welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
Saturday, February 26, 2011
Aluminum welding wire/rod
ER5183
MIG-0.8MM, 0.9MM, 1.0MM, 1.2MM, 1.6MM
TIG-1.6MM, 2.0MM, 2.4MM, 3.2MM, 4.0MM
SPECIFICATIONS CLASSIFICATIONS
AWS A5.10 AWS ER5183
ASME SFA 5.10
DESCRIPTION / APPLICATION
Galaxy Alloy 5183 is a AlMg4.5Mn aluminum filler
Metal. This item is designed to weld high magnesium alloys to meet higher tensile strength requirements. Use on 5083 and 5654 base materials when required tensile strengths are 276 MPa or greater. Typical applications are in the marine and cryogenic industries, and high strength structural aluminum fabrication
MIG-0.8MM, 0.9MM, 1.0MM, 1.2MM, 1.6MM
TIG-1.6MM, 2.0MM, 2.4MM, 3.2MM, 4.0MM
SPECIFICATIONS CLASSIFICATIONS
AWS A5.10 AWS ER5183
ASME SFA 5.10
DESCRIPTION / APPLICATION
Galaxy Alloy 5183 is a AlMg4.5Mn aluminum filler
Metal. This item is designed to weld high magnesium alloys to meet higher tensile strength requirements. Use on 5083 and 5654 base materials when required tensile strengths are 276 MPa or greater. Typical applications are in the marine and cryogenic industries, and high strength structural aluminum fabrication
co2 das shield
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-4
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
Aluminum welding wire
AlSi5 ER4043
Spec:
MIG-0.8MM, 0.9MM, 1.0MM, 1.2MM, 1.6MM
TIG-1.6MM, 2.0MM, 2.4MM, 3.2MM, 4.0MM
SPECIFICATIONS CLASSIFICATIONS
AWS A5.10 AWS ER4043
ASME SFA 5.10
DESCRIPTION/APPLICATION
Galaxy ER4043 is 5% silicon aluminum. This alloy
is recommended for welding 3003, 3004, 5052, 6061,
6063 and casting alloys 43, 355, 356 and 214.
Spec:
MIG-0.8MM, 0.9MM, 1.0MM, 1.2MM, 1.6MM
TIG-1.6MM, 2.0MM, 2.4MM, 3.2MM, 4.0MM
SPECIFICATIONS CLASSIFICATIONS
AWS A5.10 AWS ER4043
ASME SFA 5.10
DESCRIPTION/APPLICATION
Galaxy ER4043 is 5% silicon aluminum. This alloy
is recommended for welding 3003, 3004, 5052, 6061,
6063 and casting alloys 43, 355, 356 and 214.
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 Welding wire ER70S-6
co2 Welding wire:AWS ER70S-6 0.8mm-2.0mm
Submerged arc welding wire:2.5mm-5.0mm
Flux-cored welding wire:E71T-1 E71T-11 0.8-1.6
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features
:
Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application
:
low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
:
0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
:
10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:
ISO 9001 :2000
MOQ
:
one container
Transportantion
:
by sea
Original
:
Hebei China
Welding wire chemical
Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties
of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference
current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Submerged arc welding wire:2.5mm-5.0mm
Flux-cored welding wire:E71T-1 E71T-11 0.8-1.6
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features
:
Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application
:
low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
:
0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
:
10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:
ISO 9001 :2000
MOQ
:
one container
Transportantion
:
by sea
Original
:
Hebei China
Welding wire chemical
Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties
of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference
current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
co2 Welding wire
Standard:AWS A5.28M:2005 GB/T 8110-2008
Gas Shielding Welding Wire of Carbon Steel,high quality, little spark, perfect shape
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in pla
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Gas Shielding Welding Wire of Carbon Steel,high quality, little spark, perfect shape
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in pla
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
co2 das shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 das shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 das shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 das shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
Aluminum welding wire
Aluminum Welding wire Specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon wel
We are professional manufactory for the aluminum welding wire, load in Ningbo of China, E110
Aluminum welding wire/rod
Aluminum Welding wire
Specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon welding rod, low silicon welding rod, high silicon welding rod.The product surface is luminous, and the welding performance is good. It is used in each kind of aluminum material welding.
