Size: 1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Packing: 25kgs/spool
Based on sutomers' size requirements
Min. Order Quantity: 2T

Submerged arc welding wires EM12

Submerged arc welding wires
EM12
AWS A 5.17
Size:1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Submerged Arc Welding Wires
EM12
AWS A5.17
Size: 1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Packing: 25kgs/coil
Min. Order Quantity: 2T

Submerged arc welding wires EM12

Welding Wires
Submerged Arc Welding Wires
EM12 AWS A 5.17
Size:1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Welding Wires
Submerged Arc Welding Wires
EM12
AWS A 5.17
EN756: S2
DIN 8557: S2
Size: 1.2mm/1.6mm/2.0mm/2.4mm/2.5mm/3.0mm/3.2mm/4.0mm/5.0mm
Packing: 15KGS/SPOOL; 25KGS/COIL

Submerged arc welding wires EM12

1 Low welding costs.
2 High productivity and low electricity consumption.
3 Easy to operate. All-position welding.

Chemical Composition:
P
Ni
Cr
≤0.030
≤0.30
≤0.20

Mechanical Performance of the Deposited Metal:

σb
σs
δ5
AKV(J)

(MPa)
(MPa)
(%)
0
-20
SJ301
415-550
≥330
≥22
≥80
≥34
HJ431
415-550
≥330
≥22
≥27

Submerged buried arc welding wire

Submerged arc welding wire
1carbon steel and low-alloy steel.
2Stable electric arc,low splashing,high depsition
3size:2.4-5.0
S
ubmerged-buried Arc Welding Wire

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----



Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged-Arc Welding Wire EM12 H08A H08MNA

Submerged-Arc Welding Wire EM-12
1.welding wire supplier 25kg/coil
2.ISO BV IEI SGS certificate
1.6-4.0mm
Submerged Arc Welding Wire EM-12(H08A H08MNA H10MN2)
Submerged-Arc Welding Wire
stone bridge welding


Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----

Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650




Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days

PLEASE CONTACT WITH
Miss Alice

Submerged-Arc Welding Wire EM12

A big coil of wire for submerged arc welding with many certificate
Be made from welding rod H08MnA
Submerged arc welding wire

1.Submerged-Arc Welding Wire
1)Packing:plastic inside and weave bag outside
2)Weight:25kg/coil 50kg/coil 100kg/coil
3)Brand :stone bridge brand and hero brand
4)Price term:FOB CNF CIF
5)Loading port :Tianjin port
6)Lead time :10 days

7)Low material:H08A H08MnA H10Mn2 H10MnSi

2
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

3 Welding wire chemical
Composition (%)

Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
4
Mechanical properties
of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----
5 Specification and reference
current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

AWS ER70S-6

Stable electric arc,.Little splashing,Moderate deflection,Good welding seam,Smooth wire carring,Adapt for automatic Etc.
CO2 Gas Shielded Welding Wire AWS ER70S-6:

Stable electric arc,.Little splashing,Moderate deflection,Good welding seam,Smooth wire carring,Adapt for automatic Etc.

The products take the advanced technology of surface cleaning and copper plating, the surface is smooth, and the copper is well-distributed. The rust inhibitor, which is made of new type composite rusisting materials, brings about good antirust performance. The close package can keep the bright color and nonrust for long time. They adopt the refined rowing and winding technology, has excellent bonding performance.

Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts



Update Date:2011/9/30 9:36:02

Submerged-Arc Welding Wire H08A,buried arc welding wire

Submerged arc welding wire of carbon steel and low-alloy steel.Stable electric arc,low splashing,high depsition.


Submerged-Arc Welding Wire

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----


Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged-Arc Welding Wire H08A,buried arc welding wire

Submerged arc welding wire of carbon steel and low-alloy steel.Stable electric arc,low splashing,high depsition.
Submerged-Arc Welding Wire
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----

Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged-Arc Welding Wire H08MnA (ISO)

Submerged arc welding wire of carbon steel and low-alloy steel.Stable electric arc,low splashing,high depsition.


WE ARE MANUFACTURER OF WELDING WIRE WITH STONE BRIDGE AND HERO BRAND

Submerged-Arc Welding Wire

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----


Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged-Arc Welding Wire H10Mn2 (ISO)

Submerged arc welding wire of carbon steel and low-alloy steel.Stable electric arc,low splashing,high depsition.


WE ARE MANUFACTURER OF WELDING WIRE WITH STONE BRIDGE AND HERO BRAND

Submerged-Arc Welding Wire

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----


Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650

Submerged-Arc Welding Wires manufacturer

Submerged-Arc Welding Wires manufacturer
1.welding wires supplier 25kg/coil
2.ISO BV IEI SGS certificate
1.6-4.0mm
Submerged Arc Welding Wires manufacture
Submerged-Arc Welding Wires
welding wires with flux
Hero /stone bridge brand

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----

Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650




Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days

PLEASE CONTACT WITH
Miss Alice

AWS ER70S-6

Mig welding wire:AWS ER70S-6,DIN SG2:0.8~2.0mm
Submerged Arc Welding Wire
Flux-cored welding wire

MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:

mig
welding wires has the characteristics of excellent
technical performance,fast melting speed, high efficient fusion, stable electric
arc, less welding splash,favorable wetness performance,average & beautiful
welding seam,good anti-oxygenic & anti-corrasive property, less sensitive to the
atmosphere holes.

Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

Submerged-Arc Welding wire ISO certificate

Submerged-Arc Welding Wire ISO certificate
1.AWS EL-8 EM12 EH14
2.size :2.0-5.0mm
3.ISO BV IEI SGS certificate
Submerged-Arc Welding wire ISO certificate

stone bridge /hero brand

original:shijiazhuang city


Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----


Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650