Saturday, June 18, 2011

HIgh Mn Autensite F.C.W

HIgh Mn Autensite Welding Wire:
1.excellent mechanical properties
2.own strong research team
3.professional technical support
HIgh Mn Autensite Welding Wire

DY-YD58(M) is good surfacing material for resisting impact and abrasive wear.

APPLICATION

Mainly used for surfacing of rail switch , Scoop , breaker roll , dipper blade , jaw plate , and repairing for Mn13CASTINGS . The shielding gas is pure CO2 or Ar+CO2.

Typical Chemical Composition of Deposition Metal (%)

C
Mn
Si
Cr
Ni
S
P
Fe
0.9
14
0.48
3.2
3.0
0.008
0.015
the
remainded




Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
210HB
As welded
48HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
250-400
Voltage Range (V)
28-34



shielding gas is pure co2 or co2+Ar.

HJ 49-1 welding wire

HJ50-6 has the characteristics of excellent technicalperformance, fast melting speed, high efficient fusion.
Brand/Model
HJ50-6 /ER50-6/ER70S-6
Standards
Confirm to GB/T 8110-2008 ,Correspond to AWS A5.18 /JIS Z3316
Chemical components of welding wire

C
Mn
Si
S
P
Cu
Cr
Ni
Mo
Other
0.06-0.15
1.40-1.85
0.80-1.15


0.035

0.025

0.050
_
_
_

0.50
Mechanical properties of deposited metal
σ0.2
(MPa)
σb
(MPa)
δ5
(%)
AKV
(J)
≥420
≥500
≥22
≥27-29
Characteristics
Applicable for welding of low carbon steel and low alloy steel.Mainly used for all position welding of 50kg steel plate. Good low temperature flexibility.
Specification
φ0.6mm,φ0.8mm,φ0.9mm,φ1.0mm,φ1.2mm
Package
0.9kg,4.5kg,5kg,15kg,20kg,27kg plastic spool layer wind.
Or as per customers requirements


HOT SELL --MIG WELDING WIRE 1070 1100 4043 5356

HOT SELL --MIG WELDING WIRE 1070 1100 4043 5356
1.Spatter small
2. better color matching after anodizing.
3.low noise
HOT SELL --MIG WELDING WIRE 1070 1100 4043 5356

Aluminum magnesium alloy welding wire is designed for 5XXX series alloy when 40Ksi (276Mpa) tensile strength is not required .It has a better color matching after anodizing.
Specifications:ER5356
1) Si:0.5%
2) Cu: 0.1%
3) Mn: 0.05-0.20%
5) Mg: 4.5-5.5%
6) Zn: 0.1%
7) Al: balance

HOT SELL ER49-1/ER70S-6 welding wire (SG2)

HOT SELL ER49-1/ER70S-6 welding wire SG2
1.model:AWS ER70S-6
2.size 0.6-2.0mm
3.IEI SGS BV ISO CIQ certificate




HOT SELL ER49-1/ER70S-6 welding wire ER70S-6 SG2
2Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: ISO IEI SGS BV CIQ


Supplier:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand and Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice

HOT SELL ER49-1/ER70S-6 welding wire ER70S-6 SG2
MAG welding wire
ER70s-6 CO2 welding wire
CO2 GAS SHIELDED welding wire 5KG

CO2 SG2 WELDING WIRE SAW ER70S-6
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50

HOT SELL ER49-1/ER70S-6 welding wire (SG2)

HOT SELL ER49-1/ER70S-6 welding wire SG2
1.model:AWS ER70S-6
2.size 0.6-2.0mm
3.IEI SGS BV ISO CIQ certificate




HOT SELL ER49-1/ER70S-6 welding wire ER70S-6 SG2
2Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: ISO IEI SGS BV CIQ


Supplier:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand and Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice

HOT SELL ER49-1/ER70S-6 welding wire ER70S-6 SG2
SG2 welding wire
ER70s-6 CO2 welding wire
MIG welding wire

CO2 SG2 WELDING WIRE SAW ER70S-6
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50

HOT Sale for co2/mig Welding Wire AWS ER70S-6 15kg/spool

mig/co2 gas welding wire
complete specifications
high quality,reasonable price.
Free sample
Certificate: ISO,BV,IEI,SGS,COC
Mig/co2 gas Welding wire AWS ER70s-6:
Supply good quality, reasonable price co2 welding wire

Features Specifications: WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material: excellent ER70S-6 steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.


CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
Tensile Num KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20


Dia:0.8,1.0,1.2,1.6mm
Packing term:5kg,10kg,20kg/spool
Certificate: ISO,IEI,BV,SGS,VOC,COC

HQ welding wire ER70S-6 /SG2 welding wire ( BV )

HQ welding wire gas shield welding wire
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire BV APPROVEL
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

HQ welding wire ER70S-6 /SG2 welding wire ( BV )

HQ welding wire gas shield welding wire
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire BVDIN SG2
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

AC&DC welder

Convenient stepless adjustment of welder current.
Suitable for welding low carbon steel,medium carbon steel,low alloy

HQ welding wire ER70S-6 /SG2 welding wire ( BV APPROVEL)

HQ welding wire gas shield welding wire
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire BV APPROVEL
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

HQ welding wire ER70S-6 /gas shielded welding wire (CE certificate)

HQ welding wire gas shield welding wire
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire SAW WELD
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

HQ welding wire ER70S-6 AWS A5.18 /SG2 welding wire ( BV )

HQ welding wire AWS A5.18 ER70S-6/SG2
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire BV A 5.18 DIN SG2
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

HQ welding wire ER70S-6 AWS A5.18 /SG2 welding wire ( BV )

HQ welding wire AWS A5.18 ER70S-6/SG2
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire BV A5.18 DIN SG2
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

HQ welding wire ER70S-6 AWS A5.18 /SG2 welding wire ( BV )

HQ welding wire AWS A5.18 ER70S-6/SG2
1. Good quality
2. Competitive price
3. Professional knowledge
4. Fast delivery




