welding wire

welding wire
Instruction: Welding process with excellent performance, stable arc, small spatter, good weld molding, cladding
welding wire
Instruction: Welding process with excellent performance, stable arc, small spatter, good weld molding, cladding high efficiency, suitable for welding a variety of locations.
Application:1. All kinds of 500MPa grade weld structural steel components.
2. All kinds of 500MPa grade plate, pipe welding.
Specification:F0.8?F1.0?F1.2?F1.6
WT: 15KG---20KG

Wire chemical composition(%)
C
MN
SI
S
P
CU
0.06-0.15
1.4-1.85
0.8-1.15
0.035
0.025
0.5
Fused metallization chemical composition (%)
C
MN
SI
S
P
CU
0.06-0.15
1.4-1.85
0.8-1.15
0.035
0.025
0.5
Fused metallization mechanical behavior
Pilot project



Akv(J)
Guarantee value
500
420
22
47(-20)
General results
560
470
27
96
Reference current(DC+)
Specification(mm)
Welding current(A)
CO2 gas flow(L/min)
Arc voltage
0.8
40--100
15
16--22
1.0
50--220
15--20
16--27
1.2
80--350
15--25
26--30
1.6
170--550
20--25
27--31

welding wire

low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specificat
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features:
Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automatical.
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification:
0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f:
10kg, 15kg or 20kg packed in plastic spool.
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50


Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
≥500
≥420
≥22
-29°
C≥27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

MIG/CO2 gas-shield welding wire:AWS ER70S-6,DIN SG2:0.8~2.0mm
Submerged Arc Welding Wire
Flux-cored welding wire
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

CO2 Mig Mag Welding Wire

CO2 Mig Wire :
(1) Good Weldability
(2) Low Residue
(3) Low Splash
(4) High Reliability
CO2 Mig Mag Welding Wire:

Description:
The product has a nice welding property, and many advantages such as fast to melt, deposit efficiently, arc stable, less spatter, beautiful weld appearance, good oxidation resistance, low gas sensitivity, easy to operate, and so on, it is suitable for automatic, semi-automatic all-position welding facilities.
Application:
Our final products are mainly used in all-position welding of carbon steel, low alloy steel and low-alloy high-strength steel, widely used in constructional engineering, bridge construction, vehicle manufacture, shipbuilding, iron, steel framework and pressure vessel industry, can also be used in pipes and sheet The high-speed welding.

Specification

GB/T
AWS
JIS
DIN
BS
ER50-6
ER70S-6
YGW12
SG2
A18

Chemical Composition of Deposited Metal (%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035


≤0.50

Mechanical Properties or Deposited Metal

Item
Tensile Strength (σb)Mpa
Yield Point
(σ0.2)Mpa
Elongation
δ5%
Akv impact(J)
Guarantee value
≥500
≥420
≥22
≥27(-29°C)
General Result
525
435
28
95

Diameter And Reference Current(DC+)
Diameter(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Current(A)
50-120
70-240
80-350
170-450

Notice
To avoid the wire rust
,the wire should be located in
dry
environments, and open the packs just when welding
Please
clean out
the oil, rust, water and other impurities from the wire surface, before welding.






welding wire

Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or se

Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm

welding wire

low price and high quality
diameter :2.0mm-5.5mm

Brand/Model
HJ-10Mn2 / H10Mn2
Standards
Comfirm with GB H10Mn2,Correspond to AWS EH 14,JIS W41, DIN S4
Chemical components of welding wire

C
Mn
Si
S
P
Cu
Cr
Ni
≤0.12
1.50-1.90
≤ 0.070
≤0.035
≤0.035.
≤ 0.350
≤0.20
≤0.30
Mechanical properties of deposited metal
σ0.2
(MPa)
σb
(MPa)
δ5
(%)

AKV
(J)
≥400
480-650
≥22
≥27-20

Characteristics
Widely applied in the shipping, pressure vessel, pipe line industry, and it is available in the welding of heavy steel sheet with narrow bevel endsnarrow clearance structure and different kinds of diametrical circle welding seam.