Technology data for your reference:
AWS
Joint Strength
Parent metal
Characteristics
Standard
(Mpa)
ER1070
Above 55
Pure aluminum series105010701080
Good anti-corrosive and plasticity
ER1100
80-110
Pure aluminum series1100
Good anti-corrosive and plasticity
ER1200
80-110
Pure aluminum series1200
Good anti-corrosive and plasticity
ER2319
400-450
Pure aluminum series2219
High intensity after heat treatment
ER4043
170-250
Al-Mg-Si casting aluminum
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4047
170-250
Casting Al. ,Al-Cu casting ,Ag-Mg-Si casting
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4145
200-300
Al-Cucasting20142017
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER5554
180-240
low Mg content5052,5454casting
Use chemical equipment with a temperature above 65
ER5654
210-270
medium Mg content5154casting
medium intensity,good anti-corrosive
ER5356
270-310
Al-Mg casting, Al-Mg-Si casting, Al-Zn-Mg casting
Typical welding wire used most widely, good mechanics performance and anti-corrosiveness
ER5556
280-320
Al-Zn-Mg casting, Al-Mg casting
The connector intensity is high, and the moulding performance and tenacity is inferior to 5183
ER5183
280-310
Al-Mgcasting5083
Typical welding wire used most widely, good mechanical performance and anti-corrosiveness
We are professional manufactory for the aluminum welding wire, load in Ningbo of China, E110
Aluminum welding wire/rod
Aluminum Welding wire
Specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon welding rod, low silicon welding rod, high silicon welding rod.The product surface is luminous, and the welding performance is good. It is used in each kind of aluminum material welding.
Technology data for your reference:
AWS
Joint Strength
Parent metal
Characteristics
Standard
(Mpa)
ER1070
Above 55
Pure aluminum series105010701080
Good anti-corrosive and plasticity
ER1100
80-110
Pure aluminum series1100
Good anti-corrosive and plasticity
ER1200
80-110
Pure aluminum series1200
Good anti-corrosive and plasticity
ER2319
400-450
Pure aluminum series2219
High intensity after heat treatment
ER4043
170-250
Al-Mg-Si casting aluminum
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4047
170-250
Casting Al. ,Al-Cu casting ,Ag-Mg-Si casting
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4145
200-300
Al-Cucasting20142017
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER5554
180-240
low Mg content5052,5454casting
Use chemical equipment with a temperature above 65
ER5654
210-270
medium Mg content5154casting
medium intensity,good anti-corrosive
ER5356
270-310
Al-Mg casting, Al-Mg-Si casting, Al-Zn-Mg casting
Typical welding wire used most widely, good mechanics performance and anti-corrosiveness
ER5556
280-320
Al-Zn-Mg casting, Al-Mg casting
The connector intensity is high, and the moulding performance and tenacity is inferior to 5183
ER5183
280-310
Al-Mgcasting5083
Typical welding wire used most widely, good mechanical performance and anti-corrosiveness
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
Friday, February 25, 2011
co2 gas shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 gas shield
welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
Aluminum welding wire
Aluminum Welding wire Specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon wel
We are professional manufactory for the aluminum welding wire, load in Ningbo of China, E110
Aluminum welding wire/rod
Aluminum Welding wire
Specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon welding rod, low silicon welding rod, high silicon welding rod.The product surface is luminous, and the welding performance is good. It is used in each kind of aluminum material welding.
