We can supply high quality welding wires, TIG rods, and all kinds of tungsten electrodes.
MIG Wire and TIG Rods ( welding wire
ISO9001
Aluminum Wire & Rod
AWS Code
Chemical Composition (%)
Mechanical Properties
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
Impurity
Melt
Density
ER1100
0.95
0.95
0.05~0.20
0.05
—
—
0.1
—
0.15
643~657°C
2.7 g/m
3
ER4043
4.5~6.0
0.8
0.3
0.05
0.05
—
0.1
0.2
0.15
573~632°C
2.69 g/m
3
ER4047
11.0~13.0
0.8
0.3
0.15
0.1
—
0.2
—
0.15
577~582°C
2.66 g/m
3
ER5356
0.25
0.4
0.1
0.05~0.2
4.5~5.5
0.05~0.2
0.1
0.06~0.20
0.1
571~635°C
2.66 g/m
3
Certification
ISO9001
Saturday, May 28, 2011
MIG co2 welding wire ER70S-6
Small splash, produce gas less, welding, smooth, take off pierced the second easy arc starting, welding and firm.
Product name:
welding wire er70s 6
Application:
Mainly used for welding low carbon alloy steel, widely used in industries of vehicles, bridge-engineering, machine-engineering, steel structures, shipping manuf.
Mechanical Property:
Joint Strength
(MPA)δ
succumb strength
(MPA) δ0.2
elongation index
δ5%
shock value
Akv
-29 (J)
550
430
30
90
Chemical Composition:
C
Mn
Si
S
P
Cu
Other
0.08%
1.52%
0.92%
0.015%
0.020%
0.2%
≤0.50
Package :
Dia
0.6mm
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
25-110
40-140
50-200
70-250
80-350
170-450
Voltage
12-19
16-21
17-25
17-27
18-30
23-43
Weight/spool
(KG)
1/5/10
15/20
15/20
15/20
20
20
Product name:
welding wire er70s 6
Application:
Mainly used for welding low carbon alloy steel, widely used in industries of vehicles, bridge-engineering, machine-engineering, steel structures, shipping manuf.
Mechanical Property:
Joint Strength
(MPA)δ
succumb strength
(MPA) δ0.2
elongation index
δ5%
shock value
Akv
-29 (J)
550
430
30
90
Chemical Composition:
C
Mn
Si
S
P
Cu
Other
0.08%
1.52%
0.92%
0.015%
0.020%
0.2%
≤0.50
Package :
Dia
0.6mm
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
25-110
40-140
50-200
70-250
80-350
170-450
Voltage
12-19
16-21
17-25
17-27
18-30
23-43
Weight/spool
(KG)
1/5/10
15/20
15/20
15/20
20
20
AWS A5.18/ER70S-6 welding wire
CO2 welding wire,AWS ER70S-6
0.8mm,1.0mm, 1.2mm,1.6mm
Suitable for low carbon steel and low alloy steel,etc.
CO2 welding wire
1. a double deoxidized copper Coated Solid Steel Wire.
2.Suitable for welding in all position like Vertical/Horizontal. It will produce Low Hydrogen Weld
High Deposition Rate & Deep penetration.
Ideally suited for unclean & rusty surfaces. Stable Arc with very low spatter loss.
3.Compatibility:CO2 wire can be used for welding mild steel, high strength steel & low alloyed steel, it may be used on steels with moderate presence of rust & mill scale. High current is also permitted with this wire.
4. Applications: Suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required. Trouble Shooting:
0.8mm,1.0mm, 1.2mm,1.6mm
Suitable for low carbon steel and low alloy steel,etc.
CO2 welding wire
1. a double deoxidized copper Coated Solid Steel Wire.
2.Suitable for welding in all position like Vertical/Horizontal. It will produce Low Hydrogen Weld
High Deposition Rate & Deep penetration.
Ideally suited for unclean & rusty surfaces. Stable Arc with very low spatter loss.
3.Compatibility:CO2 wire can be used for welding mild steel, high strength steel & low alloyed steel, it may be used on steels with moderate presence of rust & mill scale. High current is also permitted with this wire.
4. Applications: Suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required. Trouble Shooting:
MIG gas shield welding wire
CO2 welding wire
ISO9001,CE,TUV
AWS A5.18 ER70S-6
0.8,0.9,1.0,1.2,1.6mm
for welding of carbon steel and low alloy steel
CO2 welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
5. suitable for all position
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2
ISO9001,CE,TUV
AWS A5.18 ER70S-6
0.8,0.9,1.0,1.2,1.6mm
for welding of carbon steel and low alloy steel
CO2 welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
5. suitable for all position
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2
MIG solder wire (33)
We can supply high quality welding wires, TIG rods, and all kinds of tungsten electrodes.
MIG Wire and TIG Rods ( welding wire
We can supply high quality welding wires, TIG rods, and all kinds of tungsten electrodes.
MIG solder wire
Specification:
1) Size: 0.6mm-1.6mm
2) Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position
MIG Wire and TIG Rods ( welding wire
We can supply high quality welding wires, TIG rods, and all kinds of tungsten electrodes.
MIG solder wire
Specification:
1) Size: 0.6mm-1.6mm
2) Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position
MIG solid weld wires for gas shielding
It is suitable for all-position welding; applicable to wide current range.
It is suitable for all-position welding; applicable to wide current range; stable eletric arc under the operating condition of low current; few spark spatters; widely applied to structure welding like butt joint welding and fillet welding in the industries of shipbuilding, bridge, architecture and machinery.
It is suitable for all-position welding; applicable to wide current range; stable eletric arc under the operating condition of low current; few spark spatters; widely applied to structure welding like butt joint welding and fillet welding in the industries of shipbuilding, bridge, architecture and machinery.
MIG solid welding wire 0.8mm
Mig/co2 wire ER70S-6
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig /co2 welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig /co2 welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
MIG solid welding wire 1.2mm
Mig/co2 wire ER70S-6
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig /co2 welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig /co2 welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
MIG suvirinimo viela ER70S-6
1,welding wire Application building,ships,briges,ect
2,good weldability
3,low residue
4,low splash
5,high reliability
1,
welding wire AWS A5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4,0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5,15kg, 20kg iron spool layer wind
6,100kg, 250kg, 350kg drum packing
2,good weldability
3,low residue
4,low splash
5,high reliability
1,
welding wire AWS A5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4,0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5,15kg, 20kg iron spool layer wind
6,100kg, 250kg, 350kg drum packing
MIG welding wire 0.8mm
Mig/co2 wire ER70S-6
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig /co2 welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig /co2 welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
MIG welding wire AWS ER70S-6
CO2 gas shield welding wire ER70S-6 has the excellent mechanical performance such as high depositing speed.
This series of welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
This series of welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG welding wire AWS ER70S-6
Small splash, produce gas less, welding, smooth, take off pierced the second easy arc starting, welding and firm.
Description
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with
GB/T 8110 ER50-6 ISO 636-A-W 42 3 W3Sil
AWS A5.18 ER70S-6 ISO 636-B-W 49A 3 W6
BS EN 1668-W 42 3 W3Sil JIS Z3316 YGT50
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV (J)
≥420
≥500
≥22
≥27(-30
°C
)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Description
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with
GB/T 8110 ER50-6 ISO 636-A-W 42 3 W3Sil
AWS A5.18 ER70S-6 ISO 636-B-W 49A 3 W6
BS EN 1668-W 42 3 W3Sil JIS Z3316 YGT50
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV (J)
≥420
≥500
≥22
≥27(-30
°C
)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
MIG welding wire AWS ER70S-6
ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
stable arc,little splash,good welding seam
Free sample
CO2 Gas Shielded Welding Wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER70s-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER70s-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Certificate:ISO9001:2000
stable arc,little splash,good welding seam
Free sample
CO2 Gas Shielded Welding Wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER70s-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER70s-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
AWS A5.20 E71T-1 welding material
welding material AWS E71T-1 (manufacturer ) has
been arrpoved by CCS,ABS,DNV,LR,GL,
BV,NK,KR,RINA .
welding material
AWS E71T-1 (manufacturer )
it used for high efficiency welding in all positions.