Specification
φ2.0mm-5.0mm
Package
20kg plastic spool packing (only for 2.0mm)
25kg ,50kg,150kg,250kg,350kg transverse wind without core
30kg,50kg duncle
250kg wood drum packing
Or as per customers requirements

welding wire

Submerged Arc Welding Wire (copper, no copper, refined around, 25Kg / disk, 50Kg / plate)
VOD refining furnace cha
The main products are: stainless steel wire, stainless steel wire, stainless steel griddle wire, stainless steel spring wire, stainless steel heat-resistant wire, nickel and nickel alloy wire, copper and copper alloy wire, aluminum and aluminum alloy wire, titanium and titanium alloy wire, carbon steel and low-alloy steel wire, electric wire, electric wire, and a variety of wire processing products.Cr21Ni10ER308H00Cr21Ni10ER308LH00Cr21Ni10SiER308LsiH1Cr24Ni13ER309H00Cr24Ni13ER309LHOOCr24Ni13SiER309LSiH1Cr26Ni21ER310H1Cr30Ni9ER312H0Cr19Ni12Mo2H00Cr19Ni12Mo2H00Cr19Ni12Mo2SiER316LSiH0Cr20Ni14Mo3ER317H0Cr20Ni10TiER321H00Cr20Ni10NbH1Cr21Ni10Mn6ER307H0Cr19Ni9)H1Cr19Ni9ER302H1Cr19Ni9TiH0Cr13ER410SH1Cr13ER410H2Cr13ER420H3Cr13ER420JH1Cr17ER430H1Cr13NiMoH00Cr13Ni5MoH1Cr5MoH1Cr9MoER904LER367ER310MoER309MoER309LMoH00Cr12TiER409L.
ERNi-1,ERNiCr-3,ERNiCu-7,ERNiFeCr-7
Please contact me to know details

welding wire

CO2 welding wire ER49-1
Copper coated welding wire
We can produce all kinds of packing according to customers' request.

Brand: M&R
Feature: 1. stable arc;
2. low splashing;
3. high deposited effeciency;
4. suitable for all position;
Chemical composition (%):
C Mn Si S P Cu Cr Ni Mo V
0.07-0.15 1.40-1.85 0.8-1.15 0.035 0.025 0.50 0.15 0.15 0.15 0.03
Typical mechanical properties of deposited metal:
b(MPa) 0.2(MPa) 5(%) kv(J) shielded gas
550 430 28 85 CO2

welding wire

WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels, containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.

Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2

welding wire

welding wire for welding mild steel and 500MPa grade of high strength steel structures.

MG50-6


ER 50-6
(ER70S-6)
C 0.06-0.15
Mn 1.40-1.85
Si 0.80-1.15
S≤0.035
P≤0.025
Cu≤0.50

0.8
1.0
1.2
1.6
For welding mild steel and 500MPa grade of high strength steel structures.
welding wire

welding wire

welding wire for welding mild steel and 500MPa grade of high strength steel structures.



MG50-6


ER 50-6
(ER70S-6)
C 0.06-0.15
Mn 1.40-1.85
Si 0.80-1.15
S≤0.035
P≤0.025
Cu≤0.50

0.8
1.0
1.2
1.6
For welding mild steel and 500MPa grade of high strength steel structures.










welding wire

CO2 Mig Welding Wire AWS ER70S-6 SG2 suppliers ISO Stone Bridge Brand

welding wire:AWS ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

We are a large manufactory from China,we can supply CO2 gas shield welding wire
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

welding wire
wire dia:0.8mm-1.6mm
packing:15kg/spool with carton.
welding wire
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
It is suitable for welding in all position like Vertical/Horizontal.
Co2 welding wire will produce Low Hydrogen Weld
Compatibility
: CO2 gas shielded welding wire can be used for welding mild steel, high strength steel & low alloyed steel, co2 welding wire may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.

Applications:
Co2 welding wire is

suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.


MG50-6


ER 50-6
(ER70S-6)
C 0.06-0.15
Mn 1.40-1.85
Si 0.80-1.15
S≤0.035
P≤0.025
Cu≤0.50

0.8
1.0
1.2
1.6
For welding mild steel and 500MPa grade of high strength steel structures.

welding wire

welding wire
Supply good quality welding wire in reasonable price.
welding wire

Specification: 0.6mm,0.8mm,1.0mm,1.2mm,1.6mm,2.0mm
Packing form:5kg,15kg or 20kg winding in plastic spool in carton

Application:
Used for welding low carbon steel and low alloy steel structures, especially for welding of thin plates.