HQ WELDING WIRE /SG2 gas shielded welding wire BVDIN SG2
Dia:0.8mm 0.9mm 1.0mm 1.6mm 2.0mm
Model Number: AWS ER70S-6 GB ER50-6/ DIN SG2 / BS A18/JIS Y GM12
certificate: BV COC SANCOP ISO CE certificate


Plant:Shijiazhuang Shiqiao Electric welding Material Co.,ltd
Brand :stone bridge brand /Hero Brand
Standard:AWS A5.18 ER70S-6
ATTN:Miss Alice Chai

CO2 WELDING WIRE/SG2 WELDING WIRE SAW DIN SG2
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50



Please contact with Miss ALice
SAMPLES we can supply freely
fast delivery

wait your contact

HS 83112000 carbon steel wire

carbon steel wire:our annul production is 5000t
1)good weldability
2)low residue
3)low splash
4)high reliability
carbon steel wire:

We offer the items of the welding wire by the brand of ER50-6,ER70s-6,E501T-1,E711T, H08A,H08MnA,which has the specification of 0.8~φ5.0mm for your choosing.In addition,we also supply welding rod of J501Fe18,J422,J502,J506,J507 and stainless steel electrode A102 and 431 welding flux.our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability. The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.
.


Trade Mank
Diameter
Lot No
Mfg Date
Executive Standard
Type
Date of lssue
ER 70S-6 (ER 50-6)
Φ1.2mm
X020892
2010-8-30
GB/T 8110-1995
ER 70S-6 (ER 50-6)
2010-8-30
Mechanical Properties of Deposited Metal
Chemical Compositions of the welding wire
Item
Specifieation
Actual Result
Element
Specification
Actual Result
Element
Specification
Actual Result
Tensile Strength
≥500
525
C
0.06-0.15
0.07
Cr
___
0.039
σb(Mpa)
Yield Strength
≥420
435
Mn
1.40-1.85
1.56
Ni
___
0.015
60.2(Mpa)
Elongation
≥22
28
Si
0.80-1.15
0.9
Cu
≤0.50
0.018
δ5(%)
V Impact Tem
-29
-29
S
≤0.035
0.012



(°C)
Impact Yalue
≥27
94 95 73
P
≤0.025
0.01



Impact Yalue

Hard Drawn Bare Annealed Copper Wires

1.Hard Drawn Bare Annealed Copper Wires
2. Size: 0.8mm/1.0mm/1.2mm/1.6mm..
3.Certificate:ABS,SGS,EWC,AOV,LR,TUV,DB,GL

1. Hard Drawn Bare Annealed Copper Wires
Size: 0.8mm/1.0mm/1.2mm/1.6mm..
Certificate:ABS,SGS,EWC,AOV,LR,TUV,DB,GL


2.WELDING WIRE AWS 5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,

Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4. 0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5. 15kg, 20kg iron spool layer wind
6. 100kg, 250kg, 350kg drum packing



Hardfacing Flux-cored Wires

Applied to repair surface of high impact wear parts, such as shiled machine, excavator bucket and hopper of mining machinery pro
Typical Chemical Composition of Deposited Metal
C
Si
Mn
Cr
Mo
other
0.45
0.96

6.6
0.62

Hardness(HRC)
Welded hardness
Impact hardness
≥55
≥58


Heat Stable Clear Residue Solder Wire ( 60%40%)

Heat Stable Clear Residue Solder Wire ( 60%40%)
JILIHONG wire solders are available in a variety of alloy
*
Product name: Tin Lead Solder Wire
*
Iterm No. Sn60-Pb30
*Alloy Compositions

Alloy compositions(%)
Sn
Cu
Pb
Sb
Bi
Ag
Zn
Fe
Al
As
Cd
63
0.002
max
The rest.
0.02
max.
0.02
max.
0.01
max
0.002
max.
0.002
max.
0.005
max.
0.03
max.
0.02
max.

*Alloy Properties

Melting Temperature
Solidus Temperature/Liquidus Temperature approx.183°C

Specific gravity
Approx. 7.4
20°C

*Properties of Flux

Item
Standard

Type
RMA

Content
2.2±0.6%

Dryness Test
Passed

AISI 308 stainless steel tiny wire

Stainless steel tiny wire
Series:304 308 308L 309 309L 316 316L 410 420 430etc
skylin metal products co,ltd.we are the professional manufactory loading in jiangsu of china produce the stainless steel tiny wire.
Material: :304 308 308L 309 309L 316 316L 410 420 430etc
Diameter:0.08MM-560MM
Surface:bright&matt
Tensile strength:1400-1750MP

Heat Stable Clear Residue Solder Wire

Heat Stable Clear Residue Solder Wire
KANGHUA wire solders are available in a variety of alloy
Heat Stable Clear Residue Solder Wire

Even and bright welding spot, favorable diffusion performance, no corrosion, no pungent smell, and no harm for integrate circuit or sensitive electronic elements; applied to frontier technologies in the fields of aviation, electronics, military industry, communication, and computer, etc.

KANGHUA’s wire solders are available in a variety of alloys, diameters, spool sizes, and solid or cored in a variety of chemistries.





The characteristics of flux
Products
R
RMA
Ra
Composition of Halogen
------
<0.1
0.1-0.5
Spreading
>75
>80
>80
Insulation Resistance
1*10(12)
>1*10(11)
>1*10(10)
Solubility Resistance
>1*10(15)
>=1*10(5)
>=5*10(4)


Excellent solderability properties
Fast soldering with low fuming and low odor
Low occurrences of spattering of flux and solder particles

Hero Submerged Arc Welding Wire EL-8(H08A) ISO

Hero Submerged arc welding wire EL-8 H08A
fire wire is made of H08A,thin coating with rutile.high efficiency ,small splash
Submerged-Arc Welding Wire
stone bridge welding

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.).
it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding
wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20

Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650



Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days


PLEASE CONTACT WITH ALICE

Hero Submerged Arc Welding Wire El-8(H08A)

Hero Submerged arc welding wire
fire wire is made of H08A,thin coating with rutile.high efficiency ,small splash good welding
Submerged-Arc Welding Wire
stone bridge welding

Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.).
it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding
wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20

Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650



Packing:plastic inside and weave bag outside
Weight:25kg/coil 50kg/coil 100kg/coil
Brand :stone bridge brand and hero brand
Price term:FOB CNF CIF
Loading port :Tianjin port
Validity :7days