Chemical Composition of deposited Metal(%)
C
Mn
Si
S
P
0.05
1.26
0.31
0.009
0.011
Mechanical Properties of Deposited Metal
σb (MPa)
tensile strength
σs (MPa)
yield strength
σ5(%)
elongation
Akv(J)
590
510
28
(-20
0
C)116
Dia.(mm)
Shielding Gas
polarity
1.2/1.4/1.6
Co
2
DC(+)
been arrpoved by CCS,ABS,DNV,LR,GL,
BV,NK,KR,RINA .
welding material
AWS E71T-1 (manufacturer )
it used for high efficiency welding in all positions.
Chemical Composition of deposited Metal(%)
C
Mn
Si
S
P
0.05
1.26
0.31
0.009
0.011
Mechanical Properties of Deposited Metal
σb (MPa)
tensile strength
σs (MPa)
yield strength
σ5(%)
elongation
Akv(J)
590
510
28
(-20
0
C)116
Dia.(mm)
Shielding Gas
polarity
1.2/1.4/1.6
Co
2
DC(+)
MIG welding wire ER70S-6(ISO Certified)
SG2/SAW/CO2/MIG welding wire
D:0.8-2.0mm
P:5. 15.18.20kg/Spool (D200 270 300 K300)
ISO.BV.SGS.COC.IEI Certified
Free Sample
SG2/SAW/CO2/MIG welding wire ER70S-6-copper coated
Brand name :stone bridge /Hero brand
CO2/MIG WELDING WIRE
ER70S-6
Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable
D:0.8-2.0mm
P:5. 15.18.20kg/Spool (D200 270 300 K300)
ISO.BV.SGS.COC.IEI Certified
Free Sample
SG2/SAW/CO2/MIG welding wire ER70S-6-copper coated
Brand name :stone bridge /Hero brand
CO2/MIG WELDING WIRE
ER70S-6
Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable
MIG welding wire ER70S-6
MIG welding wire
ISO9001,CE,TUV,CCS
0.8,0.9,1.0,1.2,1.6mm
AWS ER70S-6
for vehicles, bridge, construction, machinery etc.
MIG welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Feature:
1. stable arc
2. low splashing
3. less weld pore sensitivity
4. good all-position weldability
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
Akv(-30)(J)
Shielded gas
550
430
30
85
CO2
ISO9001,CE,TUV,CCS
0.8,0.9,1.0,1.2,1.6mm
AWS ER70S-6
for vehicles, bridge, construction, machinery etc.
MIG welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Feature:
1. stable arc
2. low splashing
3. less weld pore sensitivity
4. good all-position weldability
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
Akv(-30)(J)
Shielded gas
550
430
30
85
CO2
MIG welding wire ER70S-6
CO2 welding wire, AWS ER70S-6
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg
Suitable for low carbon steel and low alloy steel
CO2 welding wire ER70S-6
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
It is suitable for welding in all position like Vertical/Horizontal.
Co2 welding wire will produce Low Hydrogen Weld
Compatibility: CO2 gas shielded welding wire can be used for welding mild steel, high strength steel & low alloyed steel, co2 welding wire may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.
Applications: Co2 welding wire is suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg
Suitable for low carbon steel and low alloy steel
CO2 welding wire ER70S-6
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
It is suitable for welding in all position like Vertical/Horizontal.
Co2 welding wire will produce Low Hydrogen Weld
Compatibility: CO2 gas shielded welding wire can be used for welding mild steel, high strength steel & low alloyed steel, co2 welding wire may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.
Applications: Co2 welding wire is suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.
MIG welding wire ER70S-6
CO2 welding wire,AWS ER70S-6
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg,etc
Suitable for low carbon steel and low alloy steel,etc.
CO2 welding wire
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
Suitable for welding in all position like Vertical/Horizontal.
It will produce Low Hydrogen Weld
High Deposition Rate & Deep penetration.
Ideally suited for unclean & rusty surfaces. Stable Arc with very low spatter loss.
Compatibility
:CO2 wire can be used for welding mild steel, high strength steel & low alloyed steel, it may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.
Applications:
Suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg,etc
Suitable for low carbon steel and low alloy steel,etc.
CO2 welding wire
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
Suitable for welding in all position like Vertical/Horizontal.
It will produce Low Hydrogen Weld
High Deposition Rate & Deep penetration.
Ideally suited for unclean & rusty surfaces. Stable Arc with very low spatter loss.
Compatibility
:CO2 wire can be used for welding mild steel, high strength steel & low alloyed steel, it may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.
Applications:
Suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.
MIG welding wire ER70S-6
welding wire
used for plain steel in carbon and low metal alloy steel constructions, used for many layers welding ,double the
welding wire
Detailed Product Description
Material:Subermerged Arc Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
used for plain steel in carbon and low metal alloy steel constructions, used for many layers welding ,double the
welding wire
Detailed Product Description
Material:Subermerged Arc Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
MIG welding wire FACTORY AWS ER70S-6 (ISO9001:2000)
welding wire AWS ER70S-6:
Excellent quality,good price with low splashing, high deposition efficiency and good appearance.
welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
Excellent quality,good price with low splashing, high deposition efficiency and good appearance.
welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
MIG welding wire er70s-6
MIG/CO2 gas shield welding wire ER70S-6 has the excellent mechanical performance such as high depositing speed.
This series of MIG welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
This series of MIG welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG welding wire
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
ER70S-3
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
ER70S-3
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG welding wire
CO2 welding wire,AWS ER70S-6
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg,etc
Suitable for low carbon steel and low alloy steel,etc.
CO2 welding wire
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
Suitable for welding in all position like Vertical/Horizontal.
It will produce Low Hydrogen Weld
High Deposition Rate & Deep penetration.
Ideally suited for unclean & rusty surfaces. Stable Arc with very low spatter loss.
Compatibility
:CO2 wire can be used for welding mild steel, high strength steel & low alloyed steel, it may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.
Applications:
Suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.
0.8mm,1.0mm, 1.2mm,1.6mm,5kg,15kg,20kg,etc
Suitable for low carbon steel and low alloy steel,etc.
CO2 welding wire
CO2 welding wire is a double deoxidized copper Coated Solid Steel Wire.
Suitable for welding in all position like Vertical/Horizontal.
It will produce Low Hydrogen Weld
High Deposition Rate & Deep penetration.
Ideally suited for unclean & rusty surfaces. Stable Arc with very low spatter loss.
Compatibility
:CO2 wire can be used for welding mild steel, high strength steel & low alloyed steel, it may be used on steels with moderate presence of rust & mill scale.
High current is also permitted with this wire.
Applications:
Suitable for Welding Structural Steels and General Fabrication, Automobile, Pressure Vessels, LPG Cylinders, Ship, Bridges, Railway Wagon & Coaches, Earth Moving Equipments and many more areas where super & special kind of welding is required.
AWS A5.20 E 70T-1 flux cored wire
Its characteristic is High tenacity low hydrogen..
Flux Cored Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
1.2MM
3) Standards:
a) GB/T10045-2001
b) E500T-1
c) AWS A5.20 E70-1
d) YFW C50DR
e) YC-YJ50MX(Q)
4)Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
5) AWS A5.20E70T-1 is a kind of TI type flux cored wire for CO2 welding ,it has high cladding efficiency,good welding technical performance in all-position welding,apply for low carbon steel and 500MPA grade strength steel welding,such as ships,pressure vessels,mechanical equipments and bridges.
6)Chemical composition of deposited metal(%)
C:0.04,Mn:1.49,Si:0.35,S :0.011,P:0.012
7)Mechanical Properties of Deposited Metal:
Yield Point:480MPA, TensileStrength:560MPA,Elongation:27%
8)Shielding Gas:CO2
Flux Cored Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
1.2MM
3) Standards:
a) GB/T10045-2001
b) E500T-1
c) AWS A5.20 E70-1
d) YFW C50DR
e) YC-YJ50MX(Q)
4)Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
5) AWS A5.20E70T-1 is a kind of TI type flux cored wire for CO2 welding ,it has high cladding efficiency,good welding technical performance in all-position welding,apply for low carbon steel and 500MPA grade strength steel welding,such as ships,pressure vessels,mechanical equipments and bridges.