welding wire

Name: Welding wire
MIG Welding wire ,Co2
1)Suitable for use in such industries as:
Metallurgical industry
Bridge build
Welding wire
Gas Shieled welding wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge build
Product name: MIG welding wire , Co2 welding wire (70s---6) ; Gas shieled welding wire
Application:
Mainly used for welding low carbon alloy steel , widely used in industries of vechicles , bridge-engineering , steel structures , shipping manufacture .
Mechanical Property:
Joint Strength Succumb Strength Elongation index Shock Value
( MPA) (MPA) 0.2 5% AKV -29(J)
550 430 30 90
Chemical Composition:
C Mn Si S P Cu other
0.08% 1.52 0.92% 0.015% 0.020% 0.2% <=0.50
Package:
Dia 0.6mm 0.8mm 0.9mm 1.0mm 1.2mm 1.6mm
Current 25---110 40-----140 50----200 70---250 80---350 170-----450
Voltage 12-----19 16------21 17-----25 17------27 18----30 23------43
Weight/spool 1/5/10 15/20 15/20 15/20 20 20
(KG)

welding wire

AWS ER70S-6 co2 welding wire Useing the advanced Electroplating copper coated technology

Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

1)Stable electric arc
2)low splashing, high deposition efficiency
3)good anti pore property
4)can be welded automatical
Features:
Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification:
0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f:

10kg, 15kg or 20kg packed in plastic spool.
Certificate:

ISO 9001:2000

welding wire

co2 gas shielding welding wire ER 70S-6
CO2 gas shielding welding wire
ER70S-6
packing: 5-20kg each spool available
diameter: 0.6-1.2mm

welding wire

welding wire:ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm
Minimum Order Quantity: 10 Metric Ton
Packaging Details: 10kg, 15kg or 20kg packed in plastic spool.
Delivery Time: 15~25 days after receive the advance.
Payment Terms: T/T , L/C
Supply Abiity: 1500 Ton per month
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

supply welding wire with high quality!

welding wire

welding wire for welding mild steel and 500MPa grade of high strength steel structures.

CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
It is suitable for welding in all position like Vertical/Horizontal.
Co2 welding wire will produce Low Hydrogen Weld
Compatibility
: CO2 gas shielded welding wire can be used for welding mild steel, high strength steel & low alloyed steel, co2 welding wire may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.

Applications:
Co2 welding wire is

suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.


MG50-6


ER 50-6
(ER70S-6)
C 0.06-0.15
Mn 1.40-1.85
Si 0.80-1.15
S≤0.035
P≤0.025
Cu≤0.50

0.8
1.0
1.2
1.6
For welding mild steel and 500MPa grade of high strength steel structures.

welding wire

WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels, containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.

Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2

Packing
Gauges
0.8mm-1.6mm
Spool
100mm
200mm
300mm
Net weight
1kg
5kg
15kg
20kg

Typical Chemical Analysis
C
Si
P
S
Cr
Ni
Cu
0.06-0.15
0.45-0.75
≤0.025
≤0.035
-
-
≤0.50

Mechanical properties of deposited
Yield Strength
Elongation
Charpy-V AKV
≥420
≥22
≥27(-18)

welding wire

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm

Minimum Order Quantity: 10 Metric Ton
Packaging Details: 10kg, 15kg or 20kg packed in plastic spool.
Delivery Time: 10~20 days after receive the advance.
Payment Terms: T/T , L/C
Supply Abiity: 1500 Ton per month
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm
CO2 Welding Wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

welding wire

welding wire (ER70S-6) 5kgs/spool 15kgs/spool

welding wire

"FARINA" brand CO2 welding wire ER70S-6
We can produce all kinds of packing according to customers' request.
Brand: FARINA
Feature: 1. stable arc;
2. low splashing;
3. high deposited effeciency;
4. suitable for all position;
Chemical composition (%):
C Mn Si S P Cu Cr Ni Mo V
0.07-0.15 1.40-1.85 0.8-1.15 0.035 0.025 0.50 0.15 0.15 0.15 0.03
Typical mechanical properties of deposited metal:
b(MPa) 0.2(MPa) 5(%) kv(J) shielded gas
550 430 28 85 CO2

welding wire

CO2 welding wire ER70S-6
Copper coated welding wire
We can produce all kinds of packing according to customers' request.

Brand: M&R
Feature: 1. stable arc;
2. low splashing;
3. high deposited effeciency;
4. suitable for all position;
Chemical composition (%):
C Mn Si S P Cu Cr Ni Mo V
0.07-0.15 1.40-1.85 0.8-1.15 0.035 0.025 0.50 0.15 0.15 0.15 0.03
Typical mechanical properties of deposited metal:
b(MPa) 0.2(MPa) 5(%) kv(J) shielded gas
550 430 28 85 CO2

welding wire

welding wire
packing: 270mm black good spool,
net weight: 15kg / 20kg
wire diameter: 0.8mm -- 1.6mm
welding wire
For welding low carbon and high strength steel structures of 500MPa.
Shield gas: CO2
Wie Diameter: 0.8mm - 1.6mm
Spool: 200mm 270mm 300mm
Net Weight: 1Kg / 5Kg / 15Kg / 20Kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06 - 0.15
1.40 - 1.85
0.80 - 1.15
¡Ü0.025
¡Ü0.035
-
-
¡Ü0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy - V Akv
¡Ý420
¡Ý500
¡Ý22
¡Ý27(-29)

