Carbon Dioxide Welding Wire
1. Size: 0.8MM, 1.0MM, 1.2MM, 1.6MM
2. High efficiency, little splash and smog.
3. AWS ER 70s-6
Carbon Dioxide Welding Wire
1.
Size: 0.8MM, 1.0MM, 1.2MM, 1.6MM
2.
High efficiency, little splash and smog.
3.
AWS ER 70s-6
4. The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
5. Mechnical Properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
6. Welding Current:
Wire Size (mm)
0.8
1.0
1.2
1.6
Welding position
Welding Current (A)
40~140
50~220
80~350
120~550
Note
Wire shall be stocked in dry.Open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts.
7. Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
Welcome to your inquiry!
Xuteli Welding Material Sales Co.,ltd
Tel: 86-312-5922853
Saturday, August 20, 2011
Carbon Dioxide Welding Wire
Carbon Dioxide Welding Wire
1. Size: 0.8MM, 1.0MM, 1.2MM, 1.6MM
2. High efficiency, little splash and smog.
3. AWS ER 70s-6
Carbon Dioxide Welding Wire
1.
Size: 0.8MM, 1.0MM, 1.2MM, 1.6MM
2.
High efficiency, little splash and smog.
3.
AWS ER 70s-6
4. The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
5. Mechnical Properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
6. Welding Current:
Wire Size (mm)
0.8
1.0
1.2
1.6
Welding position
Welding Current (A)
40~140
50~220
80~350
120~550
Note
Wire shall be stocked in dry.Open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts.
7. Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
Welcome to your inquiry!
Xuteli Welding Material Sales Co.,ltd
Tel: 86-312-5922853
1. Size: 0.8MM, 1.0MM, 1.2MM, 1.6MM
2. High efficiency, little splash and smog.
3. AWS ER 70s-6
Carbon Dioxide Welding Wire
1.
Size: 0.8MM, 1.0MM, 1.2MM, 1.6MM
2.
High efficiency, little splash and smog.
3.
AWS ER 70s-6
4. The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
5. Mechnical Properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
6. Welding Current:
Wire Size (mm)
0.8
1.0
1.2
1.6
Welding position
Welding Current (A)
40~140
50~220
80~350
120~550
Note
Wire shall be stocked in dry.Open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil, rust, water etc from the work parts.
7. Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
Welcome to your inquiry!
Xuteli Welding Material Sales Co.,ltd
Tel: 86-312-5922853
Carbon Low Alloy Steel Welding Wire
carbon-steel welding wire:
1.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
2.Manufacturer.
3.Top quality,best price.
4.Good weldability.
Carbon steel welding wire Specification:
Typical Chemical Composition of Deposition Metal (%)
C
Mn
Si
S
P
≤0.18
≤1.75
≤0.90
≤0.03
≤0.03
0.05
1.35
0.45
0.012
0.008
Typical Mechanical Properties of Deposited Metal
Yield Strength
(Mpa)
Tensile
(Mpa)
Elongation
(%)
Charpy V-notch Impact energy
-20degree centigrade(J)
≥400
≥490
≥22
≥27
475
550
30
106
Size and Recommended Current Range (DC:Wire(+))
Wire Dia(mm)
1.2
1.4
1.6
Current Range(Amp)
Flat
120-300
150-400
180-450
Horizontal
120-300
150-350
180-400
Vertical-up/Overhead
120-260
150-270
180-280
Vertical -down
200-300
200-300
180-350
Shielding Gas: CO2
1.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
2.Manufacturer.
3.Top quality,best price.
4.Good weldability.
Carbon steel welding wire Specification:
Typical Chemical Composition of Deposition Metal (%)
C
Mn
Si
S
P
≤0.18
≤1.75
≤0.90
≤0.03
≤0.03
0.05
1.35
0.45
0.012
0.008
Typical Mechanical Properties of Deposited Metal
Yield Strength
(Mpa)
Tensile
(Mpa)
Elongation
(%)
Charpy V-notch Impact energy
-20degree centigrade(J)
≥400
≥490
≥22
≥27
475
550
30
106
Size and Recommended Current Range (DC:Wire(+))
Wire Dia(mm)
1.2
1.4
1.6
Current Range(Amp)
Flat
120-300
150-400
180-450
Horizontal
120-300
150-350
180-400
Vertical-up/Overhead
120-260
150-270
180-280
Vertical -down
200-300
200-300
180-350
Shielding Gas: CO2
Carbon Steel CO2 Welding Wire
Carbon Steel CO2 Welding Wire
AWS Specification: AWS A5.18
AWS Classification: ER70S-6
wire dia:0.6mm-1.6mm
Carbon Steel CO2 Welding Wire
AWS Specification:
AWS A5.18
AWS Classification:
ER70S-6
Diameter:
023’’ (0.6mm), 030’’ (0.8mm), 035’’ (0.9mm), 038’’(1.0mm), 045’’ (1.2mm), 1/16’’(1.6mm)
welding wire of good soldering workmanship, stable arc, little spatter, quick wire melting, strong anti-rust, suitable for all position weld. Contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. This product requires a shielding gas: CO2 and/or CO2 mix.
Typical Applications:
General shop applications with poor fit-up or rusty, oily plates
Steel castings or forging salvage
Home projects
Tanks, containers, pipes, ships, engineering machinery, steel structure and pressure vessiles.
Construction work
Welding Current for MIG process:
DCEP
Typical Wire Chemistry
C 0.07
Mn 1.58
Si 0.86
P 0.016
S 0.011
Cu 0.24
Typical Mechanical Properties
Rm(Mpa) 530
ReL(MPa) 430
A(%) 29
Akv(J)-29°C 90
AWS Specification: AWS A5.18
AWS Classification: ER70S-6
wire dia:0.6mm-1.6mm
Carbon Steel CO2 Welding Wire
AWS Specification:
AWS A5.18
AWS Classification:
ER70S-6
Diameter:
023’’ (0.6mm), 030’’ (0.8mm), 035’’ (0.9mm), 038’’(1.0mm), 045’’ (1.2mm), 1/16’’(1.6mm)
welding wire of good soldering workmanship, stable arc, little spatter, quick wire melting, strong anti-rust, suitable for all position weld. Contains higher levels of manganese and silicon than other standard grades of MIG wire to produce high quality welds when used on dirty, oily, or rusty steel. This product requires a shielding gas: CO2 and/or CO2 mix.
Typical Applications:
General shop applications with poor fit-up or rusty, oily plates
Steel castings or forging salvage
Home projects
Tanks, containers, pipes, ships, engineering machinery, steel structure and pressure vessiles.
Construction work
Welding Current for MIG process:
DCEP
Typical Wire Chemistry
C 0.07
Mn 1.58
Si 0.86
P 0.016
S 0.011
Cu 0.24
Typical Mechanical Properties
Rm(Mpa) 530
ReL(MPa) 430
A(%) 29
Akv(J)-29°C 90
Carbon Steel CO2 Welding Wire
Carbon Steel CO2 Welding Wire
AWS Specification: AWS A5.18
AWS Classification: ER70S-6
Carbon Steel CO2 Welding Wire
1) CO2 gas shielded
2) Stable electric arc
3) Low splashing
4) High eposition efficiency
5) Welds at any position
6) size: 0.8-1.6mm
7) applications: widely used as welding carbon steel wires in shipbuilding, bridge building, machinery manufacturing and general welding purposes
inner packing:
5kg/ 15kg/20kg /25kg spool packing.
250kg/ 350kg drum packing
welding wire: 27*10.5*27cm (0.8-1.6mm)15kg
outer packing:
welding wire: 27.5*10.5*27.cm (0.8-1.6mm)15kg
AWS Specification: AWS A5.18
AWS Classification: ER70S-6
Carbon Steel CO2 Welding Wire
1) CO2 gas shielded
2) Stable electric arc
3) Low splashing
4) High eposition efficiency
5) Welds at any position
6) size: 0.8-1.6mm
7) applications: widely used as welding carbon steel wires in shipbuilding, bridge building, machinery manufacturing and general welding purposes
inner packing:
5kg/ 15kg/20kg /25kg spool packing.
250kg/ 350kg drum packing
welding wire: 27*10.5*27cm (0.8-1.6mm)15kg
outer packing:
welding wire: 27.5*10.5*27.cm (0.8-1.6mm)15kg
Carbon Steel Wire Welding
welding wire:
1.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
2.Manufacturer.
3.Top quality,best price.
4.Good weldability
Welding Wire Description:
DY-YJ707(Q)is a basic type flux-cored wire designed for the 690Mpa class high tensile steels, and used for welding 690Mpa class high tensile steels.
Specification:
Typical Chemical Composition of Deposited Metal(%)
C
Mn
Si
S
P
Ni
Cr
Mo
Ti
<=0.12
<=1.75
<=0.60
<=0.03
<=0.03
2.00~2.50
<=0.50
0.25~0.65
<=0.03
0.05
1.65
0.50
0.008
0.012
2.20
0.35
0.41
0.015
Typical Mechanical Propertie of Deposited Metal
Yield Strength(Mpa)
Tensile (Mpa)
Elongation(%)
Charpy V-notch Impact Energy -40°C(J)
>=560
>=700
>=17
>=27
620
730
19
75
Size and Recommended Current Range(DC:Wire(+))
Wire Dia(mm)
1.2
1.4
1.6
Current Range(Amp)
Flat
120-300
150-380
180-420
Current Range(Amp)
Horizontal
120-300
150-350
180-380
Shielding gas:CO2 / 80%Ar +20%CO2
1.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
2.Manufacturer.
3.Top quality,best price.
4.Good weldability
Welding Wire Description:
DY-YJ707(Q)is a basic type flux-cored wire designed for the 690Mpa class high tensile steels, and used for welding 690Mpa class high tensile steels.
Specification:
Typical Chemical Composition of Deposited Metal(%)
C
Mn
Si
S
P
Ni
Cr
Mo
Ti
<=0.12
<=1.75
<=0.60
<=0.03
<=0.03
2.00~2.50
<=0.50
0.25~0.65
<=0.03
0.05
1.65
0.50
0.008
0.012
2.20
0.35
0.41
0.015
Typical Mechanical Propertie of Deposited Metal
Yield Strength(Mpa)
Tensile (Mpa)
Elongation(%)
Charpy V-notch Impact Energy -40°C(J)
>=560
>=700
>=17
>=27
620
730
19
75
Size and Recommended Current Range(DC:Wire(+))
Wire Dia(mm)
1.2
1.4
1.6
Current Range(Amp)
Flat
120-300
150-380
180-420
Current Range(Amp)
Horizontal
120-300
150-350
180-380
Shielding gas:CO2 / 80%Ar +20%CO2
Carbon Welding Electrode E6013 7018(Hero brand)
Carbon welding electrode E6013 7018
welding electrode AWS E6013 7016 7018
Certificate :ISO 9001:2000
welding electrode AWS E6013 7016 7018
Welding electrode is a kind of carbon steel electrode with titanium oxide coating
certificate:9001:2000
DIA:2.5mm*300/350mm 3.2mm*350mm 4.0mm*400mm 5.0mm*400mm
CARBON WELDING RODS WELDING ELECTRODEs welding stick E6013 (STONE BRIDGE /HERO BRAND)
welding electrodes:AWS E6013 7016 7018
2.Available size: 2.5mm*300/350mm 3.2mm*350mm 4.0mm*400mm 5.0mm*400mm
3.Chemical composition C<=0.12 Mn0.30-0.60 Si<=0.35 S<=0.035 P<=0.040
4.It is suitable for all position welding of steel sheets and irregular joints even under unfavorable conditions.
5.Has excellent welding technological performances.