6)Chemical composition of deposited metal(%)
C:0.04,Mn:1.49,Si:0.35,S :0.011,P:0.012
7)Mechanical Properties of Deposited Metal:
Yield Point:480MPA, TensileStrength:560MPA,Elongation:27%
8)Shielding Gas:CO2
MIG welding wire
MIG/CO2 gas shield welding wire ER70S-6 has the excellent mechanical performance such as high depositing speed.
This series of MIG welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
This series of MIG welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG welding wire
MIG welding wire/CO2 gas shield welding wire ER70S-6 has the excellent mechanical performance such as high depositing speed.
This series of MIG welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
MIG welding wire/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
used to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
This series of MIG welding wire is used for welding low carbon steel and low allow steel structure,such as ships,vehicles,bridges, boilers and building etc
.
MIG welding wire/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
used to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG welding wire
MIG weld wire
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.STANDARD: ER70S-6;ER49-1
3.SURFACE:COPPER COAT
4.SPOOL: WHITE OR BLAC
MIG welding wire
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.SURFACE TREATMENT:COPPER COATED
3.PACKING: AS PER CUSTOMER REQUEST
4.SPOOL: WHITE OR BLACK ETC
5. KIND OF SPOOL: PLASTIC OR METAL WIRE
6. STANDARD: ER70S-6,ER49-1
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.STANDARD: ER70S-6;ER49-1
3.SURFACE:COPPER COAT
4.SPOOL: WHITE OR BLAC
MIG welding wire
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.SURFACE TREATMENT:COPPER COATED
3.PACKING: AS PER CUSTOMER REQUEST
4.SPOOL: WHITE OR BLACK ETC
5. KIND OF SPOOL: PLASTIC OR METAL WIRE
6. STANDARD: ER70S-6,ER49-1
MIG welding wire
MIG welding wire
1.ER307Si
2.quick delivery
3.manufacturer provide directly
4.large month output
MIG welding wire
standards
: ASTM,GB,EN,JIN
mater
ial
: ER308 ER309 ER310 ER316 ER2209 ER347 ER321 ER304 ER301 ER201 ER904 ER308L ER308L ER308L-G ER308L-G ER309MoL ER308Si ER309Si ER430LNB H1Cr13 ER90S-B3 ER90S-B9
diameter:
1.0mm-5.5mm
feature:
1. Perfect welding technology with excellent resistance to intergranular corrosion.
2. Beautiful welding appearance
3. Good resistance to cracking
4. Arc stability, good corrosion resistance, mechanical properties and working ability
uses:
wire-drawing,weaving of wire mesh,soft pipe,beam of cabinet, steel wire rope, fiter material and equipment,spring,aerospace, military production, nuclear power, petrochemical, machinery, automobiles, household appliance, medical equipment, food machinery, construction, decoration, high temperature heating device,etc.
quotation need data:
material+diameter+packing weight
Chemical composition of stainless steel wire:
TIG and MIG stainless steel welding wire composition
YB5092-2005
AWS
chemical composition (%)
C
Si
Mn
P
S
Cr
Ni
Mo
H08Cr20Ni9Mn7Si
ER307Si
0.075
0.78
6.70
0.022
0.010
19.8
8.80
H06Cr21Ni10
ER308
0.045
0.45
1.90
0.020
0.009
20.8
9.80
H06Cr21Ni10Si
ER308Si
0.045
0.85
1.50
0.022
0.010
20.8
9.80
H06Cr24Ni13
ER309
0.06
0.45
1.90
0.019
0.009
24.3
13.20
H06Cr24Ni13Si
ER309Si
0.06
0.79
1.95
0.019
0.009
24.7
13.20
H03Cr24Ni13
ER309L
0.020
0.42
1.80
0.020
0.010
24.8
13.2
H03Cr24Ni13Si
ER309LSi
0.018
0.80
1.70
0.020
0.010
23.5
13.50
H21Cr16Ni35
ER330
0.20
0.38
1.50
0.022
0.010
16.5
34.5
H06Cr19Ni12Mo2
ER316
0.04
0.40
1.90
0.020
0.010
19.5
11.80
2.30
H06Cr19Ni12Mo2Si
ER316Si
0.05
0.70
1.92
0.020
0.010
19.5
11.80
2.30
H03Cr19Ni12Mo2
ER316L
0.019
0.38
1.80
0.018
0.010
19.8
12.20
2.50
H03Cr19Ni12Mo2Si
ER316LSi
0.06
0.85
1.70
0.022
0.010
18.8
12.60
2.40
H03Cr17Ni14Mo3
ER317L
0.02
0.38
1.80
0.020
0.010
18.8
13.80
3.60
H08Cr19Ni12Mo2Nb
ER318
0.06
0.42
1.50
0.022
0.010
18.5
11.80
2.30
H07Cr20Ni34Mo2Cu3Nb
ER320
0.06
0.40
1.00
0.022
0.010
19.8
33.3
2.80
Nb0.7
H02Cr20Ni34Mo2Cu3Nb
ER320L
0.018
0.33
1.50
0.013
0.010
19.8
33.60
2.50
Nb0.35
H08Cr20Ni10Ti
ER321
0.06
0.45
1.50
0.022
0.010
20.8
9.80
Ti9×C-1.0
H08Cr21Ni10Nb
ER347
0.055
0.48
1.80
0.021
0.008
20.8
9.80
Nb1×C-1.0
H12Cr26Ni21
ER310
0.09
0.50
1.66
0.020
0.010
25.5
20.50
H02Cr20Ni25Mo4Cu
ER385
0.020
0.30
1.50
0.018
0.010
20.2
24.80
4.80
Cu 1.80
H03Cr22Ni9Mo3N
ER2209
0.022
0.50
0.90
0.020
0.010
22.5
8.80
3.30
N0.08-0.20
H04Cr25Ni5Mo3Cu2N
ER2553
0.027
0.50
1.00
0.025
0.015
24.8
5.50
3.20
N0.1-0.25
H15Cr29Ni9
ER312
0.09
0.38
1.50
0.022
0.010
29.5
8.50
H03Cr24Ni13MoL
ER309LMo
0.023
0.45
1.50
0.022
0.010
23.8
13.20
2.20
H05Cr17Ni4Cu4Nb
ER630
0.04
0.39
0.50
0.022
0.010
16.5
4.80
Cu;3 Nb;0.28
H08Cr26Ni5Mo2
ER453s
0.06
0.30
0.40
0.022
0.010
25.8
4.80
2.10
H08Cr21Ni10Mn6
0.06
0.35
5.50
0.022
0.010
20.8
9.80
H05Cr22Ni11Mn6Mo3VN
ER209
0.04
0.40
4.50
0.022
0.010
21.5
10.80
2.20
N;0.20 V;0.18
1.ER307Si
2.quick delivery
3.manufacturer provide directly
4.large month output
MIG welding wire
standards
: ASTM,GB,EN,JIN
mater
ial
: ER308 ER309 ER310 ER316 ER2209 ER347 ER321 ER304 ER301 ER201 ER904 ER308L ER308L ER308L-G ER308L-G ER309MoL ER308Si ER309Si ER430LNB H1Cr13 ER90S-B3 ER90S-B9
diameter:
1.0mm-5.5mm
feature:
1. Perfect welding technology with excellent resistance to intergranular corrosion.
2. Beautiful welding appearance
3. Good resistance to cracking
4. Arc stability, good corrosion resistance, mechanical properties and working ability
uses:
wire-drawing,weaving of wire mesh,soft pipe,beam of cabinet, steel wire rope, fiter material and equipment,spring,aerospace, military production, nuclear power, petrochemical, machinery, automobiles, household appliance, medical equipment, food machinery, construction, decoration, high temperature heating device,etc.
