Mig welding wire ER70S-6 mild steel

welding wire ER70S-6
1.Mig wire/CO2 wire/SG2wire
2.Dia :0.8-1.6mm
3.packing:5Kg,15Kg
4.the filler for welding
Mig Welding wire Co2 Gas Shielded (ER70S-6):

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

AWS E71T-1 Flux Cored Wire

Flux-Cored Wire AWS E71T-1 is a tubular wire with a metallic powder flux inside.
AWS E71T-1
Flux-Cored Wire
AWS A5.20 E71T-1
GB/T 10045-2001 E501T-1

Introduction:
Flux Cored welding Wire AWS E71T-1 welding wire is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel. It’s a kind of titania type CO2 gas-shielded flux-cored welding wire which has excellent welding performance, soft and stable arc, fewer spatters, good slag detachability and beautiful appearance of weld. Suitable for downhand welding and horizontal welding. All-position welding.

Uses:
AWS E71T-1Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Such as building of ships, machines, steel structure and bridges, etc

Diameter: 0.9-1.6mm flux cored welding wire
Certificate of Approval: CCS, ABS,GL,BV,LR,NK,DNV,KR,RINA
Packing: 15kgs /spool+ppbag+carton

Mig welding wire ER70S-6(0.8,0.9,1.0,1.2,1.6mm)

welding wire:ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam
Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

CO2 Welding Wire

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
(AWS ER70S-6)
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Packing
Net weight:5kg/spool,12.5kg/spool,15kg/spool,20kg/spool
a spool/carton,72cartons/pallet

Mig welding wire ER70S-6(0.8,0.9,1.0,1.2,1.6mm)

welding wire:ER70S-6:0.8~1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam
Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

CO2 Welding Wire

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Mig welding wire ER70S-6(Dia0.8,1.0,1.2,1.6mm)

ER70S-6:0.8,1.0,1.2,1.6mm
Certificate:ISO9001:2000
Free sample be provided
Professional manufacturer

Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

Stone Bridge CO2 mig Welding Wire ER70S-6

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
(AWS ER70S-6)
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Packing
Net weight:5kg/spool,12.5kg/spool,15kg/spool,20kg/spool
a spool/carton,72cartons/pallet or as request

Mig welding wire ER70S-6(Dia0.8,1.0,1.2,1.6mm)

ER70S-6:0.8,0.9,1.0,1.2,1.6mm
Certificate:ISO9001:2000
Free sample be provided
Professional manufacturer

Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

Stone Bridge CO2 mig Welding Wire ER70S-6

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
(AWS ER70S-6)
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Packing
Net weight:5kg/spool,12.5kg/spool,15kg/spool,20kg/spool
a spool/carton,72cartons/pallet or as request

AWS E71T-1 Flux Cored welidng Wire

flux cored welding wire AWS A5.20 E71T-1
have been approved ABS,CCS,DNV,
LR,GL,BV,NK,KR,RINA FOR 3Y
flux cored welding wire AWS A5.20E71T1

Is Used for high efficiency welding in all position
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
a) 1.0mm
b) 1.2mm
c) 1.4mm
d) 1.6mm
3) Standards:
a) GB/T10045-2001
b) E501T-1
c) AWS A5.20 E71T-1
d) JIS Z3313
e) YFW C50DR
Outer packing:
Carton

Mig welding wire ER70S-6(Dia0.8,1.0,1.2,1.6mm)

ER70S-6:0.8,0.9,1.0,1.2,1.6mm
Certificate:ISO9001:2000
Free sample be provided
Professional manufacturer


Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

Stone Bridge CO2 mig Welding Wire ER70S-6

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
(AWS ER70S-6)
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Packing
Net weight:5kg/spool,12.5kg/spool,15kg/spool,20kg/spool
a spool/carton,72cartons/pallet or as request

Mig welding wire ER70S-6

1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550

Mig welding wire ER70S-6

ER70S-6:0.8,0.9,1.0,1.2,1.6mm
Certificate:ISO9001:2000
Free sample be provided
stable arc,little splash,good welding seam
Company name
:
SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD
Company type
:
Manufacturer,Exporter (for 30 years);
Self-possessed brand
:
Stone bridge brand/Hero brand;
Welding wire type:
AWS ER70S-6

Stone Bridge CO2 mig Welding Wire ER70S-6

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO
2
ER50-6
(AWS ER70S-6)
≥420
≥500
≥22
≥27(-29)
CO
2
Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43