Technology data for your reference:
AWS
Joint Strength
Parent metal
Characteristics
Standard
(Mpa)
ER1070
Above 55
Pure aluminum series105010701080
Good anti-corrosive and plasticity
ER1100
80-110
Pure aluminum series1100
Good anti-corrosive and plasticity
ER1200
80-110
Pure aluminum series1200
Good anti-corrosive and plasticity
ER2319
400-450
Pure aluminum series2219
High intensity after heat treatment
ER4043
170-250
Al-Mg-Si casting aluminum
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4047
170-250
Casting Al. ,Al-Cu casting ,Ag-Mg-Si casting
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4145
200-300
Al-Cucasting20142017
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER5554
180-240
low Mg content5052,5454casting
Use chemical equipment with a temperature above 65
ER5654
210-270
medium Mg content5154casting
medium intensity,good anti-corrosive
ER5356
270-310
Al-Mg casting, Al-Mg-Si casting, Al-Zn-Mg casting
Typical welding wire used most widely, good mechanics performance and anti-corrosiveness
ER5556
280-320
Al-Zn-Mg casting, Al-Mg casting
The connector intensity is high, and the moulding performance and tenacity is inferior to 5183
ER5183
280-310
Al-Mgcasting5083
Typical welding wire used most widely, good mechanical performance and anti-corrosiveness
We are professional manufactory for the aluminum welding wire, load in Ningbo of China, E110
Aluminum welding wire/rod
Aluminum Welding wire
Specialized in production pure aluminum welding rod, aluminum magnesium welding rod, aluminum silicon welding rod, low silicon welding rod, high silicon welding rod.The product surface is luminous, and the welding performance is good. It is used in each kind of aluminum material welding.
Technology data for your reference:
AWS
Joint Strength
Parent metal
Characteristics
Standard
(Mpa)
ER1070
Above 55
Pure aluminum series105010701080
Good anti-corrosive and plasticity
ER1100
80-110
Pure aluminum series1100
Good anti-corrosive and plasticity
ER1200
80-110
Pure aluminum series1200
Good anti-corrosive and plasticity
ER2319
400-450
Pure aluminum series2219
High intensity after heat treatment
ER4043
170-250
Al-Mg-Si casting aluminum
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4047
170-250
Casting Al. ,Al-Cu casting ,Ag-Mg-Si casting
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER4145
200-300
Al-Cucasting20142017
The anti-thermal crack performance of the welded joint is good, but the plasticity, toughness are low, becomes grey black after anodic process
ER5554
180-240
low Mg content5052,5454casting
Use chemical equipment with a temperature above 65
ER5654
210-270
medium Mg content5154casting
medium intensity,good anti-corrosive
ER5356
270-310
Al-Mg casting, Al-Mg-Si casting, Al-Zn-Mg casting
Typical welding wire used most widely, good mechanics performance and anti-corrosiveness
ER5556
280-320
Al-Zn-Mg casting, Al-Mg casting
The connector intensity is high, and the moulding performance and tenacity is inferior to 5183
ER5183
280-310
Al-Mgcasting5083
Typical welding wire used most widely, good mechanical performance and anti-corrosiveness
co2 gas welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 shield welding wire
welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 shield welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6 jis
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
Copper Coated Welding Wire ER 70s-6
1. Diameter: 0.8mm,1.0mm,1.2mm,1.6mm
2. The face is smooth.
3. Little flash and smog
Copper Coated Welding Wire ER70s-6
1. Diameter: 0.8mm,1.0mm,1.2mm,1.4mm,1.6mm
2. The face is smooth.
3. Little flash and smog. High efficiency, low power consumption
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechnical Properties:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
1. Diameter: 0.8mm,1.0mm,1.2mm,1.6mm
2. The face is smooth.
3. Little flash and smog
Copper Coated Welding Wire ER70s-6
1. Diameter: 0.8mm,1.0mm,1.2mm,1.4mm,1.6mm
2. The face is smooth.
3. Little flash and smog. High efficiency, low power consumption
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechnical Properties:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
co2 welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
0.8mm gas shield welding wire
gas shield welding wire:annual production is about 5000t
1)good weldability
2)low residue
3)low splash
4)high reliability
gas shield welding wire:
We offer the items of the welding wire by the brand of ER50-6,ER70s-6,E501T-1,E711T, H08A,H08MnA,which has the specification of 0.8~φ5.0mm for your choosing.In addition,we also supply welding rod of J501Fe18,J422,J502,J506,J507 and stainless steel electrode A102 and 431 welding flux.our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability. The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.