Hero brand CO2 gas shielded welding wire(0.8,,0.9,1.0,1.2,1.6mm)

welding wire:ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam

Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

CO2 Welding Wire

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Hero brand CO2 gas shielded welding wireER70S-6,(15kg/spool)

welding wire:ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam

Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

CO2 Welding Wire

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Hero brand CO2/MIG welding wire ER70S-6(ISO)

Hero brand co2 /mig Welding wire:AWS ER70S-6 0.8mm-2.0mm
Submerged arc welding wire copper coat welding wire


STONE BRIDGE Hero BRAND CO2/MIG WELDING WIRE COPPER COATED WELDING WIRE GAS SHIELDED WELDING WIRE ER70S-6
Type GB International Standard
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
ER50-7 ER50-7 AWS ER70S-7


Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
HS CODE:83111000

Welding wire chemical
Composition(%)

Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50

Specification and reference
current

Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Hero brand Flux-cored welding wire AWS 5.20 E71T-1

welding wire:
-flux cored wire.
-High quality,good price
-certificate:ISO9001:2000
-stable arc,less smog,good welding seam
welding wire
-
Stone Bridge/Hero brand:

Flux cored welding wire AWS E71T-1 :
- flux cored wire.
-High quality,good price
-certificate:ISO9001:2000
-stable arc,less smog,good welding seam


Performance:
The wire for calcium oxide-type fluoride slag, CO
2
gas shielded flux cored wire. Its excellent performance welding process, DC DCRP, arc stability, a small spatter, slag from easy, weld forming good for the peace of welding, Wang 400km welding and welding. Molten metal excellent mechanical properties, diffusible hydrogen content is low, high impact toughness, cracking good.

diameter: 0.8mm,1.0mm,1.2mm,1.6mm
packing:5kg/spool,15kg/spool,20kg/spool
certificate:ISO9001:2000

Hero brand Flux-cored welding wire AWS 5.20 E71T-1

welding wire:
- flux cored wire.
-High quality,good price
-certificate:ISO9001:2000
-stable arc,less smog,good welding seam
welding wire
-
Stone Bridge/Hero brand:

Flux cored welding wire AWS E71T-1 :
- flux cored wire.
-High quality,good price
-certificate:ISO9001:2000
-stable arc,less smog,good welding seam


Performance:
The wire for calcium oxide-type fluoride slag, CO
2
gas shielded flux cored wire. Its excellent performance welding process, DC DCRP, arc stability, a small spatter, slag from easy, weld forming good for the peace of welding, Wang 400km welding and welding. Molten metal excellent mechanical properties, diffusible hydrogen content is low, high impact toughness, cracking good.

diameter: 0.8mm,1.0mm,1.2mm,1.6mm
packing:5kg/spool,15kg/spool,20kg/spool
certificate:ISO9001:2000

0.8 0.9-1.6 2.0mm co2 Welding wire DIN SG2 ER70S-6

0.8 0.9-1.6 2.0mm co2 Welding wire SG2 ER70S-6 Hero
1.Gas-shielded Solid Welding Wire
2.DIN SG2 AWS ER70S-6
0.8 0.9-1.6 2.0mm co2 Gas shield arc Welding wire SG2 ER70S-6-Hero
Features Specifications:
WELDING WIRE,mig welding wire,co2 welding wire
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000

CONTACT WITH Ms Alice

CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20






















Friday, June 17, 2011

AL. wire drawing machine

we can produce the complete line and build factory for aluminum wire production. Our Al. wire drawing machine is professional.
1. we can supply and build factory for Al. wire production/ aluminum wire production.
2.our Al. wire drawing machine is very professional.
3.produce them with high speed.

Hero brand SG2 co2/mig welding wire ER70S-6(ISO)

Hero brand co2 /mig Welding wire:AWS ER70S-6
Size:0.8mm-2.0mm
Package:12.5/15/20kg/spool
free samples can provide


HERO CO2/MIG WELDING WIRE COPPER COATED WELDING WIRE GAS SHIELDED WELDING WIRE ER70S-6

Brand name :stone bridge /Hero brand

Brand type:SQ ER70S-6
Material :ER70S-6
Ø
5.5MM
Products Specification:0.8mm-1.6mm
Classification:Recommended products
Products introduction:SQ ER70S-6
Standard :GB ER50S-6

Equal:AWS 5.18 ER70S-6
DIN SG2
BS A18
JIS YGM1
Type GB International Standard
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
ER50-7 ER50-7 AWS ER70S-7

Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
HS CODE:83113000


Welding wire chemical
Composition(%)

Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50

Hero brand co2/mig welding wire AWS ER70S-6 15KG/SPOOL

welding wire:ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam

Welding wire:
welding wire ER70S-6
Detailed Product Description
Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 5kg, 15kg or 20kg packed in plastic spool.
Certificate: ISO 9001:2000

Hero brand co2/mig welding wire AWS ER70S-6 15KG/SPOOL

welding wire:ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam

Welding wire:

AWS ER70S-6 is a copper carbon steel and low alloy steel welding wire, with the good hot metal mobility and the good resisting cracking quality. The components Mn and Si can stop stomas and slag, promote the resisting cracking quality and is helpful to get the good mechanical quality.
Application:Chemical composition of ER50-6 (AWS ER70S-6) :
C
Mn
Si
P
S
Cu
0.060.15
1.40---1.85
0.801.15
≤0.025
≤0.035
≤0.50
Mechanical properties of deposited metal
Type Name
GB
Equal
Tensile Strength (MPa)
Yield Strength (Mpa )
Elongation
(%)
Impact value
(J)
Tempature
ER 50-6
ER 50-6
AWS ER70S-6
≥500
≥420
≥22
≥27
-29
Diameter and reference current:
Diameter(mm)
Φ0.8
Φ1.0
Φ1.2
Φ1.6
Welding current(A)
40-140
50-220
80-350
170-550

Hero brand co2/mig welding wire AWS ER70S-6 15KG/SPOOL

welding wire AWS ER70S-6 used for welding low carbon alloy steel with excellent quality and good price.