6.The arc is stable and the spatter loss is negligible
7.It is better for welding structures of steel sheets,Vechicles,buildings,machinery-manufacture,vesseld and various structures of low carbon steel
8.The slag is fluid and when hardened it is compact and easy to remove
9.Packing:5kg per box 4 boxes per carton carton in pallets G.W 22.2KG N.W 20KG
10.Certificate:ISO 9001 nad CCS (China classification Socirty)
Package
1. Inner packing:
1) 2.5mm x 300mm, 5kg/inner box + plastic bag
2) 3.2mm x 350mm, 5kg/inner box + plastic bag
3) 4.0mm x 400mm, 5kg/inner box + plastic bag
2. Outer packing:20kg/carton
Item Code
GB
(AWS)
Chemical Composition Deposited Metal
Mechanical Properties of Deposited Metal
C
Mn
Si
S
P
others
R
el
/R
po.2
MPa
R
m
Mpa
A
%
Akv
J
J421
E4313
(E6013)
0.10
0.32/0.55
0.30
0.04
0.040
---
330
420
17
0
47
PLEASE CONTACT WITH ALICE
welding electrode AWS E6013 7016 7018
Certificate :ISO 9001:2000
welding electrode AWS E6013 7016 7018
Welding electrode is a kind of carbon steel electrode with titanium oxide coating
certificate:9001:2000
DIA:2.5mm*300/350mm 3.2mm*350mm 4.0mm*400mm 5.0mm*400mm
CARBON WELDING RODS WELDING ELECTRODEs welding stick E6013 (STONE BRIDGE /HERO BRAND)
welding electrodes:AWS E6013 7016 7018
2.Available size: 2.5mm*300/350mm 3.2mm*350mm 4.0mm*400mm 5.0mm*400mm
3.Chemical composition C<=0.12 Mn0.30-0.60 Si<=0.35 S<=0.035 P<=0.040
4.It is suitable for all position welding of steel sheets and irregular joints even under unfavorable conditions.
5.Has excellent welding technological performances.
6.The arc is stable and the spatter loss is negligible
7.It is better for welding structures of steel sheets,Vechicles,buildings,machinery-manufacture,vesseld and various structures of low carbon steel
8.The slag is fluid and when hardened it is compact and easy to remove
9.Packing:5kg per box 4 boxes per carton carton in pallets G.W 22.2KG N.W 20KG
10.Certificate:ISO 9001 nad CCS (China classification Socirty)
Package
1. Inner packing:
1) 2.5mm x 300mm, 5kg/inner box + plastic bag
2) 3.2mm x 350mm, 5kg/inner box + plastic bag
3) 4.0mm x 400mm, 5kg/inner box + plastic bag
2. Outer packing:20kg/carton
Item Code
GB
(AWS)
Chemical Composition Deposited Metal
Mechanical Properties of Deposited Metal
C
Mn
Si
S
P
others
R
el
/R
po.2
MPa
R
m
Mpa
A
%
Akv
J
J421
E4313
(E6013)
0.10
0.32/0.55
0.30
0.04
0.040
---
330
420
17
0
47
PLEASE CONTACT WITH ALICE
Carbon co2 er70s-6 Welding wire
WELDING WIREmig welding wire,co2 welding wire
Standard:AWS A5.28M:2005 GB/T 8110-2008
1kg,5kg,15kg,20kg
0.8 0.9 1.0 1.2 1.6MM
CARBON Co2 welding wire & gas shielded welding wire ER70S-6
Shijiazhuang Shiqiao Electrice Welding Material Co.,ltd
Conform with:
AWS A5.28M:2005 GB/T 8110-2008
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
welding with CO
2
gas and Ar+CO
2
gas mixtures.
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg per spool then packed in pallet
Certificate:ISO 9001 :2000
MOQ:one container
Transportantion:by sea
Original:Hebei China
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
Standard:AWS A5.28M:2005 GB/T 8110-2008
1kg,5kg,15kg,20kg
0.8 0.9 1.0 1.2 1.6MM
CARBON Co2 welding wire & gas shielded welding wire ER70S-6
Shijiazhuang Shiqiao Electrice Welding Material Co.,ltd
Conform with:
AWS A5.28M:2005 GB/T 8110-2008
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
welding with CO
2
gas and Ar+CO
2
gas mixtures.
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg per spool then packed in pallet
Certificate:ISO 9001 :2000
MOQ:one container
Transportantion:by sea
Original:Hebei China
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
Carbon dioxide protection wires(B) ER70S-6
carbon dioxide protection wires(B)
ER70S-6
Spec.:0.6 0.8 1.0
Oil, electronic, chemical, machinery, construction, aero
Carbon dioxide protection wires(B)
ER70S-6
has excellent performance, high efficiency, stable arc weld moulding, small splash, good, porosity, no crack characteristics, it is also used for argon protection and suitable for welding of high performance requirements
Oil, electronic, chemical, machinery, construction, aerospace, military industry, shipbuilding, etc
ER70S-6
Spec.:0.6 0.8 1.0
Oil, electronic, chemical, machinery, construction, aero
Carbon dioxide protection wires(B)
ER70S-6
has excellent performance, high efficiency, stable arc weld moulding, small splash, good, porosity, no crack characteristics, it is also used for argon protection and suitable for welding of high performance requirements
Oil, electronic, chemical, machinery, construction, aerospace, military industry, shipbuilding, etc
Carbon dioxide shielded welding wire
Our products has reached the national standard E4303 and US' standard AWS.Our product is of high quality and reasonable price.
This wire has g
ood
welding
performance.When welding,it is f
ast
melting and h
igh
deposition efficiency and it has s
table arc and less w
elding spatter.
It is used for carbon steel and v
ehicles,structure,shipbuilding and bridges that has 500MPa high-strength steel structure.It is also used for high-speed welding of sheet and pipe.
Our products has reached the national standard E4303 and US' standard AWS.Our product is of high quality and reasonable price.
This wire has g
ood
welding
performance.When welding,it is f
ast
melting and h
igh
deposition efficiency and it has s
table arc and less w
elding spatter.
It is used for carbon steel and v
ehicles,structure,shipbuilding and bridges that has 500MPa high-strength steel structure.It is also used for high-speed welding of sheet and pipe.
Our products has reached the national standard E4303 and US' standard AWS.Our product is of high quality and reasonable price.
Carbon dioxide welding wire
Carbon dioxide welding wire
1. Diameter: 0.8mm, 1.0mm, 1.2mm, 1.6mm
2. AWS ER70s-6
Carbon dioxide welding wire
It can be used for CO2 solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressure vessel etc.
1. Diameter: 0.8mm, 1.0mm, 1.2mm, 1.6mm
2. AWS ER70s-6
Carbon dioxide welding wire
It can be used for CO2 solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressure vessel etc.
Carbon dioxide welding wire
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressu
Arc stability, little spatter, high efficiency, and apply the position in welding.
CHS 50-6 can be used for CO2+Ar solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
Arc stability, little spatter, high efficiency, and apply the position in welding.
CHS 50-6 can be used for CO2+Ar solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
Carbon dioxide welding wire
Carbon dioxide welding wire
1. Diameter: 0.8mm, 1.0mm, 1.2mm, 1.6mm
2. AWS ER70s-6
It can be used for CO2 solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressure vessel etc.
1. Diameter: 0.8mm, 1.0mm, 1.2mm, 1.6mm
2. AWS ER70s-6
It can be used for CO2 solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressure vessel etc.
Carbon dioxide welding wire
Carbon dioxide welding wire
can be used for CO2 solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressure vessel etc
can be used for CO2 solid welding wire or CO2 solid welding wire. With excellent welding technological properties, stable arc, less spatter, a higher deposition efficiency. It is suitable for all positions.
The welding wire is used for welding low carbon structural steel and low alloy steel. Such as ships, heavy-duty machines, pressure vessel etc
Carbon steel Flux Cored Arc Welding E71T-1
Self-shielded flux cored wire is used for all-position welding,with little spatter,warming electric arc,easily moved slag
Welding wire Performance
The wire for calcium oxide-type fluoride slag, CO2 gas shielded flux cored wire. Its excellent performance welding process, DC DCRP, arc stability, a small spatter, slag from easy, weld forming good for the peace of welding, Wang 400km welding and welding. Molten metal excellent mechanical properties, diffusible hydrogen content is low, high impact toughness, cracking good.
The ratio of the weight content of the powder flux to the total weight content of titanium in the wire being from 0.3: 1 to 1: 1.
Type
Model
GB
Chemical composition(%)
C
Mn
Si
S
P
other
THY-51
E501T-1
0.18
1.75
0.90
0.030
0.030
THY-51B
E501T-1
0.18
1.75
0.90
0.030
0.030
THY-58
E501T-8
1.75
0.60
0.030
0.030
Al1.80
THY-A002
E308LT0-3
0.04
0.5-2.5
1.0
0.030
0.030
Cr18.0-21.0 Ni9.0-11.0
Chemical composition / Mechanicl propertise / Usage
Type
Model
GB
Mechanical properties
Rel/RP0.2
MPa
Rm MPa
A
%
AKV~!br!~J
THY-51
E501T-1
400
480
22
-20 º C
27
THY-51B
E501T-1
400
480
22
-20 º C
27
THY-58
E501T-8
400
480
22
-30 º C
27
THY-A002
E308LT0-3
-
520
35
-
Chemical composition / Mechanical properties / Usage
Type
Model (GB)
Usage
THY-51
E501T-1
For welding carbon steel and low-alloy steel structures like boat,bridge,pressure container and machine.
THY-51B
E501T-1
For welding structures like boat,bridge.It has strong ability to prevent surface blowhole.
THY-58
E501T-8
For on-spot installation of low carbon structures like boat,bridge,platform and other out-door welding and repairing.
THY-A002
E308LT0-3
For self-shielded welding of corrosion-resistant 00Cr19Ni10 and 0Cr18Ni11Ti stainless steel structures under 300 º C.Can also be used as tasnsition zone for difficult welding metal.
Packing:
export packing
HS Code:
83111
Min. Order:
5Tons
Transportation:
ocean shipping/land transportation
Welding wire Performance
The wire for calcium oxide-type fluoride slag, CO2 gas shielded flux cored wire. Its excellent performance welding process, DC DCRP, arc stability, a small spatter, slag from easy, weld forming good for the peace of welding, Wang 400km welding and welding. Molten metal excellent mechanical properties, diffusible hydrogen content is low, high impact toughness, cracking good.
The ratio of the weight content of the powder flux to the total weight content of titanium in the wire being from 0.3: 1 to 1: 1.
Type
Model
GB
Chemical composition(%)
C
Mn
Si
S
P
other
THY-51
E501T-1
0.18
1.75
0.90
0.030
0.030
THY-51B
E501T-1
0.18
1.75
0.90
0.030
0.030
THY-58
E501T-8
1.75
0.60
0.030
0.030
Al1.80
THY-A002
E308LT0-3
0.04
0.5-2.5
1.0
0.030
0.030
Cr18.0-21.0 Ni9.0-11.0
Chemical composition / Mechanicl propertise / Usage
Type
Model
GB
Mechanical properties
Rel/RP0.2
MPa
Rm MPa
A
%
AKV~!br!~J
THY-51
E501T-1
400
480
22
-20 º C
27
THY-51B
E501T-1
400
480
22
-20 º C
27
THY-58
E501T-8
400
480
22
-30 º C
27
THY-A002
E308LT0-3
-
520
35
-
Chemical composition / Mechanical properties / Usage
Type
Model (GB)
Usage
THY-51
E501T-1
For welding carbon steel and low-alloy steel structures like boat,bridge,pressure container and machine.
THY-51B
E501T-1
For welding structures like boat,bridge.It has strong ability to prevent surface blowhole.
THY-58
E501T-8
For on-spot installation of low carbon structures like boat,bridge,platform and other out-door welding and repairing.