Friday, September 9, 2011

welding wire

be made of excellent steel by drawing, straightening and copper coating.
It possesses excellent welding technological properti
selling point:
1. low welding costs
2. high productivity and low electricity consumption
3. easy to operate
4. little deformation after welding
5. wide applicability suitable for welding thin, medium and thick plates
function:
the welding wire is used for welding low carbon steel and low alloy steel,such as
automotive industry
shipbuilding
civil works
heavy-duty machine
boilder
pressure vessel ect
advantage:
stab arc
beautiful bead
less spatter
excellent welding technological properties

welding wire

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm

Minimum Order Quantity: 1Ton
Packaging Details: 10kg, 15kg or 20kg packed in plastic spool.
Delivery Time: 10~20 days after receive the advance.
Payment Terms: T/T , L/C
Supply Abiity: 3000 Ton per month
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm
Minimum Order Quantity: 10 Metric Ton
Packaging Details: 10kg, 15kg or 20kg packed in plastic spool.
Delivery Time: 10~20 days after receive the advance.
Payment Terms: T/T , L/C
Supply Abiity: 1500 Ton per month
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

CO2 Welding Wire
Our factory supplying good quality ER70S-6 welding wire in reasonable prices.Certificate:ISO 9001:2000
welding wire/gas shielded welding wire/CO2 gas shielded welding wire/copper welding wire/ER50-6/ER70s-6
1) ER70S-6 solid wire is suitable for CO2 shielded welding of low carbon steel and
low alloy steel, particularly suitable for welding rolling stock, container, engineering
2) Stable electric arc, low splashing, high deposition efficiency and good anti pore
property. It can carry out welding at all positions
3) Specifications: 0.6mm, 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm, 2.0mm
Packing:1kg/5kg/12.5kg/13.5kg/15kg/20kg per plastic spool

welding wire

welding wire:ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm
Minimum Order Quantity: 10 Metric Ton
Packaging Details: 10kg, 15kg or 20kg packed in plastic spool.
Delivery Time: 15~25 days after receive the advance.
Payment Terms: T/T , L/C
Supply Abiity: 1500 Ton per month
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

welding wire ER70S-6 is a copper carbon steel and low alloy steel welding wire, with the good hot metal mobility
welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

Supply good quality welding wire in reasonable price.
welding wire

Specification: 0.6mm,0.8mm,1.0mm,1.2mm,1.6mm,2.0mm
Packing form:5kg,15kg or 20kg winding in plastic spool in carton

Application:
Used for welding low carbon steel and low alloy steel structures, especially for welding of thin plates.

1.2mm ER70S-6

ER70S-6 welding wire(copper coated)
1.Mig/CO2/SG2 welding wire
2.Dia:0.8mm-1.6mm
3.Package:5Kg,15Kg
4.if 20',about 15days
CO2 Mig welding wire ER70S-6(copper coated):

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine,railway construction,pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

welding wire

welding wire :
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm

welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

CO2 welding wire ER49-1
Copper coated welding wire
We can produce all kinds of packing according to customers' request.

Brand: M&R
Feature: 1. stable arc;
2. low splashing;
3. high deposited effeciency;
4. suitable for all position;

welding wire

welding wire:
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Certificate: ISO 9001:2000

welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

welding wire
1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
CO2 Welding Wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

welding wire

welding wire:ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

CO2 Welding Wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

welding wire

weiding wire
Copper coated welding wire in drum packing
Features:
For welding low carbon and high strength steel structures of 500MPa,such as ships,bridge,build construction machine etc.
Packing:
precious layer welding wire in drum,within silicon gel,then put drum packing on pallet,every drums on one palletThe net weight of every drum is 250 kilograms

ICCS, ABS, LR, TUV, DB,NK, REACH, CWB

welding wire

co2 Welding wire:AWSER70S-6 0.8mm-2.0mm
Submerged arc welding wire:2.5mm-5.0mm
Flux-cored welding wire:E71T-1 E71T-11 0.8-1.6
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features
: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
Welding wire chemical
Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50
Mechanical properties
of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2

Specification and reference
current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

welding wire

welding wire Type: AWS ER70S-6Dia.: 0.8mm; 0.9mm; 1.0mm; 1.2mm; 1.6mm; 2.0mm.