Welding wire:

AWS ER70S-6 is a copper carbon steel and low alloy steel welding wire, with the good hot metal mobility and the good resisting cracking quality. The components Mn and Si can stop stomas and slag, promote the resisting cracking quality and is helpful to get the good mechanical quality.
Application:Chemical composition of ER50-6 (AWS ER70S-6) :
C
Mn
Si
P
S
Cu
0.060.15
1.40---1.85
0.801.15
≤0.025
≤0.035
≤0.50
Mechanical properties of deposited metal
Type Name
GB
Equal
Tensile Strength (MPa)
Yield Strength (Mpa )
Elongation
(%)
Impact value
(J)
Tempature
ER 50-6
ER 50-6
AWS ER70S-6
≥500
≥420
≥22
≥27
-29
Diameter and reference current:
Diameter(mm)
Φ0.8
Φ1.0
Φ1.2
Φ1.6
Welding current(A)
40-140
50-220
80-350
170-550

Hero brand co2/mig welding wire ER70S-6(ISO)

Hero brand co2 /mig Welding wire:AWS ER70S-6
Size:0.8mm-2.0mm
Package:5/12.5/15/20kg/spool
free samples can provide


HERO CO2/MIG WELDING WIRE COPPER COATED WELDING WIRE GAS SHIELDED WELDING WIRE ER70S-6
Type GB International Standard
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
ER50-7 ER50-7 AWS ER70S-7


Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
HS CODE:83113000

Welding wire chemical
Composition(%)

Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50

Specification and reference
current

Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Hero brand co2/mig welding wire ER70S-6(ISO)

Hero brand co2 /mig Welding wire:AWS ER70S-6
Size:0.8mm-2.0mm
Package:12.5/15/20kg/spool
free samples can provide


HERO CO2/MIG WELDING WIRE COPPER COATED WELDING WIRE GAS SHIELDED WELDING WIRE ER70S-6
Type GB International Standard
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
ER50-7 ER50-7 AWS ER70S-7


Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
HS CODE:83113000

Welding wire chemical
Composition(%)

Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50

Specification and reference
current

Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Hero brand co2/mig welding wire ER70S-6(ISO)

Hero brand co2 /mig Welding wire:AWS ER70S-6
Size:0.8mm-2.0mm
Package:12.5/15/20kg/spool
Certificate :ISO



HERO CO2/MIG WELDING WIRE COPPER COATED WELDING WIRE GAS SHIELDED WELDING WIRE ER70S-6

Hero brand co2 /mig Welding wire:AWS ER70S-6
Size:0.8mm-2.0mm
Package:12.5/15/20kg/spool
Tensile strength:(MPa):500-525
Type GB International Standard
H08Mn2SiA ER49-1
ER50-4 ER50-4 AWS ER70S-4
ER50-6 ER50-6 AWS ER70S-6 / JIS YGW12
ER50-7 ER50-7 AWS ER70S-7


Application
: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification
: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing
: 10kg, 15kg or 20kg per spool then packed in pallet
Certificate
:ISO 9001 :2000
MOQ
:one container
Transportantion
:by sea
Original
:Hebei China
HS CODE:83113000

Welding wire chemical
Composition(%)

Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50

Specification and reference
current

Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Hero brand submerged arc welding wire AWS EL-8,EM-12,EH-14

submerged arc welding wire:
specification :EL8,EM12,EH14
excellent quality, good price
ISO9001:2000
Free sample
submerged arc welding wire:
welding wire
Detailed Product Description

Features and application:
H08A and H08Eused for automatic submerged arc welding low carbon steel and some low-alloy steel stuctures (such as 16Mn),doing with high Mn type welding fiux
H08MnA for welding carbon steel and low-alloy steel structures of relevent strength grade along with flux
H10Mn2 used for automatic submerged arc welding carbon steel and low-alloy steel such as 16Mn, 14MnNb welding structures

Specification: 2.5mm,3.2mm,4.0mm,5.0mm

Packing : 25kg, 50kg packed in plastic spool.

Certificate: ISO 9001:2000

Hero brand submerged arc welding wire EL-8,Em-12,EH-14

welding wire for plain steel in carbon and low metal alloy steel constructions, used for many layers welding
welding wire
submerged arc welding wire:
Detailed Product Description
Features and application:
H08A and H08Eused for automatic submerged arc welding low carbon steel and some low-alloy steel stuctures (such as 16Mn),doing with high Mn type welding fiux
H08MnA for welding carbon steel and low-alloy steel structures of relevent strength grade along with flux
H10Mn2 used for automatic submerged arc welding carbon steel and low-alloy steel such as 16Mn, 14MnNb welding structures
Specification: 2.5mm,3.2mm,4.0mm,5.0mm
Packing : 25kg, 50kg per coil
Certificate: ISO 9001:2000

Hero brand submerged arc welding wire EL-8,Em-12,EH-14

welding wire:
good quality with reasonable price
certificate:ISO9001:2000
stable arc,less smog, good welding seam
welding wire
submerged arc welding wire:
Detailed Product Description
Features and application:
H08A and H08Eused for automatic submerged arc welding low carbon steel and some low-alloy steel stuctures (such as 16Mn),doing with high Mn type welding fiux
H08MnA for welding carbon steel and low-alloy steel structures of relevent strength grade along with flux
H10Mn2 used for automatic submerged arc welding carbon steel and low-alloy steel such as 16Mn, 14MnNb welding structures
Specification: 2.5mm,3.2mm,4.0mm,5.0mm
Packing : 25kg, 50kg per coil
Certificate: ISO 9001:2000

Hero hot sale Submerged-Arc Welding wire with Flux (CE certificate)

Hero hot sale Submerged-Arc Welding Wire with Flux
1.AWS EL-8 EM12 EH14
2.size :2.0-5.0mm
3.ISO BV IEI SGS
Hero hot sale Submerged-Arc Welding wire with Flux

stone bridge /hero brand EL-8 EM12(K) EH14

original:shijiazhuang city


Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----



Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650



Please contact with Ms ALice

Hero hot sale Submerged-Arc Welding wire with Flux

Hero hot sale Submerged-Arc Welding Wire with Flux
1.AWS EL-8 EM12 EH14
2.size :2.0-5.0mm
3.ISO BV IEI SGS
Hero hot sale Submerged-Arc Welding wire with Flux

stone bridge /hero brand

original:shijiazhuang city


Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----



Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650



Please contact with Ms ALice

High Cr Cast Iron welding wire

High Cr Cast Iron welding wire:
1qualified for classification societies
2approved by enterprise standard
3top quality product
High Cr Cast Iron welding wire:

It has excellent wear resistance and good resistance to corrosion and heat.