THY-A002
E308LT0-3
For self-shielded welding of corrosion-resistant 00Cr19Ni10 and 0Cr18Ni11Ti stainless steel structures under 300 º C.Can also be used as tasnsition zone for difficult welding metal.
Packing:
export packing
HS Code:
83111
Min. Order:
5Tons
Transportation:
ocean shipping/land transportation
1KG/roll,solder wire with rosin core,63/37
Good qualit solder wire is
1:good humidity,bright beautiful,fast
2:and high isolation resistance after cleaning
3:less dross
Solder wire with rosin core
Shenzhen Jufeng Solder Co.,Ltd
is specialized in producing and selling tin products.Such as
tin solder bars,tin solder wires,tin ingots.
please contact me and inform me your latest requirements.Thank you.
Futures:
1. High purity, excellent weldability, good infiltration.
2. Clean, beautiful, after welding, insulation, high resistance, low ionic contamination, PCB board welding residual minimal.
3. Good oxidation resistance, low tin slag and cost savings.
4. Solder joint is bright, full and uniform.
5. Economical and can produce the lowest consumption of most of the solid solder joints.
Items:
1.Sn/Pb:20/80,25/75,...,40/60,50,50,60/40,63/37
2.Diameter:0.3mm-3.0mm
3.Weight:100,200,500g,...,600,800,900,1000g
Sn
Pb
Ag
Bi
As
Zn
Fe
Sb
Al
Cd
63±1
37±1
<0.005
<0.05
<0.03
<0.005
<0.02
<0.02
<0.02
<0.002
1:good humidity,bright beautiful,fast
2:and high isolation resistance after cleaning
3:less dross
Solder wire with rosin core
Shenzhen Jufeng Solder Co.,Ltd
is specialized in producing and selling tin products.Such as
tin solder bars,tin solder wires,tin ingots.
please contact me and inform me your latest requirements.Thank you.
Futures:
1. High purity, excellent weldability, good infiltration.
2. Clean, beautiful, after welding, insulation, high resistance, low ionic contamination, PCB board welding residual minimal.
3. Good oxidation resistance, low tin slag and cost savings.
4. Solder joint is bright, full and uniform.
5. Economical and can produce the lowest consumption of most of the solid solder joints.
Items:
1.Sn/Pb:20/80,25/75,...,40/60,50,50,60/40,63/37
2.Diameter:0.3mm-3.0mm
3.Weight:100,200,500g,...,600,800,900,1000g
Sn
Pb
Ag
Bi
As
Zn
Fe
Sb
Al
Cd
63±1
37±1
<0.005
<0.05
<0.03
<0.005
<0.02
<0.02
<0.02
<0.002
Carbon steel Flux Cored Welding wire E71T-1
1. Kinds of specifications
2. Strict Quality control and on-time delivery
3. Certified by many ship's classification society
Welding Wire Type:
Carbon Steel Flux-cored Wires.
Welding Position:
F, HF.
Chemical Composition of Deposited Metal (%):
Chemical Composition
C
Mn
Si
S
P
Cr
Ni
Mo
Cu
V
Standard
≤0.18
≤1.75
≤0.90
≤0.03
≤0.03
-
-
-
-
-
Mechanical Properties of Deposited Metal:
Mechanical Composition
Yield Point Rel (Mpa)
Tensile Strength Rm (Mpa)
Elongation A4(%)
Akv1(J)Tem
Shield Gas
≥480
≥400
≥22
≥47
CO2
Diameter (mm):
0.9, 1.0, 1.2, 1.4, 1.6
Application:
It is suitable for carbon steel and part of low alloy steel structure. Such as cars, buildings, ships, bridges and high speed welding.
2. Strict Quality control and on-time delivery
3. Certified by many ship's classification society
Welding Wire Type:
Carbon Steel Flux-cored Wires.
Welding Position:
F, HF.
Chemical Composition of Deposited Metal (%):
Chemical Composition
C
Mn
Si
S
P
Cr
Ni
Mo
Cu
V
Standard
≤0.18
≤1.75
≤0.90
≤0.03
≤0.03
-
-
-
-
-
Mechanical Properties of Deposited Metal:
Mechanical Composition
Yield Point Rel (Mpa)
Tensile Strength Rm (Mpa)
Elongation A4(%)
Akv1(J)Tem
Shield Gas
≥480
≥400
≥22
≥47
CO2
Diameter (mm):
0.9, 1.0, 1.2, 1.4, 1.6
Application:
It is suitable for carbon steel and part of low alloy steel structure. Such as cars, buildings, ships, bridges and high speed welding.
Carbon steel Flux Cored Welding wire
1. Kinds of specifications
2. Strict Quality control and on-time delivery
3. Certified by many ship's classification society
Welding Wire Type:
Carbon Steel Flux-cored Wires.
Welding Position:
F, HF.
Chemical Composition of Deposited Metal (%):
Chemical Composition
C
Mn
Si
S
P
Cr
Ni
Mo
Cu
V
Standard
≤0.18
≤1.75
≤0.90
≤0.03
≤0.03
-
-
-
-
-
Mechanical Properties of Deposited Metal:
Mechanical Composition
Yield Point Rel (Mpa)
Tensile Strength Rm (Mpa)
Elongation A4(%)
Akv1(J)Tem
Shield Gas
≥480
≥400
≥22
≥47
CO2
Diameter (mm):
0.9, 1.0, 1.2, 1.4, 1.6
Application:
It is suitable for carbon steel and part of low alloy steel structure. Such as cars, buildings, ships, bridges and high speed welding.
2. Strict Quality control and on-time delivery
3. Certified by many ship's classification society
Welding Wire Type:
Carbon Steel Flux-cored Wires.
Welding Position:
F, HF.
Chemical Composition of Deposited Metal (%):
Chemical Composition
C
Mn
Si
S
P
Cr
Ni
Mo
Cu
V
Standard
≤0.18
≤1.75
≤0.90
≤0.03
≤0.03
-
-
-
-
-
Mechanical Properties of Deposited Metal:
Mechanical Composition
Yield Point Rel (Mpa)
Tensile Strength Rm (Mpa)
Elongation A4(%)
Akv1(J)Tem
Shield Gas
≥480
≥400
≥22
≥47
CO2
Diameter (mm):
0.9, 1.0, 1.2, 1.4, 1.6
Application:
It is suitable for carbon steel and part of low alloy steel structure. Such as cars, buildings, ships, bridges and high speed welding.
Carbon steel Flux Cored Wire E71T-1
Flux-Cored Welding Wire E71T-1 is a tubular wire with a metallic powder flux inside.
AWS E71T-1
Flux-Cored Welding Wire
AWS A5.20 E71T-1
GB/T 10045-2001 E501T-1
Introduction:
AWS E71T-1 welding wire is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel. It’s a kind of titania type CO2 gas-shielded flux-cored welding wire which has excellent welding performance, soft and stable arc, fewer spatters, good slag detachability and beautiful appearance of weld. Suitable for downhand welding and horizontal welding. All-position welding.
Uses:
Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Such as building of ships, machines, steel structure and bridges, etc
Diameter: 0.9-1.6mm flux cored welding wire
Certificate of Approval: CCS, ABS,GL,BV,LR,NK,DNV,KR,RINA
Packing: 15kgs /spool+ppbag+carton
AWS E71T-1
Flux-Cored Welding Wire
AWS A5.20 E71T-1
GB/T 10045-2001 E501T-1
Introduction:
AWS E71T-1 welding wire is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel. It’s a kind of titania type CO2 gas-shielded flux-cored welding wire which has excellent welding performance, soft and stable arc, fewer spatters, good slag detachability and beautiful appearance of weld. Suitable for downhand welding and horizontal welding. All-position welding.
Uses:
Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Such as building of ships, machines, steel structure and bridges, etc
Diameter: 0.9-1.6mm flux cored welding wire
Certificate of Approval: CCS, ABS,GL,BV,LR,NK,DNV,KR,RINA
Packing: 15kgs /spool+ppbag+carton
Carbon steel Submerged Arc Welding Wire AWS EL8
Carbon steel Submerged arc welding wire H08A
high efficiency small splash good welding line
AWS EL8 EM12 EM12K EH14
1.6-4.0MM
Tiptop Submerged Arc Welding Wire
EH14(H10MN2) EL8 H08A EM12 H08MNA-Hero/SQ brand
Submerged-Arc Welding Wire EL8 EM12 EM12K EH14
stone bridge welding/Hero brand
welding wire with flux AWS A5.17 welding electrode
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----
Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650
Product specification /features:
standardization :EL8 EL12 EM12K EH11K EH12K EH14
Specifications :2.mm 2.4mm 3.2mm 4.0mm
Type of packing :25kg 50kg 100kg 200kg 300kg
Packing material:carton knitting bag wooden spool
Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days
high efficiency small splash good welding line
AWS EL8 EM12 EM12K EH14
1.6-4.0MM
Tiptop Submerged Arc Welding Wire
EH14(H10MN2) EL8 H08A EM12 H08MNA-Hero/SQ brand
Submerged-Arc Welding Wire EL8 EM12 EM12K EH14
stone bridge welding/Hero brand
welding wire with flux AWS A5.17 welding electrode
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----
Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650
Product specification /features:
standardization :EL8 EL12 EM12K EH11K EH12K EH14
Specifications :2.mm 2.4mm 3.2mm 4.0mm
Type of packing :25kg 50kg 100kg 200kg 300kg
Packing material:carton knitting bag wooden spool
Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days
Carbon steel Submerged Arc Welding Wire AWS EM12
Carbon steel Submerged arc welding wire H08MNA
high efficiency small splash good welding line
AWS EL8 EM12 EM12K EH14
CARBON STEEL
Submerged Arc Welding Wire
EH14(H10MN2) EL8 H08A EM12 H08MNA-Hero/SQ brand
Submerged-Arc Welding Wire EL8 EM12 EM12K EH14
stone bridge welding/Hero brand
welding wire with flux AWS A5.17 welding electrode
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----
Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650
Product specification /features:
standardization :EL8 EL12 EM12K EH11K EH12K EH14
Specifications :2.mm 2.4mm 3.2mm 4.0mm
Type of packing :25kg 50kg 100kg 200kg 300kg
Packing material:carton knitting bag wooden spool
Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days
high efficiency small splash good welding line
AWS EL8 EM12 EM12K EH14
CARBON STEEL
Submerged Arc Welding Wire
EH14(H10MN2) EL8 H08A EM12 H08MNA-Hero/SQ brand
Submerged-Arc Welding Wire EL8 EM12 EM12K EH14
stone bridge welding/Hero brand
welding wire with flux AWS A5.17 welding electrode
Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.
Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----
Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650
Product specification /features:
standardization :EL8 EL12 EM12K EH11K EH12K EH14
Specifications :2.mm 2.4mm 3.2mm 4.0mm
Type of packing :25kg 50kg 100kg 200kg 300kg
Packing material:carton knitting bag wooden spool
Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days
Carbon steel submerged arc welding wire EM12K,EL-8,EH14,EM13K
submerged arc welding wire:
1.good anti-pore performance
2. welding slag is easy to flake,
3.high welding efficiency
Stone Bridge Brand Carbon steel submerged arc welding wire
Model:EM12K,EL-8,EH14,EM13K
Feature:
Catrbon Steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structre,such as bolis,nuclear stations,chemical containers,ships,pressure containers etc.
Description:
EL-8(H08A):For welding carbon steel of 450MPa and low alloy steel
EM1(H08MnA)2:For welding carbon steel and low alloy steel structures of relevant strength grade
H08Mn2SiA:For welding carbon steel and low alloy steel
EH14(H10Mn2):For welding carbon steel of 500MPa and low alloy steel
EM13K(H10MnSi):For welding important strength of low carbon steel and low alloy ateel,such as boilers,nuchear power station conatainers,pressure sontainers etc
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.1
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn
0.11
1.91
0.03
0.001
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength
Mpa
Yield Point
%
Elongation
%
AKV-20
J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
1.good anti-pore performance
2. welding slag is easy to flake,
3.high welding efficiency
Stone Bridge Brand Carbon steel submerged arc welding wire
Model:EM12K,EL-8,EH14,EM13K
Feature:
Catrbon Steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structre,such as bolis,nuclear stations,chemical containers,ships,pressure containers etc.