Application
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Specification
Diameter: 0.8mm,0.9mm,1.0mm,1.2mm,1.6mm
Spool sizes:
plastic spool D-200,D-270,D-300 (black,white color)
steel spool K-300
Spool weight: 5kg/spool,12.5kg/spool,15kg/spool,20kg/spool

Packing
Net weight:5kg/spool,12.5kg/spool,15kg/spool,20kg/spool
a spool/carton,72cartons/pallet or as request

Mig welding wire co2 gas shielded welding wire ,co2 welding wire

AWS ER70S-6 co2 welding wire Useing the advanced Electroplating copper coated technology


Mig welding wire co2 gas shielded welding wire ,co2 welding wire

Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20






















samples supply free

0.8 0.9 1.0 1.2 1.6 2.0mm

PLEASE CONTACT WITH ALICE

Mig welding wire co2 gas shielded welding wire co2 welding wire

co2 Gas shield arc welding wire
1.AWS ER70S-6 co2 welding wire
2.Gas shielded arc welding wire
3.size 0.6-2.0mm


Mig welding wire
co2 gas shielded arc welding wire
co2 welding wire

Original :Shijiazhuang city
Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20






















samples supply free

0.8 0.9 1.0 1.2 1.6 2.0mm

PLEASE CONTACT WITH ALICE

Mig welding wire er70s-6

CO2 gas-shield welding wire:AWS ER70S-6,DIN SG2:0.8~2.0mm
Submerged Arc Welding Wire

CO2 gas shield welding wire AWS ER70s-6
Features Specifications:

WELDING WIRE,mig welding wire,co2 welding wire
use to weld the situation in the construction thing.
High efficiency electrodes for welding some low alloy steel structures


Detailed Product Description
Material:
CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent
Ho8Mn2SiA steel by drawing, straightening and copper coating..
Application:

low carbon steel and low alloy steel, rolling stock, container,
engineering machinery, and pressure container, etc
Certificate:
ISO 9001:2000

CO2 GAS SHIELDED WELDING WIRE
Type
ChinaNationalStandard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
Max
0.035
max 0.025
max 0.50

Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation %
Temperature
Tensile Num KAV
Mi n500
Mi n 420
Mi n 22
-29°
C Mi n 27

Specifications /Reference Electric Current and Voltage Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

Mig welding wire mild steel

Mig welding wire(copper coated)
1.Mig wire/CO2 wire
2.Dia :0.8-1.6mm
3.packing:5Kg,15Kg,250Kg
4.ISO9001:2000
Mig welding wire/Co2 welding wire/sg2 (ER70S-6)welding wire
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

Mig welding wire supplier

MIG WELDING WIRE SG2
1.Copper coated welding wire
2.Dia:0.8mm-1.6mm
3.Packing:5Kg,15Kg,250Kg
4.ISO9001:2000
welding wire
sg2 ER70S-6/
Mig welding wire/CO2 welding wire
Specification:
1)Size: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
2)Application: Suitable to single or multiple weld welding of carbon steel and low alloy steel with strength grade of 500MPa (e.g. the welding of vehicle, bridge, construction, and mechanical structure etc), also applicable to high speed welding of thin plates and pipes etc.

Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position

Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)


/

AWS E71T-1 welding material

welding material AWS E71T-1 (manufacturer ) has
been arrpoved by CCS,ABS,DNV,LR,GL,
BV,NK,KR,RINA .
welding material AWS E71T-1 (manufacturer ) it used for high efficiency welding in all positions.


Chemical Composition of deposited Metal(%)
C
Mn
Si
S
P
0.05
1.26
0.31
0.009
0.011

Mechanical Properties of Deposited Metal
σb (MPa)
tensile strength
σs (MPa)
yield strength
σ5(%)
elongation
Akv(J)
590
510
28
(-20
0
C)116

Dia.(mm)
Shielding Gas
polarity
1.2/1.4/1.6
Co
2
DC(+)

Mig welding wire,Co2 welding wire,ER70S-6

Mig welding wire,Co2 welding wire,ER70S-6
Mig welding wire,Co2 welding wire,ER70S-6"

ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
Application
Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
Conform with
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1

Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg5kg15kg18kg20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6


Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts

Mig welding wire/SG2 Welding wire (0.8-1.6mm) 15kg/spool

MIG WIRE/SG2 Welding wire
Dia: 0.8-1.6mm
Spool: D200 D270 D300 K300
Free samples!
ISO Certified.