APPLICATION

It is suitable for surfacing of wear component, which are created by moderate impact and grinding abrasion.

Typical Chemical Composition of Deposition Metal (%)

C
Mn
Si
Cr

S

P



3.20
0.80
0.70
24.50
0.012
0.018








Typical Mechanical Properties of Deposited Metal



HRC
Remarks
50
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
Current Range(A)
350-450
Voltage Range (V)
30-45

High Cr Cast Iron welding wire

High Cr Cast Iron welding wire:
1qualified for classification societies
2approved by enterprise standard
3top quality product
High Cr Cast Iron welding wire:

It has excellent wear resistance and good resistance to corrosion and heat.

APPLICATION

It is suitable for surfacing of wear component, which are created by moderate impact and grinding abrasion. Such as hammers, breaker blades, screw feeders, metallurgical sintering screen, and others, with welding flux HJ107.

Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr

S

P

Fe

4.85
2.25
1.50
27.50
0.012
0.018

the remainded




Typical Mechanical Properties of Deposited Metal



HRC
Remarks
58
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
Current Range(A)
350-450
Voltage Range (V)
30-45

High Cr Cast Iron welding wire

High Cr Cast Iron welding wire:
1qualified for classification societies
2approved by enterprise standard
3top quality product
High Cr Cast Iron welding wire:

It has excellent wear resistance and good resistance to corrosion and heat.

APPLICATION

It is suitable for surfacing of wear component, which are created by moderate impact and grinding abrasion.
Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr

S

P



3.20
1.25
0.96
15.00
0.012
0.018






Typical Mechanical Properties of Deposited Metal



HRC
Remarks
50
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
Current Range(A)
350-450
Voltage Range (V)
30-45

High Cr Cast Iron welding wire

High Cr Cast Iron welding wire:
1qualified for classification societies
2approved by enterprise standard
3top quality product
High Cr Cast Iron welding wire:

It has excellent wear resistance and good resistance to corrosion and heat.

APPLICATION

It is suitable for surfacing of wear component, which are created by moderate impact and grinding abrasion.

Typical Chemical Composition of Deposition Metal (%)

C
Mn
Si
Cr
S

P
Mo
Nb
W
5.00
0.70
1.20
22.50
0.012
0.018
4.50
7.00
2.00





Typical Mechanical Properties of Deposited Metal



HRC
Remarks
50
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
Current Range(A)
350-450
Voltage Range (V)
30-45

High Cr Cast Iron welding wire

High Cr Cast Iron welding wire:
1qualified for classification societies
2approved by enterprise standard
3top quality product
High Cr Cast Iron welding wire:

It has excellent wear resistance and good resistance to corrosion and heat.

APPLICATION

It is suitable for surfacing of wear component, which are created by moderate impact and grinding abrasion. Such as hammers, breaker blades, screw feeders, metallurgical sintering screen, and others, with welding flux HJ107.

Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr
S
P
other
Fe

2.50
1.00
0.60
27.00
0.012
0.018
2.00
the remainded




Typical Mechanical Properties of Deposited Metal



HRC
Remarks
50
As welded

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
3.2
Current Range(A)
350-450
Voltage Range (V)
30-45

High Mn Autensite F.C.W

High Mn Autensite F.C.W:
1)Good impact and abrasion resistance
2)strong work hardening effect
3)Austenite the 1st layer

High Mn Autensite F.C.W

Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr



S
P
0.96
19.00
0.45
5.00



0.008
0.012



Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Mn Autensite F.C.W

High Mn Autensite F.C.W:
1)resistant to high temperature
2)the shielding gas is pure CO2
3)used with the contant hardness
High Mn Autensite F.C.W

DY-YD59(Q) is usd for reparing components that suffer heavy impact and abrasive wear, the sufacing layer has good plastic , toughness ,and crack resistance.

Application:
Mainly used for protecting surfacing and repairing of buckets , mid-temperature valves, and hot -forging dies.


Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr
Mo
V
Ni
S
P
0.60
16.4
0.65
16.7
1.52
0.45
2.56
0.013
0.016



Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Mn Autensite F.C.W

High Mn Autensite F.C.W:
1)resistant to high temperature
2)the shielding gas is pure CO2
3)used with the contant hardness
High Mn Autensite F.C.W

DY-YD57(Q) can be used with the hardness below 700 °C.

APPLICATION

Mainly used for surfacing parts that work in the conditions high temperature and heavy impact , such as guide plate of hot mill , hot forging die , valve , etc. The shielding gas is pure CO2 or Ar+CO2.

Typical Chemical Composition of Deposition Metal (%)

C
Mn
Si
Cr
Mo
V
Ni
S
P
0.60
16.4
0.65
16.7
1.52
0.45
2.56
0.013
0.016



Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Mn Autensite F.C.W

High Mn Autensite F.C.W:
1)resistant to high temperature
2)the shielding gas is pure CO2
3)used with the contant hardness
High Mn Autensite F.C.W

DY-YD56(Q) is used for surfacing wear components created by the friction between soil and sand or
bulletproof

material, with Carbon instead of Nitrogen, and improved cracking resistance.
The shielding gas is pure CO2 or Ar+CO2.

Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr

N

S
P
0.64
16.00
0.62
3.00

0.10

0.01
0.011



Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Mn Autensite F.C.W

High Mn Autensite F.C.W:
1)resistant to high temperature
2)the shielding gas is pure CO2
3)used with the contant hardness
High Mn Autensite F.C.W

DY-YD59(M) is usd for reparing components that suffer heavy impact and abrasive wear, the sufacing layer has good plastic , toughness ,and crack resistance.

Application:
Mainly used for protecting surfacing and repairing of buckets , mid-temperature valves, and hot -forging dies.


Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr
Mo
V
Ni
S
P
0.60
16.4
0.65
16.7
1.52
0.45
2.56
0.013
0.016



Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Mn Autensite F.C.W

High Mn Autensite F.C.W:
1)resistant to high temperature
2)the shielding gas is pure CO2
3)used with the contant hardness
High Mn Autensite F.C.W

DY-YD56(M) is used for surfacing wear components created by the friction between soil and sand or
bulletproof

material, with Carbon instead of Nitrogen, and improved cracking resistance.
The shielding gas is pure CO2 or Ar+CO2.

Typical Chemical Composition of Deposition Metal (%)


C
Mn
Si
Cr

N

S
P
0.64
16.00
0.62
3.00

0.10

0.01
0.011



Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Mn Autensite welding wire

High Mn Autensite welding wire:
1)surfacing layer with good tenacity and ductility for carbon and lowalloy

High Mn Autensite welding wire:
Shielding Gas: CO2

Typical Chemical Composition of Deposition Metal (%)



C
Mn
Si
Cr

S

P
Mo


0.10
14.70
0.36
10.00

0.009

0.01
0.8







Typical Mechanical Properties of Deposited Metal

Hardness
(welding 4 layers)
Remarks
250HB
As welded
40HRC
As working

Size and Recommended Current and Voltage Range
(DC:Wire(+))

Wire Dia.(mm)
1.6
Current Range(A)
200-350
Voltage Range (V)
28-34

High Quality Bar Solder (63/37)

High Quality Bar Solder (63/37)
1,material:lead,tin
2,high quality,high purity, glossy, beatiful
3,payment term:L/C, T/T
High Quality Bar Solder (63/37)
*Product name: Tin Lead Solder Wire
*Iterm No. Sn63-Pb37
*Alloy Compositions
Alloy compositions(%)
Sn
Cu
Pb
Sb
Bi
Ag
Zn
Fe
Al
As
Cd
63
0.002
max
The rest.
0.02
max.
0.02
max.
0.01
max
0.002
max.
0.002
max.
0.005
max.
0.03
max.
0.02
max.

*Alloy Properties
Melting Temperature
Solidus Temperature/Liquidus Temperature approx.183°C

Specific gravity
Approx. 7.4
20°C

*Properties of Flux
Item
Standard

Type
RMA

Content
2.2±0.6%

Dryness Test
Passed

*It depends on each diameter of solder wire and flux content.
This value is obtained from test result under condition of temperature at 40°C,
Humidity at 95%, voltage –applied at DC100v after 1000hrs.
*Size (Diameter): ø0.5mm~ ø2.3mm Net mass 1.0Kg/Plastic Reel
*Packaging: Each plastic reel has shrink-wrap packing.
Net 10Kg(10Reels) as 1 unit in a cardboard box.
*Storage condition: keep away from humidity and high temperature. Store within shelf life & doors at normal temperature.
Shelf life is not more than one(1) year after the manufactured date.
*Cautions: Before use, read and understand warning of Material Safety Data Sheet. The relevant regulations must be respected when handling and disposal. All statements, technical information and recommendations contained herein are based on test data or other information available to us, which we believe to be reliable, but the accuracy or completeness there of is not guaranteed.

ALAMBRE PARA SOLDADURA CO2 MIG

ALAMBRE PARA SOLDADURA
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO9001
ALAMBRE PARA SOLDADURA, welding

wire, ER70S-6, CO2 welding wire



Application

Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts

High Quality Brass wire

widely used
anneal and unanneal
high quality and best price
Brass wire:mainly including brass wire phosphor bronze wire and red copper wire
Material;brass wire , phosphor bronze wire ,red copper wire
Weaving pattern: Plain weave, twill weave

Diameter;0.025m-5m anneal and unanneal
Use:electrical wire and cable ,electrician and electric appliance ,machine and chemical ,metal weaving

Thursday, June 16, 2011

High Quality CO2 Gas Shielded Arc Welding Wire ER70S-6

CO2 Gas Shielded Arc Welding Wire ER70S-6:
a. Competitive Price
b. Good Weldability
c. Low Residue
d. High Reliability
High Quality CO2 Gas Shielded Arc Welding Wire ER70S-6:


The product has a good performance technology, melting fast, efficient cladding, the stability of arc welding spatter is extremely small, moist and good weld uniform appearance, and strong anti-oxidation corrosion, small gas sensitivity, easy to operate, suitable for automatic, semi-automatic all-position welding facilities.


The main application of carton steel, alloy steel and low-level 500Mpa high-strength low-alloy steel of all position welding, widely used in vehicles, buildings, bridges,shipbuildings,iron,steel and pressure vessel industry,can also be used in pipes and sheet The high-speed welding.
High Quality CO2 Gas Shielded Arc Welding Wire ER70S-6
Introduction:
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Low welding costs.High productivity and low electricity consumption.
2. Easy to operate. All-position welding.Little deformation after welding.
3.Suitable for welding thin, medium and thick plates.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30°C)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550
20~25



High Quality ER70S-6 Carbon Steel Welding Wire Copper

ER70S-6 Welding Wire Copper Coated:
a. Competitive Price
b. Good Weldability
c. Low Residue
d. High Reliability
High Quality ER70S-6 Carbon Steel Welding Wire Copper Coated:


The product has a good performance technology, melting fast, efficient cladding, the stability of arc welding spatter is extremely small, moist and good weld uniform appearance, and strong anti-oxidation corrosion, small gas sensitivity, easy to operate, suitable for automatic, semi-automatic all-position welding facilities.