Description:
EL-8(H08A):For welding carbon steel of 450MPa and low alloy steel
EM1(H08MnA)2:For welding carbon steel and low alloy steel structures of relevant strength grade
H08Mn2SiA:For welding carbon steel and low alloy steel
EH14(H10Mn2):For welding carbon steel of 500MPa and low alloy steel
EM13K(H10MnSi):For welding important strength of low carbon steel and low alloy ateel,such as boilers,nuchear power station conatainers,pressure sontainers etc
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.1
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn
0.11
1.91
0.03
0.001
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength
Mpa
Yield Point
%
Elongation
%
AKV-20
J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Carbon steel submerged arc welding wire EM12K,EL-8,EH14,EM13K
submerged arc welding wire:
1.Model:H08A,H08MnA,H10Mn2,H10Mnsi
2.welding slag is easy to flake
3.high welding efficiency
Stone Bridge Brand Carbon steel submerged arc welding wire
Model:AWS:EM12K,EL-8,EH14,EM13K
G B:H08A,H08MnA,H10Mn2,H10Mnsi
Feature:
Catrbon Steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structre,such as bolis,nuclear stations,chemical containers,ships,pressure containers etc.
Description:
EL-8(H08A):For welding carbon steel of 450MPa and low alloy steel
EM1(H08MnA)2:For welding carbon steel and low alloy steel structures of relevant strength grade
H08Mn2SiA:For welding carbon steel and low alloy steel
EH14(H10Mn2):For welding carbon steel of 500MPa and low alloy steel
EM13K(H10MnSi):For welding important strength of low carbon steel and low alloy ateel,such as boilers,nuchear power station conatainers,pressure sontainers etc
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.1
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn
0.11
1.91
0.03
0.001
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength
Mpa
Yield Point
%
Elongation
%
AKV-20
J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
1.Model:H08A,H08MnA,H10Mn2,H10Mnsi
2.welding slag is easy to flake
3.high welding efficiency
Stone Bridge Brand Carbon steel submerged arc welding wire
Model:AWS:EM12K,EL-8,EH14,EM13K
G B:H08A,H08MnA,H10Mn2,H10Mnsi
Feature:
Catrbon Steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structre,such as bolis,nuclear stations,chemical containers,ships,pressure containers etc.
Description:
EL-8(H08A):For welding carbon steel of 450MPa and low alloy steel
EM1(H08MnA)2:For welding carbon steel and low alloy steel structures of relevant strength grade
H08Mn2SiA:For welding carbon steel and low alloy steel
EH14(H10Mn2):For welding carbon steel of 500MPa and low alloy steel
EM13K(H10MnSi):For welding important strength of low carbon steel and low alloy ateel,such as boilers,nuchear power station conatainers,pressure sontainers etc
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.1
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn
0.11
1.91
0.03
0.001
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength
Mpa
Yield Point
%
Elongation
%
AKV-20
J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Carbon steel submerged arc welding wire
GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.
The submerged arc welding is proved by ISO9001:2000.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.
The submerged arc welding is proved by ISO9001:2000.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
Carbon steel submerged arc welding wire
GB:H08A,H08MnA,H10Mn2,H08Mn2SiA,H10MnSi
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.
The submerged arc welding is proved by ISO9001:2000.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
AWS:EL-8,EM-12,EH14,EM13K
Factory supply high quality products with best prices.
The submerged arc welding is proved by ISO9001:2000.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
Carbon steel submerged arc welding wire
Good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
The submerged arc welding is proved by ISO9001:2000.
They are applicable for carbon steel, low alloy steel structure, lamella, high tensile steel,etc.
And be good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
The submerged arc welding is proved by ISO9001:2000.
They are applicable for carbon steel, low alloy steel structure, lamella, high tensile steel,etc.
And be good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
1mm stainless steel wire
1mm stainless steel wire
1.0.8mm-5.5mm
2.manufacturer provide
3.can be customized
4.quick lead time
1mm Stainless steel wire
standards
: ASTM,GB,EN,JIN
mater
ial
: ER308 ER309 ER310 ER316 ER2209 ER347 ER321 ER304 ER301 ER201 ER904 ER308L ER308L-G ER309MoL ER308Si ER309Si ER430LNB H1Cr13 ER90S-B3 ER90S-B9
diameter:
0.8mm-5.5mm
feature:
1. Perfect welding technology with excellent resistance to intergranular corrosion.
2. Beautiful welding appearance
3. Good resistance to cracking
4. Arc stability, good corrosion resistance, mechanical properties and working ability
uses:
wire-drawing,weaving of wire mesh,soft pipe,beam of cabinet, steel wire rope, fiter material and equipment,spring,aerospace, military production, nuclear power, petrochemical, machinery, automobiles, household appliance, medical equipment, food machinery, construction, decoration, high temperature heating device,etc.
quotation need data:
material+diameter+packing weight
Bitmap
Jiangsu Xinghai Special Steel Co.,Ltd
AWS
Chemical compositions of stainless steel welding wire(≤%)
C
Si
Mn
P
S
Cr
Ni
Mo
H08Cr21Ni10
ER308
0.06
0.30
1.50
0.022
0.010
20.8
9.80
≤0.5
H06Cr21Ni10
ER308
0.045
0.30
1.50
0.022
0.010
20.8
9.80
≤0.5
H03Cr21Ni10
ER308L
0.023
0.30
1.50
0.022
0.010
20.8
9.80
≤0.5
H12Cr24Ni13
ER309
0.07
0.30
1.50
0.022
0.010
23.55
13.20
≤0.5
H03Cr24Ni13
ER309L
0.022
0.28
1.50
0.022
0.010
23.7
13.20
≤0.5
H08Cr26Ni21
ER310
0.07
0.26
1.50
0.022
0.010
25.8
20.7
≤0.5
H12Cr26Ni21
ER310
0.09
0.26
1.50
0.020
0.010
25.5
21.30
≤0.5
H21Cr16Ni35
ER330
0.20
0.25
1.50
0.022
0.010
16.5
34.5
≤0.5
H08Cr19Ni12Mo2
ER316
0.07
0.30
1.50
0.022
0.010
19.5
11.80
2.30
H06Cr19Ni12Mo2
ER316
0.05
0.30
1.50
0.022
0.010
19.5
11.80
2.30
H03Cr19Ni12Mo2
ER316L
0.020
0.28
1.50
0.022
0.010
19.8
12.20
2.50
H08Cr19Ni14Mo3
ER317
0.06
0.30
1.50
0.022
0.010
18.8
13.60
3.40
H03Cr19Ni14Mo3
ER317L
0.02
0.28
1.50
0.022
0.010
18.8
13.80
3.60
H08Cr19Ni12Mo2Nb
ER318
0.06
0.30
1.50
0.022
0.010
18.5
11.80
2.30
H07Cr20Ni34Mo2Cu3Nb
ER320
0.06
0.30
1.00
0.022
0.010
19.8
33.3
2.80
Nb0.7
H02Cr20Ni34Mo2Cu3Nb
ER320L
0.018
0.15
1.50
0.013
0.010
19.8
33.60
2.50
Nb0.35
H08Cr20Ni10Ti
ER321
0.06
0.35
1.50
0.022
0.010
20.8
9.80
≤0.5
Ti9×C-1.0
H08Cr21Ni10Nb
ER347
0.055
0.30
1.50
0.022
0.010
20.8
9.80
Nb10×C-1.0
H02Cr27Ni32Mo3Cu
ER383
0.018
0.30
1.50
0.017
0.010
27.5
32.50
3.5
Cu 1.10
H02Cr20Ni25Mo4Cu
ER385
0.020
0.30
1.50
0.018
0.010
20.2
24.80
4.80
Cu 1.80
H03Cr22Ni9Mo3N
ER2209
0.022
0.40
0.90
0.022
0.010
22.5
8.80
3.50
N0.08-0.20
H04Cr25Ni5Mo3Cu2N
ER2553
0.027
0.50
1.00
0.025
0.015
24.8
5.50
3.20
N0.1-0.25
H15Cr29Ni9
ER312
0.09
0.38
1.50
0.022
0.010
29.5
8.50
H03Cr24Ni13MoL
ER309LMo
0.023
0.35
1.50
0.022
0.010
23.8
13.20
2.20
H05Cr17Ni4Cu4Nb
ER630
0.04
0.39
0.50
0.022
0.010
16.5
4.80
Cu;3 Nb;0.28
H08Cr26Ni5Mo2
ER453s
0.06
0.30
0.40
0.022
0.010
25.8
4.80
2.10
H08Cr21Ni10Mn6
0.06
0.35
5.50
0.022
0.010
20.8
9.80
H05Cr22Ni11Mn6Mo3VN
ER209
0.04
0.40
4.50
0.022
0.010
21.5
10.80
2.20
N;0.20 V;0.18
1.0.8mm-5.5mm
2.manufacturer provide
3.can be customized
4.quick lead time
1mm Stainless steel wire
standards
: ASTM,GB,EN,JIN
mater
ial
: ER308 ER309 ER310 ER316 ER2209 ER347 ER321 ER304 ER301 ER201 ER904 ER308L ER308L-G ER309MoL ER308Si ER309Si ER430LNB H1Cr13 ER90S-B3 ER90S-B9
diameter:
0.8mm-5.5mm
feature:
1. Perfect welding technology with excellent resistance to intergranular corrosion.
2. Beautiful welding appearance
3. Good resistance to cracking
4. Arc stability, good corrosion resistance, mechanical properties and working ability
uses:
wire-drawing,weaving of wire mesh,soft pipe,beam of cabinet, steel wire rope, fiter material and equipment,spring,aerospace, military production, nuclear power, petrochemical, machinery, automobiles, household appliance, medical equipment, food machinery, construction, decoration, high temperature heating device,etc.