CO2 gas shielded welding wire

CO2 gas-shielded welding wires are primarily used for all position welding of steel
structures, pressure vessels, containers, construction machinery, ships, railways,
automobiles, motorcycles, etc.
Type: AWS ER70S-6Dia.: 0.8mm; 0.9mm; 1.0mm; 1.2mm; 1.6mm; 2.0mm.
Kinds: 5kg; 15kg; 20kg
Reel: plastic spool-270mm or 300mm
Package: standard export paper carton

welding wire

Summary Table of Gas-shielded Solid Welding Wire
Model GB AWS Current Main Applications
Summary Table of Gas-shielded Solid Welding Wire
Model
GB
AWS
Current
Main Applications


DC+
Used for welding atmospheric corrosion-resistant steel structures with corresponding strength, such as locomotive vehicles, offshore engineering, bridges, etc.
ER49-1

DC+
Used for welding low-carbon steel and some low-alloy steel structures.
ER50-3
ER70S-3
DC+
1. Used for welding low-carbon steel thin plates.
2. Used for welding low-carbon steel parts with thorough surface treatment.
ER50-4
ER70S-4
DC+
1. Used for welding sheet metal and thin plates.
2. Used for welding steel pipes.
ER50-6
ER70S-6
DC+
1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
ER50-G
ER70S-G
DC+
1. Used for welding all kinds of 500MPa structural steel parts, thick plates and thick pipelines.
2. Used for high speed welding on 500MPa base metals.
ER60-G
ER90S-G

Suitable for welding 600MPa high strength steel structures, such as construction machinery, pipelines, ships, pressure vessels, etc.
ER60-G
ER90S-G

Suitable for welding 600MPa high strength steel structures, such as construction machinery, etc.
ER70-G
ER100S-G

Suitable for welding 700MPa high strength steel structures, such as construction machinery, hoisting machinery, bridges, pipelines, ships, pressure vessels, etc.
ER80-G
ER110S-G
DC+
Suitable for welding high strength structures with tensile strength of 790MPa. It can be used for welding some key structures, such as pressure vessels, construction machinery, hoisting machinery, ships, mining machinery, etc.
ER55-G

DC+

welding wire

welding wire:ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

1) Stable electric arc
2) Low splashing
3) High deposition efficiency
4) Welds at any position
5) Diameter: , 0.8-2.0mm
Minimum Order Quantity: 10 Metric Ton
Packaging Details: 10kg, 15kg or 20kg packed in plastic spool.
Delivery Time: 15~25 days after receive the advance.
Payment Terms: T/T , L/C
Supply Abiity: 1500 Ton per month
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features:
Stable electric arc, low splashing, high deposition efficiency and
good anti pore property, It can be welded automatically or semi-automatical.
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc.
Specification:
0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f:
10kg, 15kg or 20kg packed in plastic spool.
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
≥500
≥420
≥22
-29°
C≥27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

ER70S-6 is a copper carbon steel and low alloy steel welding wire, with the good hot metal mobility and the good resisting crack

welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

The annual output of CO2 Gas-shielded welding wire run up to 30000MT .

welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

welding wire

welding wire
wire dia:0.8-1.6mm
packing:15kg/spool with carton
welding wire
The series of welding wires can be used to welding low carbon steel and low alloyed steel structure, such as ships, vehicles, bridges, boilers and buildings etc.
CO2gas shielding welding wireshave excellent mechanical performance such as fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam. Suitable for all-position welding work.
MIG/MAG Wire ER70S-6 & MIG/MAG Wire ER70S-3 etc.
PACKING: Precision layer wire on the black metal spool or plastic spool covered with the wax paper, each
Spool in ploybag with two big silicon in the carton, then put on wooden pallets

Gauges
0.8-1.6 MM
Spool
100 MM 200 MM 270 MM 300 MM
Net weight
1kg
5kg
15kg
20kg
Applications: Widely used as welding carbon steel wires in shipbuilding, Bridge building, machinery manufacturing and general welding purposes.

welding wire

Argon Arc Welding Wire
1. Diameter: 1.0mm,2 .0mm, 3.0mm,4.0mm
2. Packed in 5kg or 15kg carton.
3. Flat surface.
Argon Arc Welding Wire


1. Diameter: 1.0mm,2 .0mm, 3.0mm,4.0mm
2. Packed in 5kg or 15kg carton.
3. Flat surface.


Chemicals Content as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5





Uses:

Our products are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.

welding wire

CO2 welding wire ER70S-6
Copper coated welding wire
We can produce all kinds of packing according to customers' request.