The main application of carton steel, alloy steel and low-level 500Mpa high-strength low-alloy steel of all position welding, widely used in vehicles, buildings, bridges,shipbuildings,iron,steel and pressure vessel industry,can also be used in pipes and sheet The high-speed welding.
Er70S-6 welding wire
Introduction:
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Low welding costs.High productivity and low electricity consumption.
2. Easy to operate. All-position welding.Little deformation after welding.
3.Suitable for welding thin, medium and thick plates.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30°C)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550
20~25


High Quality ER70s-6 Welding Wire

ER70s-6 Welding Wire
1)melting fast,
2)efficient cladding
3)low splash
4)high reliability
ER70s-6 Welding Wire
MODEL:GB/T ER50-6 AWS ER70S-6 DIN SG2
Features Specifications:

use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures

Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
co2 gas shielded welding wire
Introduction
: Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Chemical Composition of Welding Wire(%)
C
Mn
Si
P
S
Cu
0.06-0.15
0.80-0.15
0.80-1.15
≤0.025
≤0.035
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
15/18
15/18
15/20
15/20
15/20






High Quality Er70s-6 Welding Wire Supplier

High Quality Er70s-6 Welding Wire Supplier:
(1) Good Weldability
(2) Low Residue
(3) Low Splash
(4) High Reliability
High Quality Er70s-6 Welding Wire Supplier:
We offer the items of the welding wire by the brand of ER50-6,ER70s-6,E501T-1,E711T, H08A,H08MnA,which has the specification of 0.8~φ5.0mm for your choosing.
In addition,we also supply welding rod of J501Fe18,J422,J502,J506,J507 and stainless steel electrode A102 and 431 welding flux.
Our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability.
The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.


Trade Mank
Diameter
Lot No
Mfg Date
Executive Standard
Type
Date of lssue
ER 70S-6 (ER 50-6)
Φ1.2mm
X020892
2010-8-30
GB/T 8110-1995
ER 70S-6 (ER 50-6)
2010-8-30
Mechanical Properties of Deposited Metal
Chemical Compositions of the welding wire
Item
Specifieation
Actual Result
Element
Specification
Actual Result
Element
Specification
Actual Result
Tensile Strength
≥500
525
C
0.06-0.15
0.07
Cr
___
0.039
σb(Mpa)
Yield Strength
≥420
435
Mn
1.40-1.85
1.56
Ni
___
0.015
60.2(Mpa)
Elongation
≥22
28
Si
0.80-1.15
0.9
Cu
≤0.50
0.018
δ5(%)
V Impact Tem
-29
-29
S
≤0.035
0.012



(°C)
Impact Yalue
≥27
94 95 73
P
≤0.025
0.01



Impact Yalue


High Quality Gas Shielded Welding Wire Supplier

1welding wire model No.:ER70s-6
2material:CO2
3diameter:0.8mm-1.6mm
4melting point:1300
Description:
ER70S-6
is a kind of mild steel copper coated welding wire , suitable for 100% CO2 and Argon & CO2 mixed gas protective welding with stable feasibility , good welding seams , less spatters and excellent welding process properties.
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts

High Quality Gas Shielded Welding Wire Supplier

Welding Wire Er70s-6
1 Low welding costs,All-position welding.
2 Easy to operate. All-position welding
3.Size:0.6-1.6MM,15kg
Supply High Quality welding wire
Er70S-6 welding wire
Introduction:
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Low welding costs.High productivity and low electricity consumption.
3. Easy to operate. All-position welding.Little deformation after welding.
4.Suitable for welding thin, medium and thick plates.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30°C)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550
20~25









AWS E71T-1 Welding Wire
Introduction:
It is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel.
Uses:
Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels,
Chemical Composition of Deposited Metal (%)
(CO
2
Shielding Gas)
Chemical Composition
C
Mn
Si
S
P
Guarantee Value
≤0.18
≤1.75
≤0.90
≤0.030
≤0.030
General Result
0.05
1.46
0.42
0.010
0.017
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥480
≥400
≥22
≥27(-20°C)
General Result
580
480
27
128
Reference Current
(DC+)
Wire Diameter(mm)
φ1.2
φ1.4
φ1.6
Current Range(A)
Downhand Welding
120~300
150~400
180~450
Vertical Upward Welding and Overhead Position Welding
120~260
150~270
180~280
Vertical Downward Welding and Overhead Position Welding
200~300
220~300
250~300
Horizontal Welding
120~280
150~320
180~350















High Quality Mig Welding Wire Copper Coated of AWS ER70S-6

1.MODE NO.:ER70S-6/A18/ER50-6/SG2/YGW12
2.DIAMETER:08-2.0mm
3.ISO 9001
4.USE FOR WELDING OF CARBON STEEL AND LOW ALLOY STEEL
High Quality Mig Welding Wire Copper Coated of AWS ER70S-6:
Description:
The product has a nice welding property, and many advantages such as fast to melt, deposit efficiently, arc stable, less spatter, beautiful weld appearance, good oxidation resistance, low gas sensitivity, easy to operate, and so on, it is suitable for automatic, semi-automatic all-position welding facilities.
Application:
Our final products are mainly used in all-position welding of carbon steel, low alloy steel and low-alloy high-strength steel, widely used in constructional engineering, bridge construction, vehicle manufacture, shipbuilding, iron, steel framework and pressure vessel industry, can also be used in pipes and sheet The high-speed welding.

Specification

GB/T
AWS
JIS
DIN
BS
ER50-6
ER70S-6
YGW12
SG2
A18

Chemical Composition of Deposited Metal (%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035


≤0.50

Mechanical Properties or Deposited Metal

Item
Tensile Strength (σb)Mpa
Yield Point
(σ0.2)Mpa
Elongation
δ5%
Akv impact(J)
Guarantee value
≥500
≥420
≥22
≥27(-29°C)
General Result
525
435
28
95

Diameter And Reference Current(DC+)
Diameter(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Current(A)
50-120
70-240
80-350
170-450

Notice
To avoid the wire rust
,the wire should be located in
dry
environments, and open the packs just when welding
Please
clean out
the oil, rust, water and other impurities from the wire surface, before welding.











ALPHA tin wire

1.ALPHA tin wire
2. good quality
3. 450g
ALPHA tin wire

Alpha tin wire with the percentage content of different chemical and flux for manual welding and automatic welding.
have the most disposable welding core similar to the activity of RMA type flux residues and transparent.
water-soluble core solder provides excellent wetting, bright solder joints after, designed specifically for water cleaning processes.
RMA and RA are the core welding symbol IPCJ-STD-006 and JIS Z 3283AA-level / A level standard.
The flux can be dissolved in solvents with less smoke, easy flying characteristics
Flux content: content ranging from 1.2% to 3.5%.
For most applications, the proposed flux content of 1.8 to% 2.0.