quotation need data:
material+diameter+packing weight
Bitmap
Jiangsu Xinghai Special Steel Co.,Ltd
AWS
Chemical compositions of stainless steel welding wire(≤%)
C
Si
Mn
P
S
Cr
Ni
Mo
H08Cr21Ni10
ER308
0.06
0.30
1.50
0.022
0.010
20.8
9.80
≤0.5
H06Cr21Ni10
ER308
0.045
0.30
1.50
0.022
0.010
20.8
9.80
≤0.5
H03Cr21Ni10
ER308L
0.023
0.30
1.50
0.022
0.010
20.8
9.80
≤0.5
H12Cr24Ni13
ER309
0.07
0.30
1.50
0.022
0.010
23.55
13.20
≤0.5
H03Cr24Ni13
ER309L
0.022
0.28
1.50
0.022
0.010
23.7
13.20
≤0.5
H08Cr26Ni21
ER310
0.07
0.26
1.50
0.022
0.010
25.8
20.7
≤0.5
H12Cr26Ni21
ER310
0.09
0.26
1.50
0.020
0.010
25.5
21.30
≤0.5
H21Cr16Ni35
ER330
0.20
0.25
1.50
0.022
0.010
16.5
34.5
≤0.5
H08Cr19Ni12Mo2
ER316
0.07
0.30
1.50
0.022
0.010
19.5
11.80
2.30
H06Cr19Ni12Mo2
ER316
0.05
0.30
1.50
0.022
0.010
19.5
11.80
2.30
H03Cr19Ni12Mo2
ER316L
0.020
0.28
1.50
0.022
0.010
19.8
12.20
2.50
H08Cr19Ni14Mo3
ER317
0.06
0.30
1.50
0.022
0.010
18.8
13.60
3.40
H03Cr19Ni14Mo3
ER317L
0.02
0.28
1.50
0.022
0.010
18.8
13.80
3.60
H08Cr19Ni12Mo2Nb
ER318
0.06
0.30
1.50
0.022
0.010
18.5
11.80
2.30
H07Cr20Ni34Mo2Cu3Nb
ER320
0.06
0.30
1.00
0.022
0.010
19.8
33.3
2.80
Nb0.7
H02Cr20Ni34Mo2Cu3Nb
ER320L
0.018
0.15
1.50
0.013
0.010
19.8
33.60
2.50
Nb0.35
H08Cr20Ni10Ti
ER321
0.06
0.35
1.50
0.022
0.010
20.8
9.80
≤0.5
Ti9×C-1.0
H08Cr21Ni10Nb
ER347
0.055
0.30
1.50
0.022
0.010
20.8
9.80
Nb10×C-1.0
H02Cr27Ni32Mo3Cu
ER383
0.018
0.30
1.50
0.017
0.010
27.5
32.50
3.5
Cu 1.10
H02Cr20Ni25Mo4Cu
ER385
0.020
0.30
1.50
0.018
0.010
20.2
24.80
4.80
Cu 1.80
H03Cr22Ni9Mo3N
ER2209
0.022
0.40
0.90
0.022
0.010
22.5
8.80
3.50
N0.08-0.20
H04Cr25Ni5Mo3Cu2N
ER2553
0.027
0.50
1.00
0.025
0.015
24.8
5.50
3.20
N0.1-0.25
H15Cr29Ni9
ER312
0.09
0.38
1.50
0.022
0.010
29.5
8.50
H03Cr24Ni13MoL
ER309LMo
0.023
0.35
1.50
0.022
0.010
23.8
13.20
2.20
H05Cr17Ni4Cu4Nb
ER630
0.04
0.39
0.50
0.022
0.010
16.5
4.80
Cu;3 Nb;0.28
H08Cr26Ni5Mo2
ER453s
0.06
0.30
0.40
0.022
0.010
25.8
4.80
2.10
H08Cr21Ni10Mn6
0.06
0.35
5.50
0.022
0.010
20.8
9.80
H05Cr22Ni11Mn6Mo3VN
ER209
0.04
0.40
4.50
0.022
0.010
21.5
10.80
2.20
N;0.20 V;0.18
Carbon steel submerged arc welding wire
Good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
The submerged arc welding is proved by ISO9001:2000.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
The submerged arc welding is proved by ISO9001:2000.
Carbon steel submerged arc welding wires are used with corresponding flux and gotten excellent mechanical seam.They have a series of advantages,such as high effciency,stable welding quality,high depositing efficiency etc.
The series of welding wires are used to welding important low carbon steel and low allow steel structure,such as boils,nuclear stations,chemical containers,ships,pressure containers etc.They have good anti-pore performance, the welding slag is easy to flake, high welding efficiency and tenacity.
Deposited metal Chemistry Composition:
TYPE
C
Mn
Si
P
S
Cu
H08A
0.07
0.5
0.01
0.0009
0.016
0.01
H08MnA
0.07
0.94
0.24
0.011
0.025
0.01
H10Mn2
0.11
1.91
0.03
0.01
0.019
0.01
Deposited metal Machine Functions:
TYPE
Tensile Strength Mpa
Yield Point %
Elongation %
AKV-20 J
H08A
238
427
29
44
H08MnA
521
425
32
85
H10Mn2
554
465
30
78
Diameter and Current:
Diameter (mm)
2.5mm
3.2mm
4.0mm
5.0mm
Currents (A)
350-450
425-525
475-575
550-650
Friday, August 19, 2011
(co2) Gas shielded welding wire AWS 5.18 ER70S-6/DIN SG2/BS A18/JIS YGM
CO2 Gas Shielded Welding Wire (AWS ER70S-6)
1.mig welding wire/co2 welding wire
2.welding material
CE SONCAP IEI COC BV
Qualified CO2 protect Welding wire ER70S-6 0.8/0.9/1.0/1.2/1.6/2.0mm
Solid/copper coated welding wire ER70S-6 A5.18 SG2
Mig welding wire /co2 gas shielded welding wire SG2
CE SONCAP IEI COC BV SGS AWS CERTIFICATE
Brand :stone bridge /hero
Shijiazhuang Shiqiao Electric Welding Material Co.,ltd
Brand type:SQ ER70S-6
Material :ER70S-6 Ø5.5MM
Products Specification:0.8mm-1.6mm
Classification:Recommended products
Products introduction:SQ ER70S-6
Standard :GB ER50S-6
Equal:AWS 5.18 ER70S-6/DIN SG2/BS A18/JIS YGM
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
welding wire chemical composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Please contact with Ms Alice
1.mig welding wire/co2 welding wire
2.welding material
CE SONCAP IEI COC BV
Qualified CO2 protect Welding wire ER70S-6 0.8/0.9/1.0/1.2/1.6/2.0mm
Solid/copper coated welding wire ER70S-6 A5.18 SG2
Mig welding wire /co2 gas shielded welding wire SG2
CE SONCAP IEI COC BV SGS AWS CERTIFICATE
Brand :stone bridge /hero
Shijiazhuang Shiqiao Electric Welding Material Co.,ltd
Brand type:SQ ER70S-6
Material :ER70S-6 Ø5.5MM
Products Specification:0.8mm-1.6mm
Classification:Recommended products
Products introduction:SQ ER70S-6
Standard :GB ER50S-6
Equal:AWS 5.18 ER70S-6/DIN SG2/BS A18/JIS YGM
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
welding wire chemical composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Please contact with Ms Alice
2# Solder Wire
Features:
1) Diameter: 0.5mm-3.0mm
2) Sn/Pb: 63/37,60/40,55/45,50/50,40/60,30/70,20/80
3)Weight:50-1000g
2# solder wire:
1)It's suitable for the lighting and electronic products soldering which has high reliability and excellent solderability,we can supply 1#,2#,3#,4# various types solder wire.
2)It generates less smoke,less smell during the soldering work.
3)Good properties in resisting the soldering spots brige.With bright and nice soldering spots and high surface insulation resistance.
1) Diameter: 0.5mm-3.0mm
2) Sn/Pb: 63/37,60/40,55/45,50/50,40/60,30/70,20/80
3)Weight:50-1000g
2# solder wire:
1)It's suitable for the lighting and electronic products soldering which has high reliability and excellent solderability,we can supply 1#,2#,3#,4# various types solder wire.
2)It generates less smoke,less smell during the soldering work.
3)Good properties in resisting the soldering spots brige.With bright and nice soldering spots and high surface insulation resistance.
Carbon steel welding wire
Co2 gas shielded welding wire has the excellent mechanical performance.
AWS
Chemical Composition(%)
Main Applications
C
Mn
Si
S
P
Cr
Ni
Cu
ER70S-3
0.06-0.15
0.9-1.4
0.45-0.75
≤0.035
≤0.025
-
-
≤0.50
Used for welding 450 and 500MPa structural steel with single and mutipass welding.
ER70S-6
≤0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
-
-
≤0.50
Used for welding 500MPa low alloy steel single and mutipass welding;also for high speed thin plates ,pipe line steel welding
AWS
Chemical Composition(%)
Main Applications
C
Mn
Si
S
P
Cr
Ni
Cu
ER70S-3
0.06-0.15
0.9-1.4
0.45-0.75
≤0.035
≤0.025
-
-
≤0.50
Used for welding 450 and 500MPa structural steel with single and mutipass welding.
ER70S-6
≤0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
-
-
≤0.50
Used for welding 500MPa low alloy steel single and mutipass welding;also for high speed thin plates ,pipe line steel welding
Carbon/MIG Welding Wire (0.8 0.9 1.0 1.2 1.6 2.0mm)
Carbon /MIG welding wire (0.8 0.9 1.0 1.2 1.6 2.0mm)
Carbon steel welding wire
Gas shielded welding wire/ER50-6/ER70s-6
Carbon /MIG Welding Wire (0.8 0.9 1.0 1.2 1.6 2.0mm)
gas shielded welding wire ER50-6
mig welding wire
STONE BRIDGE BRAND
SHIJIAZHUANG SHIQIAO ELCTRIC WELDING MATERIAL CO.,LTD
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle,
the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Carbon steel welding wire
Gas shielded welding wire/ER50-6/ER70s-6
Carbon /MIG Welding Wire (0.8 0.9 1.0 1.2 1.6 2.0mm)
gas shielded welding wire ER50-6
mig welding wire
STONE BRIDGE BRAND
SHIJIAZHUANG SHIQIAO ELCTRIC WELDING MATERIAL CO.,LTD
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle,
the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Carton fair promotion sale co2 welding wire AWS ER70S-6
mig/co2 welding wire AWS ER70S-6
Dia:0.6-0.8-1.0-1.2-1.6mm
Packing: 5-15-20kg
ISO certificate!
Free Samples
CO2 Welding wire,
MIG WIRE
MIG WELDING WIRE./
SG2 WIRE
Welcome to our booth: 15.4 G38. DATE FROM 15TH-19TH OCT 2010.
BOOTH TEL:0086-15931105031
ER70S-6
Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.
ADVANTAGE
Excellent Welding
•Characteristics-ER70S-6 Wire renders good wetting action, straight bead edges, excellent arc action and high resistance to rust or mill scale porosity.
•More Resistance to porosity in the weld deposit.
SPOOL TYPE: WHITE/BLACK SPOOL:D200 270 300. METAL FRAME: K300
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable
CONFORMANCE
Conforms to ER70S-6 per
AWS A5.18
ABS : 3YSA
CCS : 3YSM
DNV : IIIYMS
Dia:0.6-0.8-1.0-1.2-1.6mm
Packing: 5-15-20kg
ISO certificate!
Free Samples
CO2 Welding wire,
MIG WIRE
MIG WELDING WIRE./
SG2 WIRE
Welcome to our booth: 15.4 G38. DATE FROM 15TH-19TH OCT 2010.
BOOTH TEL:0086-15931105031
ER70S-6
Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.
ADVANTAGE
Excellent Welding
•Characteristics-ER70S-6 Wire renders good wetting action, straight bead edges, excellent arc action and high resistance to rust or mill scale porosity.
•More Resistance to porosity in the weld deposit.
SPOOL TYPE: WHITE/BLACK SPOOL:D200 270 300. METAL FRAME: K300
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
•Any Application Where a "Finished" Weld Appearance is Desirable
CONFORMANCE
Conforms to ER70S-6 per
AWS A5.18
ABS : 3YSA
CCS : 3YSM
DNV : IIIYMS
China Flux Cored Wire Manufacturer
China Flux Cored Wire Manufacturer:
1.all position capability
2.Low fume&spatter
3.good slag removable
4.ABS,BV,LR,GL,DNV
China Flux Cored Wire Manufacturer
Arame Tubular Wire:
E71T-1
The FRW-71Ni range of flux cored wire reduces production costs through higher deposition rates with excellent high integrity deposits. Superb weld profiles with low spatter and fume levels result in good operator appeal.
Applications:
China Flux Cored Wire Manufacturer/Arame Tubular Wire is s
uitable for applications such as shipbuilding,oil platform,storage tanks, structural fabrication, machinery, earth moving equipment and fatigue loaded structures.
Chemical compostiton of deposited metal (shield gas:co2):
C
Mn
Si
P
S
0.036
1.40
0.52
0.013
0.011
Mechanical properties of deposited metal (shield gas:co2)
Yield Strength
Mpa(σb)
Tensile Strength
Mpa(σb)
Elongation
%(δ5)
Impact Value
-20°C(J)
505
570
26
120
Shipping approvals:
ABS,LR,BV,GL,DNV,KR,CCS,CE.