quotation need data:
material+diameter+packing weight
Chemical composition of stainless steel wire:
TIG and MIG stainless steel welding wire composition
YB5092-2005
AWS
chemical composition (%)
C
Si
Mn
P
S
Cr
Ni
Mo
H08Cr20Ni9Mn7Si
ER307Si
0.075
0.78
6.70
0.022
0.010
19.8
8.80
H06Cr21Ni10
ER308
0.045
0.45
1.90
0.020
0.009
20.8
9.80
H06Cr21Ni10Si
ER308Si
0.045
0.85
1.50
0.022
0.010
20.8
9.80
H06Cr24Ni13
ER309
0.06
0.45
1.90
0.019
0.009
24.3
13.20
H06Cr24Ni13Si
ER309Si
0.06
0.79
1.95
0.019
0.009
24.7
13.20
H03Cr24Ni13
ER309L
0.020
0.42
1.80
0.020
0.010
24.8
13.2
H03Cr24Ni13Si
ER309LSi
0.018
0.80
1.70
0.020
0.010
23.5
13.50
H21Cr16Ni35
ER330
0.20
0.38
1.50
0.022
0.010
16.5
34.5
H06Cr19Ni12Mo2
ER316
0.04
0.40
1.90
0.020
0.010
19.5
11.80
2.30
H06Cr19Ni12Mo2Si
ER316Si
0.05
0.70
1.92
0.020
0.010
19.5
11.80
2.30
H03Cr19Ni12Mo2
ER316L
0.019
0.38
1.80
0.018
0.010
19.8
12.20
2.50
H03Cr19Ni12Mo2Si
ER316LSi
0.06
0.85
1.70
0.022
0.010
18.8
12.60
2.40
H03Cr17Ni14Mo3
ER317L
0.02
0.38
1.80
0.020
0.010
18.8
13.80
3.60
H08Cr19Ni12Mo2Nb
ER318
0.06
0.42
1.50
0.022
0.010
18.5
11.80
2.30
H07Cr20Ni34Mo2Cu3Nb
ER320
0.06
0.40
1.00
0.022
0.010
19.8
33.3
2.80
Nb0.7
H02Cr20Ni34Mo2Cu3Nb
ER320L
0.018
0.33
1.50
0.013
0.010
19.8
33.60
2.50
Nb0.35
H08Cr20Ni10Ti
ER321
0.06
0.45
1.50
0.022
0.010
20.8
9.80
Ti9×C-1.0
H08Cr21Ni10Nb
ER347
0.055
0.48
1.80
0.021
0.008
20.8
9.80
Nb1×C-1.0
H12Cr26Ni21
ER310
0.09
0.50
1.66
0.020
0.010
25.5
20.50
H02Cr20Ni25Mo4Cu
ER385
0.020
0.30
1.50
0.018
0.010
20.2
24.80
4.80
Cu 1.80
H03Cr22Ni9Mo3N
ER2209
0.022
0.50
0.90
0.020
0.010
22.5
8.80
3.30
N0.08-0.20
H04Cr25Ni5Mo3Cu2N
ER2553
0.027
0.50
1.00
0.025
0.015
24.8
5.50
3.20
N0.1-0.25
H15Cr29Ni9
ER312
0.09
0.38
1.50
0.022
0.010
29.5
8.50
H03Cr24Ni13MoL
ER309LMo
0.023
0.45
1.50
0.022
0.010
23.8
13.20
2.20
H05Cr17Ni4Cu4Nb
ER630
0.04
0.39
0.50
0.022
0.010
16.5
4.80
Cu;3 Nb;0.28
H08Cr26Ni5Mo2
ER453s
0.06
0.30
0.40
0.022
0.010
25.8
4.80
2.10
H08Cr21Ni10Mn6
0.06
0.35
5.50
0.022
0.010
20.8
9.80
H05Cr22Ni11Mn6Mo3VN
ER209
0.04
0.40
4.50
0.022
0.010
21.5
10.80
2.20
N;0.20 V;0.18
Friday, May 27, 2011
MIG welding wires
MIG welding wires
Merit:high stresses, corrosive environment, high temperatures;
Size:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm
MIG welding wires, welding materials
Main Brands for MIG automative welding wires:
ENi-1,Eni-0, ENiCr, ENiCrMo, ENiCrFe, ENiCrFeMo
ENiCr-3, ENiFeCr-1,ErNiCu-7...
Specification:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm...
Other grades we also can customize the special sizes for your request.
Welcome you to contact us for premium quality and best service.
Merit:high stresses, corrosive environment, high temperatures;
Size:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm
MIG welding wires, welding materials
Main Brands for MIG automative welding wires:
ENi-1,Eni-0, ENiCr, ENiCrMo, ENiCrFe, ENiCrFeMo
ENiCr-3, ENiFeCr-1,ErNiCu-7...
Specification:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm...
Other grades we also can customize the special sizes for your request.
Welcome you to contact us for premium quality and best service.
MIG wire - ER70S-6
1.welding wire - ER70S-6
2.stable arc
3.low splashing
4.high deposited effeciency
5.suitable for all position
1,welding wire - ER70S-6 is a mild steel welding wire that contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. The high silicon content increases the fluidity of the weld pool, thus creating a smoother bead appearance and resulting in minimal post-weld grinding. This wire is engineered to provide porosity-free, x-ray quality welds at the highest tensile strength (as welded) of all the plain carbon steel wires. This product requires a shielding gas: CO
2
and/or CO
2
mix.
2,Features:excellent spatter control and bead profile
fluid puddle, good wash-in at weld toes and flat weld beads minimize defects, scrap or re-work
manufactured under a quality system certified to ISO 9001 requirements.
3,Specification:
Conforms to AWS 5.18
4,Application:
industrial, farming, construction and mining equipment
automotive repair
for welding on metals with a medium-to-high presence of dirt, rust or mill scale
single-pass welds on sheet metal applications
multiple pass welds on thick sections
all-position welding
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
5,0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
6,15kg, 20kg iron spool layer wind
7,100kg, 250kg, 350kg drum packing
mig welding gun and mig parts binzel type
8,MB15,MB23,MB24,MB25,MB26,MB36,MB40KD,MB240D,MB401D,MB501D,MB610,MB602,MB61GD
9,TIG gun, consumables and cables, MIG/MAG gun, consumables and cables, long-life spot-welding electrode, and welding accessories (such as pricker, earth clamp, welding clamp, yarn-gripping hose, yarn-wrapping hose, quick coupling, coupling, etc.).
10,Its specifications and varieties exceed 3000.
11,The company supplies unpatented welding tools and their consumables from some major brands in the world, such as Panasonic, OTC, HITACH, BINZLE, BERNARD, HOBART, L-TEC, AIRCO/ESAB, MILLER, TWECO, LINCOLN Plasma, TIG, MIG/MAG Torch, Nozzle, Tip, Electrode, Contact Tip, Gas Diffuser, Insulator, Ceramic Cap, etc
12,is no way affiliated with the above-named manufacturers. In this catalogue, all references to original manufacture's equipment numbers, part numbers, torches, and trade names or trademarks, are for identification and convenience ONLY
2.stable arc
3.low splashing
4.high deposited effeciency
5.suitable for all position
1,welding wire - ER70S-6 is a mild steel welding wire that contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. The high silicon content increases the fluidity of the weld pool, thus creating a smoother bead appearance and resulting in minimal post-weld grinding. This wire is engineered to provide porosity-free, x-ray quality welds at the highest tensile strength (as welded) of all the plain carbon steel wires. This product requires a shielding gas: CO
2
and/or CO
2
mix.
2,Features:excellent spatter control and bead profile
fluid puddle, good wash-in at weld toes and flat weld beads minimize defects, scrap or re-work
manufactured under a quality system certified to ISO 9001 requirements.
3,Specification:
Conforms to AWS 5.18
4,Application:
industrial, farming, construction and mining equipment
automotive repair
for welding on metals with a medium-to-high presence of dirt, rust or mill scale
single-pass welds on sheet metal applications
multiple pass welds on thick sections
all-position welding
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
5,0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
6,15kg, 20kg iron spool layer wind
7,100kg, 250kg, 350kg drum packing
mig welding gun and mig parts binzel type
8,MB15,MB23,MB24,MB25,MB26,MB36,MB40KD,MB240D,MB401D,MB501D,MB610,MB602,MB61GD
9,TIG gun, consumables and cables, MIG/MAG gun, consumables and cables, long-life spot-welding electrode, and welding accessories (such as pricker, earth clamp, welding clamp, yarn-gripping hose, yarn-wrapping hose, quick coupling, coupling, etc.).
10,Its specifications and varieties exceed 3000.