Brand: M&R
Feature: 1. stable arc;
2. low splashing;
3. high deposited effeciency;
4. suitable for all position;
Chemical composition (%):
C Mn Si S P Cu Cr Ni Mo V
0.07-0.15 1.40-1.85 0.8-1.15 0.035 0.025 0.50 0.15 0.15 0.15 0.03
Typical mechanical properties of deposited metal:
b(MPa) 0.2(MPa) 5(%) kv(J) shielded gas
550 430 28 85 CO2

CO2 Mig Welding Wire AWS ER70S-6 SG2 ISO Stone Bridge Brand

welding wire:AWS ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

We are a large manufactory from China,we can supply CO2 gas shield welding wire
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

welding wire
wire diameter:0.6-1.6mm
packing:15kg/spool with carton
welding wire
wire diamter:0.6-1.6mm



MG50-6


ER 50-6
(ER70S-6)
C 0.06-0.15
Mn 1.40-1.85
Si 0.80-1.15
S≤0.035
P≤0.025
Cu≤0.50

0.8
1.0
1.2
1.6
For welding mild steel and 500MPa grade of high strength steel structures.

welding wire

AWS ER70S-6 co2 welding wire Useing the advanced Electroplating copper coated technology
Electroplating copper coated technology for the welding wires.
Features:
1) Our wire is copper coated solid wire for CO2 welding for general engineering and structural application
2) Gives spatter-free welding with CO2 gas and Ar + CO2gas mixtures
3) The weld deposit is free from porosities with very smooth and uniform weld bead
4) Size (diameter): 0.6 - 2.0mm
Packing:
1) 5kg / 12.5kg / 13.5kg / 15kg precision layer wound plastic spools
2) Sealed in moisture-proof air tight plastic bag and cartons with silica
gel drying agent to prevent corrosion and rust, increase shelf life of
wires and cartons on the pallet
Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

welding wire (ER70S-6)

Thursday, September 8, 2011

welding wire

Description: welding wire co2
1)good weldability
2)efficient cladding
3)low residue
4)high reliability
welding wire co2
(AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
welding wire co2
Introduction
: Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Chemical Composition of Welding Wire(%)
C
Mn
Si
P
S
Cu
0.06-0.15
0.80-0.15
0.80-1.15
≤0.025
≤0.035
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
15/18
15/18
15/20
15/20
15/20


welding wire

WELDING WIRE
1) Sizes: 0.8-1.6mm
2) high quality & lower price
3) fast delivery

WELDING WIRE
1) MIG/MAG wire: ER70S-6, ER70S-7, ER80S-G, ER80S-D2
2) Submerged arc welding wire EL8, EL12, EM12, EH14, EA2
3) Size:0.8mm,1.0mm,1.2mm,1.6mm

Where to Use:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers.

We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company

CO2 Mig Welding Wire AWS ER70S-6

CO2 gas-shield welding wire:AWS ER70S-6,DIN SG2:0.8~2.0mm
Submerged Arc Welding Wire

CO2 gas shield welding wire AWS ER70s-6
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

CO2 Mig Welding Wires SG2 AWS ER70S-6 ISO

welding wire:AWS ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

We are a large manufactory from China,we can supply Stone Bridge Brand CO2 gas shield welding wire
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

weld wire ER70S-6
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.STANDARD: ER70S-6;ER49-1
3.SURFACE:COPPER COAT
4.SPOOL: WHITE OR BLACK
welding wire ER70S-6
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.SURFACE TREATMENT:COPPER COATED
3.PACKING: AS PER CUSTOMER REQUEST
4.SPOOL: WHITE OR BLACK ETC
5. KIND OF SPOOL: PLASTIC OR METAL WIRE
6. STANDARD: ER70S-6,ER49-1

welding wire

welding wire
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.STANDARD: ER70S-6;ER49-1
3.SURFACE:COPPER COAT
4.SPOOL: WHITE OR BLACK
welding wire ER70S-6
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.SURFACE TREATMENT:COPPER COATED
3.PACKING: AS PER CUSTOMER REQUEST
4.SPOOL: WHITE OR BLACK ETC
5. KIND OF SPOOL: PLASTIC OR METAL WIRE
6. STANDARD: ER70S-6,ER49-1

welding wire

welding wire
It is used for collating steel nails.
we specialized in this products.
welding wire
It is used for collating steel nails.
we specialized in this products many years,we know what's your favour.