1.all position capability
2.Low fume&spatter
3.good slag removable
4.ABS,BV,LR,GL,DNV
China Flux Cored Wire Manufacturer
Arame Tubular Wire:
E71T-1
The FRW-71Ni range of flux cored wire reduces production costs through higher deposition rates with excellent high integrity deposits. Superb weld profiles with low spatter and fume levels result in good operator appeal.
Applications:
China Flux Cored Wire Manufacturer/Arame Tubular Wire is s
uitable for applications such as shipbuilding,oil platform,storage tanks, structural fabrication, machinery, earth moving equipment and fatigue loaded structures.
Chemical compostiton of deposited metal (shield gas:co2):
C
Mn
Si
P
S
0.036
1.40
0.52
0.013
0.011
Mechanical properties of deposited metal (shield gas:co2)
Yield Strength
Mpa(σb)
Tensile Strength
Mpa(σb)
Elongation
%(δ5)
Impact Value
-20°C(J)
505
570
26
120
Shipping approvals:
ABS,LR,BV,GL,DNV,KR,CCS,CE.
China filler metal
TiBright flux-cored silver brazing materials numerous advantages compared to traditional metal-joining methods. It consists of a
Flux Cored Silver Brazing Material
Availability:
TiBright flux-cored silver brazing materials numerous advantages compared to traditional metal-joining methods. It consists of a filler metal in strip form that is rolled around a powdered flux. For mostly instead of hand manual torch brazing, especially recommend for automatically brazing working cycle.
Product size:
Product size: the most commonly used diameter lengths are: 1.5 mm, 1.6 mm, 1.8 mm, 2.0 mm, 2.4 mm, . We can also specially make the size to meet the requirements of our customers.
Advantages:
Flux and relative operations are not needed.
Workers and equipments are not exposed to dust atmosphere.
Precise composition of materials can reduce the amount of pores and enhance the quality of the welding points. Environmental friendly, non-corrosive, no post cleaning needed.
Length:
400mm,450mm,500mm,914mm,1000mm.
Packing:
0.5kg,1kg,2kg,2.25kg,5kg/roll. 10 Kg/Roll
Class modification
Melting/Solid Temperature
Brazing
Temperature
Brazing alloy Composition
Ag
Cu
Zn
Sn
Others
FC-316
608 — 630 °C
650— 760°C
56
24
5
15
< 0.15.
FC-303
675--743°C
780-850°C
45
30
25
--
< 0.15
FC-322
650 – 710 °C
720--815 °C
40
30
30
< 0.15
FC-314
660--740 °C
750--830 °C
35
39
25
1
< 0.15
FC-311
675--765°C
770--870°C
30
38
32
--
< 0.15
Flux Cored Silver Brazing Material
Availability:
TiBright flux-cored silver brazing materials numerous advantages compared to traditional metal-joining methods. It consists of a filler metal in strip form that is rolled around a powdered flux. For mostly instead of hand manual torch brazing, especially recommend for automatically brazing working cycle.
Product size:
Product size: the most commonly used diameter lengths are: 1.5 mm, 1.6 mm, 1.8 mm, 2.0 mm, 2.4 mm, . We can also specially make the size to meet the requirements of our customers.
Advantages:
Flux and relative operations are not needed.
Workers and equipments are not exposed to dust atmosphere.
Precise composition of materials can reduce the amount of pores and enhance the quality of the welding points. Environmental friendly, non-corrosive, no post cleaning needed.
Length:
400mm,450mm,500mm,914mm,1000mm.
Packing:
0.5kg,1kg,2kg,2.25kg,5kg/roll. 10 Kg/Roll
Class modification
Melting/Solid Temperature
Brazing
Temperature
Brazing alloy Composition
Ag
Cu
Zn
Sn
Others
FC-316
608 — 630 °C
650— 760°C
56
24
5
15
< 0.15.
FC-303
675--743°C
780-850°C
45
30
25
--
< 0.15
FC-322
650 – 710 °C
720--815 °C
40
30
30
< 0.15
FC-314
660--740 °C
750--830 °C
35
39
25
1
< 0.15
FC-311
675--765°C
770--870°C
30
38
32
--
< 0.15
China hot products Co2 welding wire ER70S-6(Bright copper)
co2 Welding wire ER70S-6 bright copper
1.welding wire ER70S-6
2.welding consumables
3.mig welding wire
4.5kg/15kg/20kg/spool
Shijiazhuang SHiqiao Electrice Welding Material Co.,ltd
WE ARE MANUFACTURER OF WELDING WIRE WITH STONE BRIDGE
/hero brand
china hot products Co2 welding wire ER70S-6(Bright copper)
co2 gas protect welding wire/consumables (ER70S-6)
co2 welding wire /mig welding wire
Welding Wire,
1. Diameter: 0.8-1.2mm;
2. Packing: 25kgs spools - 250 drum;
3. Standard:AWS ER70S-6
co2 Welding Wire ER70S-6
Description:
ER70S-6 is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
all position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Original :Shijiazhuang
1.welding wire ER70S-6
2.welding consumables
3.mig welding wire
4.5kg/15kg/20kg/spool
Shijiazhuang SHiqiao Electrice Welding Material Co.,ltd
WE ARE MANUFACTURER OF WELDING WIRE WITH STONE BRIDGE
/hero brand
china hot products Co2 welding wire ER70S-6(Bright copper)
co2 gas protect welding wire/consumables (ER70S-6)
co2 welding wire /mig welding wire
Welding Wire,
1. Diameter: 0.8-1.2mm;
2. Packing: 25kgs spools - 250 drum;
3. Standard:AWS ER70S-6
co2 Welding Wire ER70S-6
Description:
ER70S-6 is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
all position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Original :Shijiazhuang
Clean and smooth flux cored wire E71T-1/1.4
flux cored wire E71T-1/1.4
competetive price, good quality and effective lead time
Rutile flux-cored wire used for low carbon steel and Grade 490MPa high strength steel
Purpose:
Suitable for welding in fields such as shop body, bridge, construction steel structure, manufacture of Machinery and vehicle, etc.
Main Characteristics:
*Good all-position welding, less fume, convenient and safe operation
*Good welding process, stable and mild arc with less splashing, even slag and good removability of slag
*Good anti-porosity of primer, smooth and beautiful welding, stable and reliable welding quality
*Clean and smooth wire, continuous and reliable feeding, fast welding, high efficiency and low cost
Equivalent Standard:
AWS A5.20/ASME SFA5.20 E71T-1 JIS Z3313 YFW-C50DR
Protection Gas:
100%CO2
Chemical Content of Fusing Metal(%)
C
Si
Mn
P
S
≤0.1
0.2~0.7
0.9~1.60
≤0.025
≤0.025
Yield strength N/mm 2
Tensile strength N/mm 2
Elongation Rate (%)
Test Temperature ºC
CVN- Shock Value
≥390
≥490
≥22
0
60
Available Sizes and Recommended Current (DC negative polarity connection)
Diameter(mm)
φ1.2
φ1.4
φ1.6
Welding current
(A)
Horizontal welding, horizontal fillet welding
120~300
200~400
200~450
Vertical upward welding, overhead position of welding
120~260
180~280
180~280
Vertical downward welding
200~300
220~320
250~300
competetive price, good quality and effective lead time
Rutile flux-cored wire used for low carbon steel and Grade 490MPa high strength steel
Purpose:
Suitable for welding in fields such as shop body, bridge, construction steel structure, manufacture of Machinery and vehicle, etc.
Main Characteristics:
*Good all-position welding, less fume, convenient and safe operation
*Good welding process, stable and mild arc with less splashing, even slag and good removability of slag
*Good anti-porosity of primer, smooth and beautiful welding, stable and reliable welding quality
*Clean and smooth wire, continuous and reliable feeding, fast welding, high efficiency and low cost
Equivalent Standard:
AWS A5.20/ASME SFA5.20 E71T-1 JIS Z3313 YFW-C50DR
Protection Gas:
100%CO2
Chemical Content of Fusing Metal(%)
C
Si
Mn
P
S
≤0.1
0.2~0.7
0.9~1.60
≤0.025
≤0.025
Yield strength N/mm 2
Tensile strength N/mm 2
Elongation Rate (%)
Test Temperature ºC
CVN- Shock Value
≥390
≥490
≥22
0
60
Available Sizes and Recommended Current (DC negative polarity connection)
Diameter(mm)
φ1.2
φ1.4
φ1.6
Welding current
(A)
Horizontal welding, horizontal fillet welding
120~300
200~400
200~450
Vertical upward welding, overhead position of welding
120~260
180~280
180~280
Vertical downward welding
200~300
220~320
250~300
Clean solder wire
High performance clean solder wire
(1)Good wettability and weldability in clean solder wire;
(2)Low residue;
(3)Not splash.
Introduction of clean solder wire
(1)
Clean solder wire can be applied in radio, communication, meters, instruments, copper, tin and irons and etc;
(2) Smooth surface, good fluidness melt;
(3) Good mechanical performance;
(4) Bright solder point.
Datasheet of clean solder wire
Components
Soldering tin alloy
Melting point °C
Solder bar
Solder wire
SnPb
Sn63Pb37
183
√
√
Sn60Pb40
183-190
√
√
Sn55Pb45
183-205
√
√
Sn50Pb50
183-216
√
√
Sn45Pb55
183-227
√
√
Sn40Pb60
183-238
√
√
Sn35Pb65
183-245
√
√
Sn30Pb70
183-255
√
√
Sn25Pb75
183-266
√
√
Sn20Pb80
183-275
√
√
Sn15Pb85
183-288
√
√
(1)Good wettability and weldability in clean solder wire;
(2)Low residue;
(3)Not splash.
Introduction of clean solder wire
(1)
Clean solder wire can be applied in radio, communication, meters, instruments, copper, tin and irons and etc;
(2) Smooth surface, good fluidness melt;
(3) Good mechanical performance;
(4) Bright solder point.
Datasheet of clean solder wire
Components
Soldering tin alloy
Melting point °C
Solder bar
Solder wire
SnPb
Sn63Pb37
183
√
√
Sn60Pb40
183-190
√
√
Sn55Pb45
183-205
√
√
Sn50Pb50
183-216
√
√
Sn45Pb55
183-227
√
√
Sn40Pb60
183-238
√
√
Sn35Pb65
183-245
√
√
Sn30Pb70
183-255
√
√
Sn25Pb75
183-266
√
√
Sn20Pb80
183-275
√
√
Sn15Pb85
183-288
√
√
Cmpetitive price co2 welding wire
co2 welding wire ER70s-6 has passed the cirtificate of ABS, CCS, GL, LR, SGS, DNN
co2 welding wire
co2 welding wire ER70s-6 has passed the cirtificate of ABS, CCS, GL, LR, SGS, DNN;
our CO2 welding wire has excellent technological properties such as smooth steady feeding, fast melting rate, high depositing efficiency, little spatter and beautiful seam, which are suitable for all position welding work.
Flux cored wire is also our mian one and has passed the cirtificates.
co2 welding wire
co2 welding wire ER70s-6 has passed the cirtificate of ABS, CCS, GL, LR, SGS, DNN;
our CO2 welding wire has excellent technological properties such as smooth steady feeding, fast melting rate, high depositing efficiency, little spatter and beautiful seam, which are suitable for all position welding work.
Flux cored wire is also our mian one and has passed the cirtificates.
2# solder wire
2# solder wire
Even and bright welding spot, favorable diffusion performance, no corrosion, no pungent smell
2# solder wire
Product Specifications:
Our solder wires have advantages as follows: surface clean, no easy-broken core, rapid melting, bright soldering point, reliable soldering. The solid, single, triple and quintuple cored solder wire is widely used in industries.