11,The company supplies unpatented welding tools and their consumables from some major brands in the world, such as Panasonic, OTC, HITACH, BINZLE, BERNARD, HOBART, L-TEC, AIRCO/ESAB, MILLER, TWECO, LINCOLN Plasma, TIG, MIG/MAG Torch, Nozzle, Tip, Electrode, Contact Tip, Gas Diffuser, Insulator, Ceramic Cap, etc
12,is no way affiliated with the above-named manufacturers. In this catalogue, all references to original manufacture's equipment numbers, part numbers, torches, and trade names or trademarks, are for identification and convenience ONLY
AWS A5.20 E71T-1 FLUX CORED WIRE
THIS PRODUCTS HAVE BEEN APPROVED BY CCS,ABS,DNV,LR,GL,BV,NK ,KR,RINA FOR 3Y
Flux Cored Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
a) 1.0mm
b) 1.2mm
c) 1.4mm
d) 1.6mm
3) Standards:
a) GB/T10045-2001
b) E501T-1
c) AWS A5.20 E71T-1
d) YFW C50DR
e) YC-YJ502(Q)
Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
Flux Cored Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
a) 1.0mm
b) 1.2mm
c) 1.4mm
d) 1.6mm
3) Standards:
a) GB/T10045-2001
b) E501T-1
c) AWS A5.20 E71T-1
d) YFW C50DR
e) YC-YJ502(Q)
Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
MIG wire - ER70S-6
MIG wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position
1.MIG wire ER70S-6 is a mild steel welding wire that contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. The high silicon content increases the fluidity of the weld pool, thus creating a smoother bead appearance and resulting in minimal post-weld grinding. This wire is engineered to provide porosity-free, x-ray quality welds at the highest tensile strength (as welded) of all the plain carbon steel wires. This product requires a shielding gas: CO
2
and/or CO
2
mix.
2.Features:
excellent spatter control and bead profile
fluid puddle, good wash-in at weld toes and flat weld beads minimize defects, scrap or re-work
manufactured under a quality system certified to ISO 9001 requirements.
3.Specification:
Conforms to AWS 5.18
4.Application:
industrial, farming, construction and mining equipment
automotive repair
for welding on metals with a medium-to-high presence of dirt, rust or mill scale
single-pass welds on sheet metal applications
multiple pass welds on thick sections
all-position welding
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
5.0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
6.15kg, 20kg iron spool layer wind
7.100kg, 250kg, 350kg drum packing
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position
1.MIG wire ER70S-6 is a mild steel welding wire that contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. The high silicon content increases the fluidity of the weld pool, thus creating a smoother bead appearance and resulting in minimal post-weld grinding. This wire is engineered to provide porosity-free, x-ray quality welds at the highest tensile strength (as welded) of all the plain carbon steel wires. This product requires a shielding gas: CO
2
and/or CO
2
mix.
2.Features:
excellent spatter control and bead profile
fluid puddle, good wash-in at weld toes and flat weld beads minimize defects, scrap or re-work
manufactured under a quality system certified to ISO 9001 requirements.
3.Specification:
Conforms to AWS 5.18
4.Application:
industrial, farming, construction and mining equipment
automotive repair
for welding on metals with a medium-to-high presence of dirt, rust or mill scale
single-pass welds on sheet metal applications
multiple pass welds on thick sections
all-position welding
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
5.0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
6.15kg, 20kg iron spool layer wind
7.100kg, 250kg, 350kg drum packing
MIG wire ER70S-6 (0.8-1.6mm)
MIG ER70S-6
Dia:0.8-1.6mm
Packing: 5kg.12.5kg.15kg 20kg
Free Samples
ISO Certified..
CO2 WELDING WIRE/MIG WIRE ER70S-6
Copper coated welding wire ER70S-6
ER70S-6 WELDING WIRE
Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300
Dia:0.8-1.6mm
Packing: 5kg.12.5kg.15kg 20kg
Free Samples
ISO Certified..
CO2 WELDING WIRE/MIG WIRE ER70S-6
Copper coated welding wire ER70S-6
ER70S-6 WELDING WIRE
Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300
MIG wire ER70S-6
Mig wire
ISO9001,TUV,DB,CE
0.8,0.9,1.0,1.2mm
AWS ER70S-6
for vehicles, bridges, construction,machinery etc
MIG welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2
ISO9001,TUV,DB,CE
0.8,0.9,1.0,1.2mm
AWS ER70S-6
for vehicles, bridges, construction,machinery etc
MIG welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2
MIG wire ER70S-6
Mig welding wire
ISO9001,TUV,DB,CE
0.8,0.9,1.0,1.2mm
AWS ER70S-6
for vehicles, bridges, construction,machinery etc
MIG welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2
ISO9001,TUV,DB,CE
0.8,0.9,1.0,1.2mm
AWS ER70S-6
for vehicles, bridges, construction,machinery etc
MIG welding wire
Model:
AWS A5.18 ER70S-6
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-allow steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
28
85
CO2
MIG wire ER70S-6
CO2 wire ER70S-6
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
MIG wire SG2 (0.6-2.0MM)
Welding Wires AWS 5.18 ER70S-6
WELDING WIRE Size: 0.8mm/1.0mm/1.2mm/1.6mm..
Certificate:ABS,SGS,EWC,AOV,LR,TUV,DB,GL
WELDING WIRE AWS 5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4. 0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5. 15kg, 20kg iron spool layer wind
6. 100kg, 250kg, 350kg drum packing
WELDING WIRE Size: 0.8mm/1.0mm/1.2mm/1.6mm..
Certificate:ABS,SGS,EWC,AOV,LR,TUV,DB,GL
WELDING WIRE AWS 5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4. 0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5. 15kg, 20kg iron spool layer wind
6. 100kg, 250kg, 350kg drum packing
MIG wire and welding electrodes
MIG Welding Wire Manufacture
1. Diameter : 0.8mm,0.9mm, 1.0mm, 1.2mm,1.6mm
2. Weight of spool : 5kg,15kg,20kg
Gas Shielded welding wire AWS ER70s-6
welding wire has excellent mechanical performance such as depositing speed and high efficiency, stable arc, little splash , good welding seam. This series of welding wires are suitable for the low carbon steel and low alloy structure, vehicle ,bridge ,container ,construction machinery ,boilers and construction etc.
- AWS : ER70S-6
- Diameter : 0.8mm,0.9mm, 1.0mm, 1.2mm,1.6mm
Weight of spool : 5kg,15kg and 20kg.
- Packing of welding wire:
Black plastic spool+welding wire+ rust-proof paper+plastic packing+carton+pattle
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
1. Diameter : 0.8mm,0.9mm, 1.0mm, 1.2mm,1.6mm
2. Weight of spool : 5kg,15kg,20kg
Gas Shielded welding wire AWS ER70s-6
welding wire has excellent mechanical performance such as depositing speed and high efficiency, stable arc, little splash , good welding seam. This series of welding wires are suitable for the low carbon steel and low alloy structure, vehicle ,bridge ,container ,construction machinery ,boilers and construction etc.
- AWS : ER70S-6
- Diameter : 0.8mm,0.9mm, 1.0mm, 1.2mm,1.6mm
Weight of spool : 5kg,15kg and 20kg.
- Packing of welding wire:
Black plastic spool+welding wire+ rust-proof paper+plastic packing+carton+pattle
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
MIG wire/welding wire AWS A5.18(ER70S-6)
CO2 welding wire AWS A5.18(ER70S-6)
Manufacture and export high quality welding wire
CO2 gas-shieled welding wire 0.8-1.6mm
Co2 welding wire/MIG welding wire (AWS A5.18 ER70S-6)
Diameter:0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
T
ensile Strength (MPa):500-525
Elongation3:0%
Feature:
1) stable arc
2) low splashing
3) high deposited efficiency
4) Suitable for all position
Application: CO2 welding wire is suitable for co2 shielded welding of low carbon steel and low alloy steel, particularly it is suitable for welding rolling stock,container, engineering machinery, and pressure container, etc.
Manufacture and export high quality welding wire
CO2 gas-shieled welding wire 0.8-1.6mm
Co2 welding wire/MIG welding wire (AWS A5.18 ER70S-6)
Diameter:0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
T
ensile Strength (MPa):500-525
Elongation3:0%
Feature:
1) stable arc
2) low splashing
3) high deposited efficiency
4) Suitable for all position
Application: CO2 welding wire is suitable for co2 shielded welding of low carbon steel and low alloy steel, particularly it is suitable for welding rolling stock,container, engineering machinery, and pressure container, etc.