.
Trade Mank
Diameter
Lot No
Mfg Date
Executive Standard
Type
Date of lssue
ER 70S-6 (ER 50-6)
Φ1.2mm
X020892
2010-8-30
GB/T 8110-1995
ER 70S-6 (ER 50-6)
2010-8-30
Mechanical Properties of Deposited Metal
Chemical Compositions of the welding wire
Item
Specifieation
Actual Result
Element
Specification
Actual Result
Element
Specification
Actual Result
Tensile Strength
≥500
525
C
0.06-0.15
0.07
Cr
___
0.039
σb(Mpa)
Yield Strength
≥420
435
Mn
1.40-1.85
1.56
Ni
___
0.015
60.2(Mpa)
Elongation
≥22
28
Si
0.80-1.15
0.9
Cu
≤0.50
0.018
δ5(%)
V Impact Tem
-29
-29
S
≤0.035
0.012
(°C)
Impact Yalue
≥27
94 95 73
P
≤0.025
0.01
Impact Yalue
1)good weldability
2)low residue
3)low splash
4)high reliability
gas shield welding wire:
We offer the items of the welding wire by the brand of ER50-6,ER70s-6,E501T-1,E711T, H08A,H08MnA,which has the specification of 0.8~φ5.0mm for your choosing.In addition,we also supply welding rod of J501Fe18,J422,J502,J506,J507 and stainless steel electrode A102 and 431 welding flux.our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability. The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.
.
Trade Mank
Diameter
Lot No
Mfg Date
Executive Standard
Type
Date of lssue
ER 70S-6 (ER 50-6)
Φ1.2mm
X020892
2010-8-30
GB/T 8110-1995
ER 70S-6 (ER 50-6)
2010-8-30
Mechanical Properties of Deposited Metal
Chemical Compositions of the welding wire
Item
Specifieation
Actual Result
Element
Specification
Actual Result
Element
Specification
Actual Result
Tensile Strength
≥500
525
C
0.06-0.15
0.07
Cr
___
0.039
σb(Mpa)
Yield Strength
≥420
435
Mn
1.40-1.85
1.56
Ni
___
0.015
60.2(Mpa)
Elongation
≥22
28
Si
0.80-1.15
0.9
Cu
≤0.50
0.018
δ5(%)
V Impact Tem
-29
-29
S
≤0.035
0.012
(°C)
Impact Yalue
≥27
94 95 73
P
≤0.025
0.01
Impact Yalue
Aluminum welding wire
We can supply the aluminum welding wire,ER1060,ER5356,ER4043,ER4047,ER5183 with competetive price and good quality.
We are professional in supply the Aluminum welding wire as follow, all the surface of welding materials are smooth and clean. The welding wire are labeled with production number and date even the source materials are kept for investigation.
ER1200/1100/1070: The products have good ductility and corrosion resistance, suited for oxyacetylene gas brazing pure aluminum as well as argon arc.
ER4043/4047/4145: Good corrosion resistance, wide range of usage, used as fulling materials while gas welding and organ arc welding of aluminum alloys other than high magnesium alloys.
ER5183/5356/5554/5654: Good corrosion resistance and high strength, wide range of usage. Argon arc welding of aluminum alloys.
Product Name:
Aluminum welding wire
Style:
MIG :
0.8mm~2.0mm
TIG:
2.0mm~4.0mm
Package :
TIG:
L:1000mm
D:1.6mm;2.0mm;2.4mm;2.5mm;3.0mm;3.2mm;4.0mm;5.0mm;6.0mm;
Weight: 10KG/ctn;5KG/ctn
MIG:
D:0.8mm;0.9mm;1.0mm;1.2mm;1.6mm;2.0mm;
Weight:20kg/spool;7kg/spool;2kg/spool;0.45kg/spool
Technical standards as per AWS related standards.