It have two size is popular 0.7mm and 0.8mm.
Packing: about 19.5kg/spool.
If you are interesting in it,please contact with me. We can discuss each other.

welding wire

stainless steel welding wire
1complete specification
2largest production base in China
3latest production equipment
4R&D
stainless steel welding wire
Our company specialized in producing stainless steel welding wire and valve steel for many years

we have the independent
research and development ability

we can produce
special wires

according to
customers' demands

..

Type
C,≤,%
Si,%
Mn,%
P,≤,%
S,≤,%
Ni,≤,%
Cr,%
Mo,%
others,%
austenite
H0Cr21Ni10
0.06
≤0.60
1.00~2.50

9.00~11.00
19.50~22.00


H00Cr21Ni10
0.03
≤0.60
1.00~2.50
9.00~11.00
19.50~22.00


H1Cr24Ni13
0.12
≤0.60
1.00~2.50
12.00~14.00
23.00~25.00


H1Cr24Ni13Mo2
0.12
≤0.60
1.00~2.50
12.00~14.00
23.00~25.00
2.00~3.00

H1Cr26Ni21
0.15
0.2~0.50
1.00~2.50
20.00~22.50
25.00~28.00


H0Cr26Ni21
0.08
≤0.60
1.00~2.50
20.00~22.50
25.00~28.00


H0Cr19Ni12Mo2
0.08
≤0.60
1.00~2.50
0.030
0.020
11.00~14.00
18.00~20.00
2.00~3.00

H00Cr19Ni12Mo2
0.03
≤0.60
1.00~2.50

11.00~14.00
18.00~20.00
2.00~3.00

H00Cr19Ni12Mo2Cu2
0.03
≤0.60
1.00~2.50
11.00~14.00
18.00~20.00
2.00~3.00
Cu:1.00~2.50
H0Cr20Ni14Mo3
0.06
≤0.60
1.00~2.50
13.00~15.00
18.50~20.50
3.00~4.00

H0Cr20Ni10Ti
0.06
≤0.60
1.00~2.50
9.00~10.50
18.50~20.50

Ti:9*C%~1.00
H0Cr20Ni10Nb
0.08
≤0.60
1.00~2.50
9.00~11.00
19.00~21.50

Nb:10*C%~1.00
H1Cr21Ni10Mn6
0.10
0.2~0.60
5.00~7.00
9.00~11.00
20.00~22.00


ferrite
H0Cr14
0.06
0.30~0.70
0.30~0.70
0.030
0.030
≤0.60
13.00~15.00


H1Cr17
0.10
≤0.50
≤0.60

15.50~17.00


martensite
H1Cr13
0.12
≤0.50
≤0.60
0.030
0.030

11.50~13.50


H1Cr5Mo
0.12
0.15~0.35
0.40~0.70
≤0.30
4.00~6.00
0.40~0.60


CO2 Mig Welding Wires er70s-6

welding wire:AWS ER70S-6:0.8~2.0mm
Submerged Arc Welding Wire:2.5~5.0mm
Flux-cored wire: E71T-1:1.2~1.6mm

We are a large manufactory from China,we can supply Stone Bridge Brand CO2 gas shield welding wire
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

welding wire

welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position..
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550



welding wire

welding wire
ISO9001,TUV DB,CE
0.8 0.9 1.01.2 1.6mm
Aws A5.18 er70S-6
For construction,mechanical structure etc
MIG mig welding wire
ISO9001,TUV DB,CE
0.8 0.9 1.01.2 1.6mm
Aws A5.18 er70S-6
For construction,mechanical structure etc
Co2 welding wire
Model:AWS A5.18 ER70S-6
Specification:
Size:0.8MM 0.9MM 1.0MM 1.2MM 1.6MM
Application:suitable to single or multiple weld welding of carbon steel and low alloy steel strength grade of 500Mpa(E.G the welding of vehicle,,bridge,construction and mechanical structure etc)also applicable to high speed welding of thin plates and pipes etc.
Feature:
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position
Packing;
Net weight 1kg 5kg 15kg
Precision layer wound on plastic spool,each spool in a box then boxes on wooden pallets
Chemical composition(%)

