Welding Electrodes 6013 7018

AWS E6013 Welding Electrodes


Description:
AWS E6013 is a low-carbon steel electrode with a high titanium coating and can be used on AC. or D.C. It has excellent welding technological properties .The arc is stable. The spatter is small. The slag viscosity is moderate. It can be used freely. The slag is easy to clean. The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel , such as ships, vehicles, building, and general machinery.

Conform with:
GB/T 5117 E4313 E6013 AWS A5.1 ISO 2560-B-E43 13 A

Chemical Composition of Wire (%):

C
Mn
Si
S
P
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength (MPa)
Tensile Strength(MPa)
Elongation (%)
AKV(J)
Guarantee Value
≥330
≥420
≥17
-
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
40-70
50-80
80-120
150-190
180-240


AWS E7018 Welding Electrodes

AWSE7018 is low-hydrogen potassium coating carbon steel welding rod and can be used on AC. or D.C . It has excellent welding technological properties. It can be used various composition. Its evident trait is composed of Fe power and can reduce welding layer.
Application:
Suitable for welding important structures made of low alloy steel.


Conform with:
GB/T 5117 E5018 E7018 AWS A5.1 ISO 2560-B-E49 18-1A
Chemical Composition of Wire(%):
C
Mn
Si
S
P
≤0.12
≤1.6
≤0.75
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength
(MPa)
Tensile Strength
(MPa)
Elongation
(%)
AKV(J)
Guarantee Value
≥400
≥490
≥22
≥27(-30°C)
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
60-90
90-120
120-150
170-200
210-250