MIG wire
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG wire
AWS ER70S-6 welding wire Useing the advanced Electroplating copper coated technology
Electroplating copper coated technology for the welding wires.
1) ER70S-6 solid wire is suitable for CO2 shielded welding of low carbon steel and low alloy steel, particularly suitable for welding rolling stock, container, engineering
2) Stable electric arc, low splashing, high deposition efficiency and good anti pore property. It can carry out welding at all positions
3) Specifications: 0.6mm, 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm, 2.0mm
Packing: 1kg/5kg/12.5kg/13.5kg/15kg/20kg per plastic spool
Electroplating copper coated technology for the welding wires.
1) ER70S-6 solid wire is suitable for CO2 shielded welding of low carbon steel and low alloy steel, particularly suitable for welding rolling stock, container, engineering
2) Stable electric arc, low splashing, high deposition efficiency and good anti pore property. It can carry out welding at all positions
3) Specifications: 0.6mm, 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.4mm, 1.6mm, 2.0mm
Packing: 1kg/5kg/12.5kg/13.5kg/15kg/20kg per plastic spool
AWS A5.20 E71T-1 welding wire
Products specification:
Aws A5.20 E71T-1 of flux cored wires.
Aws A5.20 E71T-1 of flux cored welding wires.
Products specification:
Aws A5.20 E71T-1 of flux cored wires.
E71T-1 is a kind of Ti type flux-cored wire by CO2. It is applied for all-position welding which includes vertical down welding. When the welding is taken, there small splashes, and the electric arc is stable and gentle. Furthermore, it has high slag detach ability and beautiful shaped welding seam. It is superior to solid welding wires in cladding, welding technical performance and mechanical properties of deposited metal. It is used for the welding of low carbon steel and 490 grade strength steel of moderate thickness plates welding.
Products Application:
It is applicable for the welding of carbon steel and low-alloy steel structure used for ship, bridge, architecture, vehicle and machine building.
Chemical Components: ( %)
C
Mn
Si
S
P
Standard value
≤0.10
0.5~1.75
≤0.75
≤0.03
≤0.03
Representative value
0.05
1.30
0.40
0.009
0.010
Mechanical properties of deposition metal:
Tensile strengthΣb(MPa)
Yield StrengthΣ0.2(MP)
ElongationΔ5 (%)
Impact value (Akv -20°C)J
Protective Gas
Standard value
≥480
400
≥22
≥27
CO2
Representative value
545
450
29
110
20L/min
Reference current: (DC+)
Welding Diameter (mm)
1.2
1.4
1.6
Welding Current(A)
150-350
170-400
200-400
Welding Voltage(V)
20-36
20-36
20-38
Aws A5.20 E71T-1 of flux cored wires.
Aws A5.20 E71T-1 of flux cored welding wires.
Products specification:
Aws A5.20 E71T-1 of flux cored wires.
E71T-1 is a kind of Ti type flux-cored wire by CO2. It is applied for all-position welding which includes vertical down welding. When the welding is taken, there small splashes, and the electric arc is stable and gentle. Furthermore, it has high slag detach ability and beautiful shaped welding seam. It is superior to solid welding wires in cladding, welding technical performance and mechanical properties of deposited metal. It is used for the welding of low carbon steel and 490 grade strength steel of moderate thickness plates welding.
Products Application:
It is applicable for the welding of carbon steel and low-alloy steel structure used for ship, bridge, architecture, vehicle and machine building.
Chemical Components: ( %)
C
Mn
Si
S
P
Standard value
≤0.10
0.5~1.75
≤0.75
≤0.03
≤0.03
Representative value
0.05
1.30
0.40
0.009
0.010
Mechanical properties of deposition metal:
Tensile strengthΣb(MPa)
Yield StrengthΣ0.2(MP)
ElongationΔ5 (%)
Impact value (Akv -20°C)J
Protective Gas
Standard value
≥480
400
≥22
≥27
CO2
Representative value
545
450
29
110
20L/min
Reference current: (DC+)
Welding Diameter (mm)
1.2
1.4
1.6
Welding Current(A)
150-350
170-400
200-400
Welding Voltage(V)
20-36
20-36
20-38
MIG wire
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
ER70S-3
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
ER70S-3
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG/CO2 gas shielded WELDING WIRE AWS ER70S-6 DIN SG2
MIG/CO2 welding wire AWS ER70S-6,DIN SG2
1.copper coated welding wire
2.Size:0.8~2.0mm
3.Certificate by ISO 9001:2000
Stone Bridge Brand MIG/CO2 gas shielded welding wire AWS ER70S-6 DIN SG2
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
1.copper coated welding wire
2.Size:0.8~2.0mm
3.Certificate by ISO 9001:2000
Stone Bridge Brand MIG/CO2 gas shielded welding wire AWS ER70S-6 DIN SG2
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG/CO2 GAS SHIELDED WELDING WIRE AWS ER70S-6
MIG/CO2 gas-shield welding wire:AWS ER70S-6,DIN SG2:0.8~2.0mm
Submerged Arc Welding Wire
Flux-cored welding wire
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Submerged Arc Welding Wire
Flux-cored welding wire
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG/CO2 GAS welding wire factory AWS ER70S-6
welding wire AWS ER70S-6:
Excellent quality,good price with low splashing, high deposition efficiency and good appearance.
welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
Excellent quality,good price with low splashing, high deposition efficiency and good appearance.
welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
MIG/CO2 WELDING WIRE ER70S-6 DIN SG2
MIG/CO2 welding wire AWS ER70S-6,DIN SG2
1.copper coated welding wire
2.stable arc,little splash
3.ISO 9001:2000
Stone Bridge Brand
MIG/CO2 gas shielded welding wire
MODEL:AWS ER70S-6 DIN SG2
Features Specifications:
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
1.copper coated welding wire
2.stable arc,little splash
3.ISO 9001:2000
Stone Bridge Brand
MIG/CO2 gas shielded welding wire
MODEL:AWS ER70S-6 DIN SG2
Features Specifications:
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG/CO2 WELDING WIRE ER70S-6
MIG/CO2 welding wire:AWS ER70S-6,DIN SG2
Size:0.8~2.0mm
Submerged Arc Welding Wire
Flux-cored welding wire
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
mig
welding wires has the characteristics of excellent
technical performance,fast melting speed, high efficient fusion, stable electric
arc, less welding splash,favorable wetness performance,average & beautiful
welding seam,good anti-oxygenic & anti-corrasive property, less sensitive to the
atmosphere holes.
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Size:0.8~2.0mm
Submerged Arc Welding Wire
Flux-cored welding wire
MIG/CO2 gas shield welding wire AWS ER70s-6
Features Specifications:
mig
welding wires has the characteristics of excellent
technical performance,fast melting speed, high efficient fusion, stable electric
arc, less welding splash,favorable wetness performance,average & beautiful
welding seam,good anti-oxygenic & anti-corrasive property, less sensitive to the
atmosphere holes.
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:
low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
MIG/CO2 welding wire 0.8mm
CO2 wire ER70S-6
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
0.8 0.9-1.6 2.0mmGas shield arc Welding wire
0.8 0.9-1.6 2.0mmGas shield arc Welding wire
1.Welding Wire Gas-shielded Solid Welding Wire
2.Submerged-arc Welding Wire
0.8 0.9-1.6 2.0mmGas shield arc Welding wire
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000
CONTACT WITH Ms Alice
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
1.Welding Wire Gas-shielded Solid Welding Wire
2.Submerged-arc Welding Wire
0.8 0.9-1.6 2.0mmGas shield arc Welding wire
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000
CONTACT WITH Ms Alice
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
AWS A5.20E 70T-1 flux cored wire
Its characteristic is High tenacity low hydrogen...
Flux Cored Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
1.4MM
3) Standards:
a) GB/T10045-2001
b) E500T-1
c) AWS A5.20 E70-1
d) YFW C50DR
e) YC-YJ50MX(Q)
4)Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
5) AWS A5.20E70T-1 is a kind of TI type flux cored wire for CO2 welding ,it has high cladding efficiency,good welding technical performance in all-position welding,apply for low carbon steel and 500MPA grade strength steel welding,such as ships,pressure vessels,mechanical equipments and bridges.