Alloy
Al
Mg
Fe & Si
Fe
Si
Cu
Mn
Zn
Ti
Cr
ER1100
99.0min
-
0.095
-
-
0.05-0.20
0.05
0.10
-
-
ER2319
rem
0.02
-
0.30
0.20
5.8-
6.8
0.20-0.40
0.10
0.10-0.20
-
ER4043
rem
0.05
-
0.80
4.5-6.0
0.30
0.05
0.10
0.20
-
ER4047
rem
0.10
-
0.80
11.0-13.0
0.30
0.15
0.20
-
-
ER5356
rem
4.5-5.5
-
0.40
0.25
0.10
0.05-0.20
0.10
0.06-0.20
0.05-0.20
ER5183
rem
4.3-5.2
-
0.40
0.40
0.10
0.5-1.0
0.25
0.15
0.05-0.25
ER5554
rem
2.4-3.0
-
0.40
0.25
0.10
0.5-1.0
0.25
0.05-0.20
0.05-0.20
ER5556
rem
4.7-5.5
-
0.40
0.25
0.10
0.5-1.0
0.25
0.05-0.20
0.05-0.20
ER4145
rem
0.15
-
0.80
9.3-10.7
3.3-4.7
0.15
0.20
-
0.15
We are professional in supply the Aluminum welding wire as follow, all the surface of welding materials are smooth and clean. The welding wire are labeled with production number and date even the source materials are kept for investigation.
ER1200/1100/1070: The products have good ductility and corrosion resistance, suited for oxyacetylene gas brazing pure aluminum as well as argon arc.
ER4043/4047/4145: Good corrosion resistance, wide range of usage, used as fulling materials while gas welding and organ arc welding of aluminum alloys other than high magnesium alloys.
ER5183/5356/5554/5654: Good corrosion resistance and high strength, wide range of usage. Argon arc welding of aluminum alloys.
Product Name:
Aluminum welding wire
Style:
MIG :
0.8mm~2.0mm
TIG:
2.0mm~4.0mm
Package :
TIG:
L:1000mm
D:1.6mm;2.0mm;2.4mm;2.5mm;3.0mm;3.2mm;4.0mm;5.0mm;6.0mm;
Weight: 10KG/ctn;5KG/ctn
MIG:
D:0.8mm;0.9mm;1.0mm;1.2mm;1.6mm;2.0mm;
Weight:20kg/spool;7kg/spool;2kg/spool;0.45kg/spool
Technical standards as per AWS related standards.
Alloy
Al
Mg
Fe & Si
Fe
Si
Cu
Mn
Zn
Ti
Cr
ER1100
99.0min
-
0.095
-
-
0.05-0.20
0.05
0.10
-
-
ER2319
rem
0.02
-
0.30
0.20
5.8-
6.8
0.20-0.40
0.10
0.10-0.20
-
ER4043
rem
0.05
-
0.80
4.5-6.0
0.30
0.05
0.10
0.20
-
ER4047
rem
0.10
-
0.80
11.0-13.0
0.30
0.15
0.20
-
-
ER5356
rem
4.5-5.5
-
0.40
0.25
0.10
0.05-0.20
0.10
0.06-0.20
0.05-0.20
ER5183
rem
4.3-5.2
-
0.40
0.40
0.10
0.5-1.0
0.25
0.15
0.05-0.25
ER5554
rem
2.4-3.0
-
0.40
0.25
0.10
0.5-1.0
0.25
0.05-0.20
0.05-0.20
ER5556
rem
4.7-5.5
-
0.40
0.25
0.10
0.5-1.0
0.25
0.05-0.20
0.05-0.20
ER4145
rem
0.15
-
0.80
9.3-10.7
3.3-4.7
0.15
0.20
-
0.15
co2 welding wire
welding wire ER70S-4
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
co2 welding wire
welding wire ER70S-6 jis
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550