C

Mn

Si

S

P

Cu

Cr

Ni

Mo

V
0.10
1.50-2.00
0.30
0.010
≤0.012
0.02-0.08
0.35-1.55
0.5-1.25
0.002-0.008
0.03
Typical mechanical properties of deposited metal:
T/S(Mpa)
Y/S(MPA)
A(%)
Akv(J)
Shielded gas
550
430
28
85
CO2
We offer good products, excellent service, favorable prices, timely delivery and has established long term business relationship with many foreign customers.
We are a professional manufacturer and exporter of metal welding wire and rods in China. Established in 2004 with registered capital of 641 million US dollars, we specialize in stainless steel wires, stainless steel spring wires, hydrogen steel wires, flux-cored wires, carbon steel electrodes, stainless steel tiny wires, MIG welding wires, submerged arc welding wires, copper welding wires and other related products. Our products are widely used in electronics, communication, instruments and ...
View more
>>
Basic Information
Business Type:
Manufacturer, Trading Company
Product/Service (We Sell):
stainless steel welding wire,stainless steel rod,stainless steel tiny wire,stainless steel bright wire,tin brass welding wire,tin solder wire,tin solder bar,aluminum ring,carbon steel electrode,aluminum ring
Number of Employees:
51 - 100 People
Trade & Market
Main Markets:
North America
South America
Eastern Europe
Southeast Asia
Africa
Oceania
Mid East
Eastern Asia
Western Europe
Total Annual Sales Volume:
US$10 Million - US$50 Million
Export Percentage:
31% - 40%
Factory Information
Management Certification:
ISO 9001:2008
Contract Manufacturing:
OEM Service Offered Design Service Offered Buyer Label Offered

CO2 Mig welding wire ER70S-6(Dia0.8,1.0,1.2,1.6mm)

ER70S-6:0.8,1.0,1.2,1.6mm
Certificate:ISO9001:2000
Free sample be provided
Professional manufacturer

Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

Stone Bridge CO2 mig Welding Wire ER70S-6

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
(AWS ER70S-6)
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Packing
Net weight:5kg/spool,12.5kg/spool,15kg/spool,20kg/spool
a spool/carton,72cartons/pallet or as request




welding wire

welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20

CO2 Mig welding wire sg2 supplier

MIG WELDING WIRE SG2
1.Copper coated welding wire
2.Dia:0.8mm-1.6mm
3.Packing:5Kg,15Kg,250Kg
4.ISO9001:2000
welding wire
sg2 ER70S-6/
Mig welding wire/CO2 welding wire
Specification:
1)Size: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
2)Application: Suitable to single or multiple weld welding of carbon steel and low alloy steel with strength grade of 500MPa (e.g. the welding of vehicle, bridge, construction, and mechanical structure etc), also applicable to high speed welding of thin plates and pipes etc.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position

Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)


/

welding wire

welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40
years or so, it has been developed as a kind of important melt welding method and widely
applied to all kinds of fields like automotive industry, construction machinery production,
shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical
industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been
developing rapidly. It has accounted for 40-50% in welding materials in some industrialized
countries. In china, it has been popularized in many departments, and gradually it is partly
replacing manual arc welding with electrodes gradually. Some of its characteristics are as
follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-
resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has
low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550

welding wire

welding wire.
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery
GB/T:ER50-6 DIN:SG2 JIS:YGW12

AWS:ER70S-6 BS:A18 EN:G3Sil

PACKING
SIZE
DIAMETER OF SPOOL
N.W
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1KG,5KG,15KG,18KG,20KG



CHEMICAL COMPOSITION(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
MECHANISM
YIELD σ
0.2
(Mpa)
STRENGTH σ
b
(Mpa)
ENGLOATIONδ
5
(%)
AK IMPACT(J)
≥420
≥500
≥22
≥27(-29)


DIAMETER OF WELDING WIRE(mm)
φ0.8
φ1.0
φ1.2
φ1.6



40~140
50~220
80~350
120~550



CHARACTERISTICS:

1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate all position welding.
4. Very low hydrogen content in the weld and lower nitrogen content excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability suitable for welding thin, medium and thick plates.

(DIA 0.8 0.9 1.0 1.2 1.6 2.0) Welding wire ER70S-6 (CE Approval)

DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 (CE approval)
1.Gas-shielded Welding Wire
2.DIN SG2 AWS ER70S-6
DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 15KG/SPOOL ISO APPROVAL
WELDING WIRE,mig welding wire,co2 welding wire solid welding wire
Gas shielded welding wire
WELDING WIRES ELECTRODES

Detailed Product Description Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000
WELDING POSITION :

CONTACT WITH Ms Alice

CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
























1.2mm ER70S-6

ER70S-6 welding wire(copper coated)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
CO2 Mig welding wire ER70S-6

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine,railway construction,pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)