6)Chemical composition of deposited metal(%)
C:0.04,Mn:1.49,Si:0.35,S :0.011,P:0.012
7)Mechanical Properties of Deposited Metal:
Yield Point:480MPA, TensileStrength:560MPA,Elongation:27%
8)Shielding Gas:CO2
Flux Cored Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
1.4MM
3) Standards:
a) GB/T10045-2001
b) E500T-1
c) AWS A5.20 E70-1
d) YFW C50DR
e) YC-YJ50MX(Q)
4)Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
5) AWS A5.20E70T-1 is a kind of TI type flux cored wire for CO2 welding ,it has high cladding efficiency,good welding technical performance in all-position welding,apply for low carbon steel and 500MPA grade strength steel welding,such as ships,pressure vessels,mechanical equipments and bridges.
6)Chemical composition of deposited metal(%)
C:0.04,Mn:1.49,Si:0.35,S :0.011,P:0.012
7)Mechanical Properties of Deposited Metal:
Yield Point:480MPA, TensileStrength:560MPA,Elongation:27%
8)Shielding Gas:CO2
MIG/CO2 welding wire E70T-1
WELDING WIRE E70T-1
Its characteristic is High tenacity low hydrogen
MIG/CO2 WELDING WIRE E70T-1
Flux Cored welding Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
2.0mm
3) Standards:
a) GB/T10045-2001
b) E500T-1
c) AWS A5.20 E710-1
d) YC-YJ70-1(Q)
4)Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
5) AWS A5.20 E70-1 is a kind of TI type flux cored wire for CO2 welding ,it has high cladding efficiency,good welding technical performance in flat position welding and horizontal position welding,apply for low carbon steel and 500MPA grade strength steel welding,such as ships,pressure vessels,mechanical equipments and bridges.
6)Chemical composition of deposited metal(%)
C:0.07,Mn:1.46,Si:0.39,S :0.012,P:0.014,Ni:0.86,Mo:0.16
7)Mechanical Properties of Deposited Metal:
Yield Point:540MPA, TensileStrength:620MPA,Elongation:26%
8)Shielding Gas:CO2
Its characteristic is High tenacity low hydrogen
MIG/CO2 WELDING WIRE E70T-1
Flux Cored welding Wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
2.0mm
3) Standards:
a) GB/T10045-2001
b) E500T-1
c) AWS A5.20 E710-1
d) YC-YJ70-1(Q)
4)Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
5) AWS A5.20 E70-1 is a kind of TI type flux cored wire for CO2 welding ,it has high cladding efficiency,good welding technical performance in flat position welding and horizontal position welding,apply for low carbon steel and 500MPA grade strength steel welding,such as ships,pressure vessels,mechanical equipments and bridges.
6)Chemical composition of deposited metal(%)
C:0.07,Mn:1.46,Si:0.39,S :0.012,P:0.014,Ni:0.86,Mo:0.16
7)Mechanical Properties of Deposited Metal:
Yield Point:540MPA, TensileStrength:620MPA,Elongation:26%
8)Shielding Gas:CO2
MIG/CO2 welding wire ER70S-6 /SG2 welding wire (SAW)
Co2 welding wire /SG2 welding wire SAW wire
1.AWS ER70S-6
2.size 0.6/2.0mm
3 BV COC SANCOP ISO CE certificate
CO2 WELDING WIRE /SG2 welding wire net weight SAW WELD
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate
Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand and Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai
CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-alloy steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
5. suitable for all position
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
30
85
CO2
1.AWS ER70S-6
2.size 0.6/2.0mm
3 BV COC SANCOP ISO CE certificate
CO2 WELDING WIRE /SG2 welding wire net weight SAW WELD
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate
Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand and Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai
CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Specification:
1)Size: 0.8mm-1.6mm
2)Application: for welding of carbon steel and 500Mpa grade low-alloy steel, such as vehicles, bridges, construction and machinery structure etc.
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallet.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. beautiful seam
5. suitable for all position
Chemical composition (%):
C
Mn
Si
S
P
Cu
Cr
Ni
Mo
V
0.07-0.15
1.40-1.85
0.8-1.15
≤0.035
≤0.025
≤0.50
≤0.15
≤0.15
≤0.15
≤0.03
Typical mechanical properties of deposited metal:
T/S(MPa)
Y/S(MPa)
A(%)
kv(J)
shielded gas
550
430
30
85
CO2
MIG/CO2 welding wire ER70S-6(BV Certified)
CO2/MIG welding wire ER70S-6
D:0.8-2.0mm
P:5. 15.18.20kg/Spool (D200 270 300 K300)
ISO.BV.SGS.COC.IEI Certified
Free Sample
SG2/SAW/CO2/MIG welding wire ER70S-6-copper coated
Brand name :stone bridge /Hero brand
CO2/MIG WELDING WIRE
ER70S-6
Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable
D:0.8-2.0mm
P:5. 15.18.20kg/Spool (D200 270 300 K300)
ISO.BV.SGS.COC.IEI Certified
Free Sample
SG2/SAW/CO2/MIG welding wire ER70S-6-copper coated
Brand name :stone bridge /Hero brand
CO2/MIG WELDING WIRE
ER70S-6
Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable
MIG/CO2 wire
welding wire ER70S-6
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
MIG/MAG welding wire(ER70S-6)
MIG/MAG Welding Wire (AWS ER70S-6)
copper coated welding wire
mild steel welding wire
size 0.8 1.0 1.2 1.6 2.0mm
Features Specifications: MIG/MAG WELDING WIRE,mig welding wire,co2 welding wire
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
MAG/MIG WELDING WIRE
STANDARD:GB,AWS JIS
Chemical Composition of Welding Wire(%)
Type:ER50-6
C: <0.093
Mn: <1.13
Si: <0.83
S: <0.012
P:< 0.010
Cu:<0.063
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength Mpa
Elogation(%)
Temperature
Tensile Num Kav
550
450
30
66(-29)
27
Specifications/Reference Electric Current/ Voltage/ Packing/ Weight
Diameter
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
40-140A
50-200A
70-260A
80-350A
170-550A
Voltage
16-24
16-27
16-27
17.5-30
18-35
Packaging
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
copper coated welding wire
mild steel welding wire
size 0.8 1.0 1.2 1.6 2.0mm
Features Specifications: MIG/MAG WELDING WIRE,mig welding wire,co2 welding wire
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
MAG/MIG WELDING WIRE
STANDARD:GB,AWS JIS
Chemical Composition of Welding Wire(%)
Type:ER50-6
C: <0.093
Mn: <1.13
Si: <0.83
S: <0.012
P:< 0.010
Cu:<0.063
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength Mpa
Elogation(%)
Temperature
Tensile Num Kav
550
450
30
66(-29)
27
Specifications/Reference Electric Current/ Voltage/ Packing/ Weight
Diameter
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
40-140A
50-200A
70-260A
80-350A
170-550A
Voltage
16-24
16-27
16-27
17.5-30
18-35
Packaging
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
Thursday, May 26, 2011
MIG/MAG welding wire
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating
Features Specifications: WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
STANDARD:GB,AWS JIS
Chemical Composition of Welding Wire(%)
Type:ER50-6
C: <0.093
Mn: <1.13
Si: <0.83
S: <0.012
P:< 0.010
Cu:<0.063
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength Mpa
Elogation(%)
Temperature
Tensile Num Kav
550
450
30
66(-29)
27
Specifications/Reference Electric Current/ Voltage/ Packing/ Weight
Diameter
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
40-140A
50-200A
70-260A
80-350A
170-550A
Voltage
16-24
16-27
16-27
17.5-30
18-35
Packaging
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
Features Specifications: WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing f: 10kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000
CO2 GAS SHIELDED WELDING WIRE
STANDARD:GB,AWS JIS
Chemical Composition of Welding Wire(%)
Type:ER50-6
C: <0.093
Mn: <1.13
Si: <0.83
S: <0.012
P:< 0.010
Cu:<0.063
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength Mpa
Elogation(%)
Temperature
Tensile Num Kav
550
450
30
66(-29)
27
Specifications/Reference Electric Current/ Voltage/ Packing/ Weight
Diameter
0.8mm
0.9mm
1.0mm
1.2mm
1.6mm
Current
40-140A
50-200A
70-260A
80-350A
170-550A
Voltage
16-24
16-27
16-27
17.5-30
18-35
Packaging
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
1Roll/Carton
Size:27.5X10.5X27.5CM
72Roll/Pallet
Size:114X84X82CM
MIG/MAG wire
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
ER70S-3
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO2
ER70S-3
WELDING WIRE
MIG/MAG WIRE ER70S-6
For welding low carbon and high strength steel structures of 500Mpa.80%Ar+20%CO
2
CO2 gas-shielded welding wires are primarily used for all position welding of steel structures, pressure vessels,
containers, construction machinery, ships, railways, automobiles, motorcycles and 300MW thermoelectric generators and are characterized by excellent welding performance and mechanical performance, stable electric arc, few splattering, good welding seam forming and high deposition efficiency.