Lead free solder wire/bar (Sn-Ag, Sn-Sb, Sn-Cu, Sn-Ag-Cu ):
Lead free solder paste (Sn-Ag, Sn-Sb, Sn-Cu, Sn-Ag-Cu ):
Type of flux
Water-soluble solder wire
No-clean solder wire
Resin-core solder wire
Way of soldering
wave-soldering
dip soldering
Packaging
a) Wire dimensions: Diameters from 0.5 mm to 5 mm
b) Supplied on spools: 250g, 500g, and 1kg
c) Packed in cartons of 60 x 250 g, 40 x 500g, 20 x 1kg
d) Boxes and spools carry product information labels
e) Quality assurance: Certificates of Conformity can be issued for each shipment batch if requested at the time of ordering
Even and bright welding spot, favorable diffusion performance, no corrosion, no pungent smell
2# solder wire
Product Specifications:
Our solder wires have advantages as follows: surface clean, no easy-broken core, rapid melting, bright soldering point, reliable soldering. The solid, single, triple and quintuple cored solder wire is widely used in industries.
Lead free solder wire/bar (Sn-Ag, Sn-Sb, Sn-Cu, Sn-Ag-Cu ):
Lead free solder paste (Sn-Ag, Sn-Sb, Sn-Cu, Sn-Ag-Cu ):
Type of flux
Water-soluble solder wire
No-clean solder wire
Resin-core solder wire
Way of soldering
wave-soldering
dip soldering
Packaging
a) Wire dimensions: Diameters from 0.5 mm to 5 mm
b) Supplied on spools: 250g, 500g, and 1kg
c) Packed in cartons of 60 x 250 g, 40 x 500g, 20 x 1kg
d) Boxes and spools carry product information labels
e) Quality assurance: Certificates of Conformity can be issued for each shipment batch if requested at the time of ordering
Co Welding Wire ER70S
WELDING WIRE ER70S
1) Sizes: 0.8-1.6mm
2) welding of carbon steel and low alloy steel
3) high quality & lower price
WELDING WIRE ER70S-3 / ER70S- 6
1) MIG/MAG wire: ER70S-6, ER70S-7, ER80S-G, ER80S-D2
2) Submerged arc welding wire EL8, EL12, EM12, EH14, EA2
3) Size:0.8mm,1.0mm,1.2mm,1.6mm
4) Diameter (mm) 0.8/0.9/1.0/1.2/1.6MM
5) Packing: 5kg/spool 12.5kg/spool 18kg/spool 20kg/spool
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
• Any Application Where a "Finished" Weld Appearance is Desirable4
1) Sizes: 0.8-1.6mm
2) welding of carbon steel and low alloy steel
3) high quality & lower price
WELDING WIRE ER70S-3 / ER70S- 6
1) MIG/MAG wire: ER70S-6, ER70S-7, ER80S-G, ER80S-D2
2) Submerged arc welding wire EL8, EL12, EM12, EH14, EA2
3) Size:0.8mm,1.0mm,1.2mm,1.6mm
4) Diameter (mm) 0.8/0.9/1.0/1.2/1.6MM
5) Packing: 5kg/spool 12.5kg/spool 18kg/spool 20kg/spool
TYPICAL APPLICATION
• Construction Equipment
• Agricultural Equipment
• Automotive
• Ornamental Iron
• Sheetmetal Containers
• Ductwork
• Tubular Framework
• Light to Heavy Structural Steel Fabrication
• Any Application Where a "Finished" Weld Appearance is Desirable4
Co2 Gas Shileded Welding Wire
CO2 Gas Shileded Welding Wire
1. Diameter : 0.8,mm 1.0mm,1.2mm, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
1. Diameter : 0.8,mm 1.0mm,1.2mm, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
Co2 Welding Wire
CO2 Welding Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
We have some other products, if you need any of them, pls feel free to contact us !
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
We have some other products, if you need any of them, pls feel free to contact us !
Co2 Welding Wire
CO2 Welding Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
We have some other products, if you need any of them, pls feel free to contact us !
Thanks&best regards,
Tina
Tel: 86-312-5922853
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
We have some other products, if you need any of them, pls feel free to contact us !
Thanks&best regards,
Tina
Tel: 86-312-5922853
Co2 Welding Wire
CO2 Welding Wire
1. Diameter : 0.8, 1.0,1.2, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
1. Diameter : 0.8, 1.0,1.2, 1.6 mm.
2. AWS ER70s-6.
3. Small splash and smog.
CO2 Welding
Wire
1. Diameter : 0.8mm, 1.0mm,1.2mm, 1.6 mm.
2. AWS ER 70s-6.
3. Small splash and smog.
The content is as follows:
C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030
Mechanical properties of deposited metal:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)
370-375
535-545
27.5-28.5
Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.
Co2 Carbon Welding Wire
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Co2 Copper Coated Welding Wire (ER70S-6)/welding wire
WELDING WIRE/co2 copper coated welding wire ER70S-6
CO2 gas shielded welding wire/ER50-6/ER70s-6
IEI SGS BV CIQ COC SANCOP
WELDING WIRE Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
CO2 gas shielded welding wire/ER50-6/ER70s-6
IEI SGS BV CIQ COC SANCOP
WELDING WIRE Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Co2 Copper Coated Welding Wire (ER70S-6)
co2 copper coated welding wire ER70S-6
welding wire/gas shielded welding wire/
CO2 gas shielded welding wire/ER50-6/ER70s-6
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
welding wire/gas shielded welding wire/
CO2 gas shielded welding wire/ER50-6/ER70s-6
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Co2 Copper Coated Welding Wire (ER70S-6)
co2 copper coated welding wire
CO2 gas shielded welding wire/ER50-6/ER70s-6
0.8-2.0mm CE IEI SGS BV COC SONCAP AWS
Co2 Copper Coated Welding Wire (ER70S-6)
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
CO2 gas shielded welding wire/ER50-6/ER70s-6
0.8-2.0mm CE IEI SGS BV COC SONCAP AWS
Co2 Copper Coated Welding Wire (ER70S-6)
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
2% Flux solder wire
Solder Materials
Low lead impurity, Good fluidity, Low generation of solder dross, High mechanical streng
Solder Materials
It accords with RA Grade standard of GB/T3131-2001 Standard; it is widely used in capacitor manufacturing, directly realizing soft soldering connection on the galvanized coating and gold alloy coating on the head face of capacitor, and suitable for braze welding of metal base which is hard to weld, such as nickel plating part, galvanized part, Dumet wire, and copper, etc; and it is of high soldering speed, brightness, nice appearance, and reliable joint quality, etc.
Low lead impurity
Good fluidity
Low generation of solder dross
High mechanical strength
Low aggressive to solder pot material
Alloy
metaling range
Sn63/Pb37
183C
Sn60/Pb40
183-190C
Sn55/Pb45
183-203C
Sn50/Pb50
183-216C
Sn45/Pb55
183-227C
Sn40/Pb60
183-238C
Sn35/Pb65
183-247C
Sn30/Pb70
183-255C
Sn25/Pb75
183-266C
Sn20/Pb80
183-280C
Standard Wire Diameters
x
Diameter (inch)
0.125
0.092
0.062
0.050
0.040
0.031
0.025
0.020
Diameter (mm)
3.18
2.33
1.57
1.27
1.01
0.80
0.63
0.50
Standard Wire Gauge
11
13
16
18
19
21
23
25
Low lead impurity, Good fluidity, Low generation of solder dross, High mechanical streng
Solder Materials
It accords with RA Grade standard of GB/T3131-2001 Standard; it is widely used in capacitor manufacturing, directly realizing soft soldering connection on the galvanized coating and gold alloy coating on the head face of capacitor, and suitable for braze welding of metal base which is hard to weld, such as nickel plating part, galvanized part, Dumet wire, and copper, etc; and it is of high soldering speed, brightness, nice appearance, and reliable joint quality, etc.
Low lead impurity
Good fluidity
Low generation of solder dross
High mechanical strength
Low aggressive to solder pot material
Alloy
metaling range
Sn63/Pb37
183C
Sn60/Pb40
183-190C
Sn55/Pb45
183-203C
Sn50/Pb50
183-216C
Sn45/Pb55
183-227C
Sn40/Pb60
183-238C
Sn35/Pb65
183-247C
Sn30/Pb70
183-255C
Sn25/Pb75
183-266C
Sn20/Pb80
183-280C
Standard Wire Diameters
x
Diameter (inch)
0.125
0.092
0.062
0.050
0.040
0.031
0.025
0.020
Diameter (mm)
3.18
2.33
1.57
1.27
1.01
0.80
0.63
0.50
Standard Wire Gauge
11
13
16
18
19
21
23
25
Co2 Copper Coated Welding Wire (ER70S-6)
co2 copper coated welding wire ER70S-6
carbon steel welding wire
CO2 gas shielded welding wire/ER50-6/ER70s-6
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
carbon steel welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
carbon steel welding wire
CO2 gas shielded welding wire/ER50-6/ER70s-6
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
carbon steel welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Co2 Copper Coated Welding Wire (ER70S-6)
co2 copper coated welding wire ER70S-6
solder welding wire/gas shielded welding wire
CO2 gas shielded welding wire
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
solder mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
solder welding wire/gas shielded welding wire
CO2 gas shielded welding wire
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire
solder mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Co2 Copper Coated Welding Wire (ER70S-6)
co2 copper coated welding wire ER70S-6
CO2 gas shielded welding wire/ER50-6/ER70s-6
mig welding wire ER70S-6
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire er70s-6
mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
CO2 gas shielded welding wire/ER50-6/ER70s-6
mig welding wire ER70S-6
Co2 Copper Coated Welding Wire (ER70S-6)
co2 gas shielded welding wire er70s-6
mig /mag welding wire
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Co2 Copper Coated Welding Wire CE certificate
co2 copper coated welding wire
CO2 gas shielded welding wire/ER50-6/ER70s-6
0.8-2.0mm CE IEI SGS BV COC SONCAP AWS
Co2 Copper Coated Welding Wire (ER70S-6)
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
CO2 gas shielded welding wire/ER50-6/ER70s-6
0.8-2.0mm CE IEI SGS BV COC SONCAP AWS
Co2 Copper Coated Welding Wire (ER70S-6)
Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.
Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
----
≤0.50
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc
Co2 Copper Plated Solid Welding wire
Solid welding wire
1. Diameter:0.8mm-1.6mm;
2. vacuum packing;
3. Model :ER70S-6/ER49-1
4. Drum packing also available
Solid welding wire
This welding wire can be supplied on spools ranging in weight from 5 to 100 kg. These spools can be supplied both flex free and reeled in layers. The welding wire is perfectly protected with clingfilm in solid carton boxes, and can be supplied on plastic spools or on metal basket spools.
Standard pallet packaging: 72 boxes;
Solid copper plated welding wire in drums;
For large consumers, we supplies welding wire in drums of 200 to 380 kg. The drums are provided with an innovative unwinding system guaranteeing faultless wire feeding to unwinding cone and wire feeding cable. Standard pallet packaging: 2 or 4 drums.
This welding wire has been reeled in a hard cardboard drum in such a way that the welding wire always leaves the drum straightforward. The pre-aligned welding wire means saving time to change (1 drum = 15 spools), and has the further advantage of:
a) the wire motor is less charged;
b) there is less friction in the spiral;
c) there is less wear and tear of the conductors;
Learn more, pls contact us freely .
1. Diameter:0.8mm-1.6mm;
2. vacuum packing;
3. Model :ER70S-6/ER49-1
4. Drum packing also available
Solid welding wire
This welding wire can be supplied on spools ranging in weight from 5 to 100 kg. These spools can be supplied both flex free and reeled in layers. The welding wire is perfectly protected with clingfilm in solid carton boxes, and can be supplied on plastic spools or on metal basket spools.