High Quality Silver Tin Solder Wire (Sn63/Pb37 )

Sn63/Pb37 solder wire:
Even and bright welding spot, favorable diffusion performance, no corrosion, no pungent smell
High Quality Silver Tin Solder Wire (Sn63/Pb37 )

Item
Specifications

Flux content(%)
2.0±0.2

Specific gravity
7.3

Melting point
183°C

Package weight
Diameter<0.8mm,0.5kg ; Diameter>0.8mm,1.0kg Package unit 10 kgs/box

Usage
Suitable for use with standard wave soldering/solder posts

Storage information and warrantee period
Store in a cool, dry, non-corrosive environment. Product warrantee period of 3 years

Chemical composition of solder alloy







Metal element
Sn
Pb






Composition(%)
Blance
36.7






Maximum threshold of impurities in solder alloy






Metal element
Bi
Zn
Fe
Al
As
Cd
Cu
Sb
Composition(%)
0.027
0.002
0.007
0.007
0.03
0.002
0.04
0.12
Notes: This product and all components are compliant with GB/T 3131-2001



High Quality Steel Welding Wire

High Quality Steel Welding Wire:
(1) Good Weldability
(2) Low Residue
(3) Low Splash
(4) High Reliability

High Quality Steel Welding Wire:
Our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability.
The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.


Er70S-6 welding wire
Introduction:
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Low welding costs.High productivity and low electricity consumption.
3. Easy to operate. All-position welding.Little deformation after welding.
4.Suitable for welding thin, medium and thick plates.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30°C)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550
20~25





AWS E71T-1 Welding Wire
Introduction:
It is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel.
Uses:
Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels,
Chemical Composition of Deposited Metal (%)
(CO
2
Shielding Gas)
Chemical Composition
C
Mn
Si
S
P
Guarantee Value
≤0.18
≤1.75
≤0.90
≤0.030
≤0.030
General Result
0.05
1.46
0.42
0.010
0.017
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥480
≥400
≥22
≥27(-20°C)
General Result
580
480
27
128
Reference Current
(DC+)
Wire Diameter(mm)
φ1.2
φ1.4
φ1.6
Current Range(A)
Downhand Welding
120~300
150~400
180~450
Vertical Upward Welding and Overhead Position Welding
120~260
150~270
180~280
Vertical Downward Welding and Overhead Position Welding
200~300
220~300
250~300
Horizontal Welding
120~280
150~320
180~350

High Quality copper clad steel wire

Copper Coated Welding Wire ER 70s-6
1. Diameter: 0.8mm,1.0mm,1.2mm,1.6mm
2. The face is smooth.
3. Little flash and smog
Copper Coated Welding Wire ER70s-6

1. Diameter: 0.8mm,1.0mm,1.2mm,1.4mm,1.6mm
2. The face is smooth.
3. Little flash and smog. High efficiency, low power consumption

The content is as follows:

C
Si
Mn
P
S
Cr
Mo
V
Cu
Ni
0.07
0.85-0.90
1.45-1.50
0.14-0.20
0.01-0.02
0.04
0.01-0.02
0.008-0.010
0.02
0.030

Mechnical Properties:
Rel or Rp0.2
( Mpa)
Rm
A(%)
Z(%)

370-375
535-545
27.5-28.5




Uses:
They are mainly used in low carbon steel and alloy and widely used in vehicles, bridge projects, ship building and containers. We gained good reputation for our low price but high quality among our customers. So we hope we can have business relations with your company.


High Quality er70s welding wire

er70s welding wire
1)melting fast,ISO9001 certified
2)efficient cladding
3)low splash
4)high reliability
er70s welding wire
MODEL:GB/T ER50-6 AWS ER70S-6 DIN SG2
Features Specifications:

use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures

Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
co2 gas shielded welding wire
Introduction
: Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Chemical Composition of Welding Wire(%)
C
Mn
Si
P
S
Cu
0.06-0.15
0.80-0.15
0.80-1.15
≤0.025
≤0.035
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
15/18
15/18
15/20
15/20
15/20





High Quality er70s-6 copper coated welding wire

er70s welding wire
1)melting fast,ISO9001 certified
2)efficient cladding
3)low splash
4)high reliability
High Quality er70s-6 copper coated welding wire
MODEL:GB/T ER50-6 AWS ER70S-6 DIN SG2
Features Specifications:

use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures

Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, traightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
co2 gas shielded welding wire
Introduction
: Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Chemical Composition of Welding Wire(%)
C
Mn
Si
P
S
Cu
0.06-0.15
0.80-0.15
0.80-1.15
≤0.025
≤0.035
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27
Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
15/18
15/18
15/20
15/20
15/20





High Quality of Welding material

Welding material:our annul production is about 5000t
1)good weldability
2)low residue
3)low splash
4)high reliability
Welding material:

We offer the items of the welding wire by the brand of ER50-6,ER70s-6,E501T-1,E711T, H08A,H08MnA,which has the specification of 0.8~φ5.0mm for your choosing.In addition,we also supply welding rod of J501Fe18,J422,J502,J506,J507 and stainless steel electrode A102 and 431 welding flux.our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability. The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.
.


Trade Mank
Diameter
Lot No
Mfg Date
Executive Standard
Type
Date of lssue
ER 70S-6 (ER 50-6)
Φ1.2mm
X020892
2010-8-30
GB/T 8110-1995
ER 70S-6 (ER 50-6)
2010-8-30
Mechanical Properties of Deposited Metal
Chemical Compositions of the welding wire
Item
Specifieation
Actual Result
Element
Specification
Actual Result
Element
Specification
Actual Result
Tensile Strength
≥500
525
C
0.06-0.15
0.07
Cr
___
0.039
σb(Mpa)
Yield Strength
≥420
435
Mn
1.40-1.85
1.56
Ni
___
0.015
60.2(Mpa)
Elongation
≥22
28
Si
0.80-1.15
0.9
Cu
≤0.50
0.018
δ5(%)
V Impact Tem
-29
-29
S
≤0.035
0.012



(°C)
Impact Yalue
≥27
94 95 73