Packing
gauges
0.8mm-1.6mm
spool
100mm
200mm
270mm
300mm
Net weight
1kg, 5kg, 15kg, 20kg
Typical Chemical Analysis
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical properties of deposited metal
Yield Strength
Tensile Strength
Elongation
Charpy-V Akv
≥420
≥500
≥22
≥27(-29)
MIG/MAG Wire ER70S-3
For welding carbon steel and low-alloy steel structures.
Shield gas:80%Ar+20%CO
2
MIG/MAG zavarivanje ER70S-6
1,welding wire Application building,ships,briges,ect
2,good weldability
3,low residue
4,low splash
5,high reliability
1,
welding wire AWS A5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4,0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5,15kg, 20kg iron spool layer wind
6,100kg, 250kg, 350kg drum packing
2,good weldability
3,low residue
4,low splash
5,high reliability
1,
welding wire AWS A5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4,0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5,15kg, 20kg iron spool layer wind
6,100kg, 250kg, 350kg drum packing
MIG/TIG Welding Wires, Nickel Base Welding Wires
MIG/TIG Welding Wires
High-quality raw material, advanced technology and equipment;
Dia.0.05mm-10mm
ISO,BV
MIT/TIG Welding Wires
, Nickel Base Welding Wires
Shanghai Phoenix Alloy Co
., is a professional manufacturer of nickel base alloys as well as the welding maerials. The main products for the weilding wire we trade as below:
Nickel and Nickel base alloy
:
ENi-1, ENi-0,ErNiCr, ERNiCrMo, ErNiCrFe, ErNiCrFeMo;
Stainless Steel Welding Wires
:
ER308/308L,Er309/309L, ER316/316L,ER347,ER321,ER310, etc.
High-temperature alloy welding wire
:
Inconel alloy 625, Inconel alloy 718, Incoloy alloy 800/800H/800HT
Corrosion resistant alloy welding wire
:
Inconel 600/601, Inconel alloy 825, Monel alloy 400, Inconel alloy 690, Inconel alloy X750, etc.
Packing:
10KG, 15KG, or 20KG packed in plastic spool
Besides, we also can customize the products to the customers' requirement.
Welcome to contact us for the premium quality and best service.
High-quality raw material, advanced technology and equipment;
Dia.0.05mm-10mm
ISO,BV
MIT/TIG Welding Wires
, Nickel Base Welding Wires
Shanghai Phoenix Alloy Co
., is a professional manufacturer of nickel base alloys as well as the welding maerials. The main products for the weilding wire we trade as below:
Nickel and Nickel base alloy
:
ENi-1, ENi-0,ErNiCr, ERNiCrMo, ErNiCrFe, ErNiCrFeMo;
Stainless Steel Welding Wires
:
ER308/308L,Er309/309L, ER316/316L,ER347,ER321,ER310, etc.
High-temperature alloy welding wire
:
Inconel alloy 625, Inconel alloy 718, Incoloy alloy 800/800H/800HT
Corrosion resistant alloy welding wire
:
Inconel 600/601, Inconel alloy 825, Monel alloy 400, Inconel alloy 690, Inconel alloy X750, etc.
Packing:
10KG, 15KG, or 20KG packed in plastic spool
Besides, we also can customize the products to the customers' requirement.
Welcome to contact us for the premium quality and best service.
MIG/TIG welding wires
MIG/TIG welding wires
Merit:high stresses, corrosive environment, high temperatures;
Size:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm
MIG/TIG welding wires, welding materials
We offer a wide range of MIG & TIIG, Welding Wires in Various grades of Stainless Steel, Alloy Steel, Aluminium, Copper and Nickle & alloys. MIG WIRES are available both solid & Flux Cored.
Specification:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm...
Other grades we also can customize the special sizes for your request.
Welcome you to contact us for premium quality and best service.
Merit:high stresses, corrosive environment, high temperatures;
Size:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm
MIG/TIG welding wires, welding materials
We offer a wide range of MIG & TIIG, Welding Wires in Various grades of Stainless Steel, Alloy Steel, Aluminium, Copper and Nickle & alloys. MIG WIRES are available both solid & Flux Cored.
Specification:0.8mm,1.0mm,1.2mm,1.6mm,2.0mm...
Other grades we also can customize the special sizes for your request.
Welcome you to contact us for premium quality and best service.
AWS A5.7 C65600 brazing wire ErCuSi-A
Best for the jointing and overlay welding of Cu-Zn alloy,
especially for th MIG welding of zinc coated steel sheet
Commodity: Brazing wire
1. Standard: AWS A5.7 ERCuSi-A, DIN 1733:SG-CuSi3 , BS EN14640 CuSi3Mn1
2. Applications : Joining and overlay welding of copper zinc alloys ,low copper materials,also for an excellent wear resisting overlay welding on low and unalloyed steel as well as cast iron For MIG overlay welding of large work pieces preheating is recommended For multilayer welding on steels,pulsed arc welding is recommended .Appropriate for MIG brazing of zinc coated sheets.
3. Composition(standard value)%
Cu
Al
Si
Sn
Mn
Pb
Zn
P
Fe
Other
Balance
0.01
2.8-4.0
1.0
0.50-1.5
0.02
1.0
0.02
0.50
0.50
4. Physical properties
Electrical conductivity 3.5-4.0 S·m/mm
2
(Approx.values) Density 8.5/dm
3
Solids-Temperature 910 deg
Liquids-Temperature 1025 deg
Tensile strength 330-370N/mm
2
Elongation(Lo=5do) 40%
Hardness Brinell 80-90 HB
Welding position : PA,PB,PC,PE,PF
Shielding gas : I1,I2,I3 (Argon,Helium or Argon/Helium mixtures)
Polarity : MIG = +,WIG ~
5. Available size: 0.8mm /0.9mm/1.0mm/1.2mm/1.6mm
6. packing: 5kg/15kg spool in box
especially for th MIG welding of zinc coated steel sheet
Commodity: Brazing wire
1. Standard: AWS A5.7 ERCuSi-A, DIN 1733:SG-CuSi3 , BS EN14640 CuSi3Mn1
2. Applications : Joining and overlay welding of copper zinc alloys ,low copper materials,also for an excellent wear resisting overlay welding on low and unalloyed steel as well as cast iron For MIG overlay welding of large work pieces preheating is recommended For multilayer welding on steels,pulsed arc welding is recommended .Appropriate for MIG brazing of zinc coated sheets.
3. Composition(standard value)%
Cu
Al
Si
Sn
Mn
Pb
Zn
P
Fe
Other
Balance
0.01
2.8-4.0
1.0
0.50-1.5
0.02
1.0
0.02
0.50
0.50
4. Physical properties
Electrical conductivity 3.5-4.0 S·m/mm
2
(Approx.values) Density 8.5/dm
3
Solids-Temperature 910 deg
Liquids-Temperature 1025 deg
Tensile strength 330-370N/mm
2
Elongation(Lo=5do) 40%
Hardness Brinell 80-90 HB
Welding position : PA,PB,PC,PE,PF
Shielding gas : I1,I2,I3 (Argon,Helium or Argon/Helium mixtures)
Polarity : MIG = +,WIG ~
5. Available size: 0.8mm /0.9mm/1.0mm/1.2mm/1.6mm
6. packing: 5kg/15kg spool in box