Standard pallet packaging: 72 boxes;
Solid copper plated welding wire in drums;
For large consumers, we supplies welding wire in drums of 200 to 380 kg. The drums are provided with an innovative unwinding system guaranteeing faultless wire feeding to unwinding cone and wire feeding cable. Standard pallet packaging: 2 or 4 drums.
This welding wire has been reeled in a hard cardboard drum in such a way that the welding wire always leaves the drum straightforward. The pre-aligned welding wire means saving time to change (1 drum = 15 spools), and has the further advantage of:
a) the wire motor is less charged;
b) there is less friction in the spiral;
c) there is less wear and tear of the conductors;
Learn more, pls contact us freely .
Co2 Gas Shielded Mig Welding Wire
1welding wire model No.:ER70s-6
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
AWS ER70S-6
co2 welding wire/gas shield welding wire Useing the advanced Electroplating copper coated technology
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material
:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features
: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg packed in plastic spool.
Certificate
: ISO 9001:2000
ADVANTAGE
:
1.low welding cost
2.high productivity and low electricity consumption.
3.easy to operate.all-position welding
4.ery low hydrogen content in the weld and lower nitrogen content.excellent crack-resistance.
little deformation after welding.
wide applicability,suitable for welding thin medium and thick plates.
Co2 welding wire mainly specification:welding wire is recommended for a wide variety of postional MIG welding wire for mild and alloy steels.It is typically usded in general fabrication,maintenance bridge and structral application.co2 mig welding wire provide low spatter and excellent performance with consistent copper coating ensuring smooth feeding.
Packing to be made in 5kg/12.5kg/15kg/20kg spool,on pallets then put into 20feet container .we can also make the packing according to buyer request.
Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
AWS ER70S-6
co2 welding wire/gas shield welding wire Useing the advanced Electroplating copper coated technology
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
WELDING WIRE, Mig welding wire,co2 welding wire
Detailed Product Description
Material
:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features
: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg packed in plastic spool.
Certificate
: ISO 9001:2000
ADVANTAGE
:
1.low welding cost
2.high productivity and low electricity consumption.
3.easy to operate.all-position welding
4.ery low hydrogen content in the weld and lower nitrogen content.excellent crack-resistance.
little deformation after welding.
wide applicability,suitable for welding thin medium and thick plates.
Co2 welding wire mainly specification:welding wire is recommended for a wide variety of postional MIG welding wire for mild and alloy steels.It is typically usded in general fabrication,maintenance bridge and structral application.co2 mig welding wire provide low spatter and excellent performance with consistent copper coating ensuring smooth feeding.
Packing to be made in 5kg/12.5kg/15kg/20kg spool,on pallets then put into 20feet container .we can also make the packing according to buyer request.
Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Thursday, August 18, 2011
Co2 Gas Shielded Mig Welding Wire
1welding wire model No.:ER70s-6
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
Description:
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
Description:
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
2% resin sored Flux solder wire
Solder Materials
Low lead impurity, Good fluidity, Low generation of solder dross, High mechanical streng
Solder Materials
It accords with RA Grade standard of GB/T3131-2001 Standard; it is widely used in capacitor manufacturing, directly realizing soft soldering connection on the galvanized coating and gold alloy coating on the head face of capacitor, and suitable for braze welding of metal base which is hard to weld, such as nickel plating part, galvanized part, Dumet wire, and copper, etc; and it is of high soldering speed, brightness, nice appearance, and reliable joint quality, etc.
Low lead impurity
Good fluidity
Low generation of solder dross
High mechanical strength
Low aggressive to solder pot material
Alloy
metaling range
Sn63/Pb37
183C
Sn60/Pb40
183-190C
Sn55/Pb45
183-203C
Sn50/Pb50
183-216C
Sn45/Pb55
183-227C
Sn40/Pb60
183-238C
Sn35/Pb65
183-247C
Sn30/Pb70
183-255C
Sn25/Pb75
183-266C
Sn20/Pb80
183-280C
Standard Wire Diameters
x
Diameter (inch)
0.125
0.092
0.062
0.050
0.040
0.031
0.025
0.020
Diameter (mm)
3.18
2.33
1.57
1.27
1.01
0.80
0.63
0.50
Standard Wire Gauge
11
13
16
18
19
21
23
25
Low lead impurity, Good fluidity, Low generation of solder dross, High mechanical streng
Solder Materials
It accords with RA Grade standard of GB/T3131-2001 Standard; it is widely used in capacitor manufacturing, directly realizing soft soldering connection on the galvanized coating and gold alloy coating on the head face of capacitor, and suitable for braze welding of metal base which is hard to weld, such as nickel plating part, galvanized part, Dumet wire, and copper, etc; and it is of high soldering speed, brightness, nice appearance, and reliable joint quality, etc.
Low lead impurity
Good fluidity
Low generation of solder dross
High mechanical strength
Low aggressive to solder pot material
Alloy
metaling range
Sn63/Pb37
183C
Sn60/Pb40
183-190C
Sn55/Pb45
183-203C
Sn50/Pb50
183-216C
Sn45/Pb55
183-227C
Sn40/Pb60
183-238C
Sn35/Pb65
183-247C
Sn30/Pb70
183-255C
Sn25/Pb75
183-266C
Sn20/Pb80
183-280C
Standard Wire Diameters
x
Diameter (inch)
0.125
0.092
0.062
0.050
0.040
0.031
0.025
0.020
Diameter (mm)
3.18
2.33
1.57
1.27
1.01
0.80
0.63
0.50
Standard Wire Gauge
11
13
16
18
19
21
23
25
Co2 Gas Shielded Welding Wire and welding electrode
1welding wire model No.:ER70s-6
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
Description:
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
Description:
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Co2 Gas Shielded Welding Wire
Co2 Gas Shielded Welding Wire
Gauges: 0.8mm-2.0mm
Spool: 200mm, 270mm, 300mm
Co2 Gas Shielded Welding Wire
Gauges: 0.8mm-2.0mm
Spool: 200mm, 270mm, 300mm
Net weight: 1KG, 5KG, 10KG, 20KG 250kg 300kg 350kg
5kg, 10kg, 15kg or 20kg packed in plastic disk or wire dis
Packing:
Precision layer wire on the black plastic spool, covered with the wax paper, each
Spool in ploybag with two big silicon in the carton, then put on wooden pallets
It is common used to weld the situation in the construction thing such as: Shipbuilding, vehicle, bridge building, tube piece etc. Of to connect and fill the cape
Gauges: 0.8mm-2.0mm
Spool: 200mm, 270mm, 300mm
Co2 Gas Shielded Welding Wire
Gauges: 0.8mm-2.0mm
Spool: 200mm, 270mm, 300mm
Net weight: 1KG, 5KG, 10KG, 20KG 250kg 300kg 350kg
5kg, 10kg, 15kg or 20kg packed in plastic disk or wire dis
Packing:
Precision layer wire on the black plastic spool, covered with the wax paper, each
Spool in ploybag with two big silicon in the carton, then put on wooden pallets
It is common used to weld the situation in the construction thing such as: Shipbuilding, vehicle, bridge building, tube piece etc. Of to connect and fill the cape
Co2 Gas Shielded welding wire
Small splash, produce gas less, welding, smooth, take off pierced the second easy arc starting, welding and firm
Description
weiding wire AWS ER70S-6
ER70S-6 is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with
GB/T 8110 ER50-6 ISO 636-A-W 42 3 W3Sil
AWS A5.18 ER70S-6 ISO 636-B-W 49A 3 W6
BS EN 1668-W 42 3 W3Sil JIS Z3316 YGT50
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV (J)
420
500
22
27(-30
°C
)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Description
weiding wire AWS ER70S-6
ER70S-6 is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with
GB/T 8110 ER50-6 ISO 636-A-W 42 3 W3Sil
AWS A5.18 ER70S-6 ISO 636-B-W 49A 3 W6
BS EN 1668-W 42 3 W3Sil JIS Z3316 YGT50
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV (J)
420
500
22
27(-30
°C
)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Co2 Gas Shielded welding wire
7-15 days delivery time, 8 years Manufacturer in China.hope to do business with you...
Co2 Gas Shielded welding wire
we can offer you good quality welding wires with GL,BV,LR certificate.
Chemical composition of the wire(%):
C≤0.06-0.15 Mn≤1.40-1.85 Si≤0.8-1.15 S≤0.035 P≤0.025 Cu≤0.50
Mechanical properties of the deposited metal(%):
σ
b ≥
500MPa σ
s
≥420MPa δ
5
≥ 22 A
KV
(J) -29 'C
≥27
Reference Current
diameter: 0.8mm 1.0mm 1.2mm 1.6mm
current(A): 40-140 50--220 80--350 120--450
NOTICE: 1. Wire must be stocked in dry circumstances.Don’t open the dampproof package of spools to avoid rust.
2.Before welding, rust , water and impurities are to be removed from the welded surfaces of wordplaces.
Besides,we can supply many other kinds of screws,such as Chipboard Screw / Self-Drilling Screw / Self-Tapping Screw and so on,please don't hesitate to contact me,and I will supply you more reasonable price better quality and better service.
Co2 Gas Shielded welding wire
we can offer you good quality welding wires with GL,BV,LR certificate.
Chemical composition of the wire(%):
C≤0.06-0.15 Mn≤1.40-1.85 Si≤0.8-1.15 S≤0.035 P≤0.025 Cu≤0.50
Mechanical properties of the deposited metal(%):
σ
b ≥
500MPa σ
s
≥420MPa δ
5
≥ 22 A
KV
(J) -29 'C
≥27
Reference Current
diameter: 0.8mm 1.0mm 1.2mm 1.6mm
current(A): 40-140 50--220 80--350 120--450
NOTICE: 1. Wire must be stocked in dry circumstances.Don’t open the dampproof package of spools to avoid rust.
2.Before welding, rust , water and impurities are to be removed from the welded surfaces of wordplaces.
Besides,we can supply many other kinds of screws,such as Chipboard Screw / Self-Drilling Screw / Self-Tapping Screw and so on,please don't hesitate to contact me,and I will supply you more reasonable price better quality and better service.
Co2 Gas Shielded welding wire
We are specialize in fastener have more than 10 years experience in this field.
We' re of your service at any time.
Co2 Gas Shielded welding wire
we can offer you good quality welding wires with GL,BV,LR certificate.
Chemical composition of the wire(%):
C≤0.06-0.15 Mn≤1.40-1.85 Si≤0.8-1.15 S≤0.035 P≤0.025 Cu≤0.50
Mechanical properties of the deposited metal(%):
σ
b ≥
500MPa σ
s
≥420MPa δ
5
≥ 22 A
KV
(J) -29 'C
≥27
Reference Current
diameter: 0.8mm 1.0mm 1.2mm 1.6mm
current(A): 40-140 50--220 80--350 120--450
.
Besides,we can supply many other kinds of screws,such as Chipboard Screw / Self-Drilling Screw / Self-Tapping Screw and so on,please don't hesitate to contact me,and I will supply you more reasonable price better quality and better service.
We' re of your service at any time.
Co2 Gas Shielded welding wire
we can offer you good quality welding wires with GL,BV,LR certificate.
Chemical composition of the wire(%):
C≤0.06-0.15 Mn≤1.40-1.85 Si≤0.8-1.15 S≤0.035 P≤0.025 Cu≤0.50
Mechanical properties of the deposited metal(%):
σ
b ≥
500MPa σ
s
≥420MPa δ
5
≥ 22 A
KV
(J) -29 'C
≥27
Reference Current
diameter: 0.8mm 1.0mm 1.2mm 1.6mm
current(A): 40-140 50--220 80--350 120--450
.
Besides,we can supply many other kinds of screws,such as Chipboard Screw / Self-Drilling Screw / Self-Tapping Screw and so on,please don't hesitate to contact me,and I will supply you more reasonable price better quality and better service.
Subscribe to:
Posts (Atom)