CO2 WELDING WIRE/MIG WELDING WIRE
co2 wire/sg2 welding wire.
Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates



CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300

Mig welding wire/co2 welding wire/SG2 welding wire

Welding wire ER70S-6:
1.CO2 wire/SG2 wire/Mig wire
2.copper coated
3.Dia :0.8mm-1.6mm
4.packing:5Kg,15Kg
Welding wire ER70S-6-Mild steel(copper coated):

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel ,such as container building,construction machine,railway construction,pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Mig welding wire

Mig welding wire our CO2 welding wire has excellent technological properties such as smooth steady feeding, fast melting rate, e
Mig welding wire
Features:
1) Suitable for use in such industries as:
a) Metallurgical industry
b) Bridge building
c) Building industry
d) Chemical industry
e) Shipping industry
2) Diameters:
a) 1.0mm
b) 1.2mm
c) 1.4mm
d) 1.6mm

Packing:
One spool is vacuum packed by aluminum film and then one carton outside.
Cirtificate: ABS, CCS, LR, GL, DNV, KR, NK, BV, RINA

Mig welding wire

Mig welding wire
the products have both excellent in quality and reasonable in price
wish to cooperate with you
I am Ellen
Mig welding wire
Model: AWS ER70S-6
Size: 0.8mm 0.9mm 1.0mm 1.2mm 1.6mm
Weight: 5kgs 15kgs 20kgs
Packing: Precision layer wire on the black plastic spool, then wound the anti-rust paper, then put in the carton, at last put on the plywood pallets
Usage: It is used for welding low carton steel and 50kgf/mm 5 grade of high-strength steel structures like vehicles, building, boat, bridge and etc. And can also be used for speed welding of sheet and pipes.

If you are intersted in our products, please contact me.

Mig welding wire

CO2 welding wire
1.Diameter: 0.8-1.6mm;
2.Packing: 15/20kgs spools.
3,Good Quality,Best Price.
4,Welcome to our company.
CO2 welding wire WS-AS.18,ER70S-6
Dia:0.8-1.6
suitable for thin plates
For AWS-AS.18,ER70S-6

FEATURE:Good project result and high quality weld can be obtained .The arc has stable burning and shallow penetration ,which is quite suitable for thin plates ,easy to operate.All position welding one side welding with back formation,beautiful oppearance of weld and no spatter.


Chemical composition of AWS ER70S-6 welding wire
(
%
)

C
Mn
Si
S
P
Cu
0.06
~
0.15
1.40
~
1.85
0.85
~
1.15
≤
0.025
≤
0.025
≤
0.30


Metal mechanical property of welding seam
σ
b
(MPa)
σ
s
(MPa)
δ
5
(%)
A
KV
(J) -30°C
≥500

≥420

≥22

-29
≥27



ER70S-6 welding wire
Er70s-6 Welding

Wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.



At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.

Mig welding wire

CO2 welding wire
1.Diameter: 0.8-1.6mm;
2.Packing: 15/20kgs spools.
3,Good Quality,Best Price.
4,Welcome to our company.
CO2 welding wire WS-AS.18,ER70S-6
Dia:0.8-1.6
suitable for thin plates
For AWS-AS.18,ER70S-6

FEATURE:Good project result and high quality weld can be obtained .The arc has stable burning and shallow penetration ,which is quite suitable for thin plates ,easy to operate.All position welding one side welding with back formation,beautiful oppearance of weld and no spatter.


Chemical composition of AWS ER70S-6 welding wire
(
%
)

C
Mn
Si
S
P
Cu
0.06
~
0.15
1.40
~
1.85
0.85
~
1.15
≤
0.025
≤
0.025
≤
0.30


Metal mechanical property of welding seam
σ
b
(MPa)
σ
s
(MPa)
δ
5
(%)
A
KV
(J) -30°C
≥500

≥420

≥22

-29
≥27



ER70S-6 welding wire
Er70s-6 Welding

Wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.



At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.


Introduction
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min)
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550

Above Please Reference,any question Please contact us as following contACT INFORMATION

Mig welding wire

CO2 gas-shield welding wire ER70s-6 has excellent mechanical performance such as depositing speed and high efficiency, stable ar

CO2 gas-shield welding wireER70s-6 has excellent mechanical performance such as depositing speed and high efficiency, stable arc.

Mig welding wire

1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.STANDARD: ER70S-6;ER49-1
3.SURFACE TREATMENT:COPPER COATED
4.SPOOL: WHITE OR BLACK
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.SURFACE TREATMENT:COPPER COATED
3.PACKING: AS PER CUSTOMER REQUEST
4.SPOOL: WHITE OR BLACK ETC
5. KIND OF SPOOL: PLASTIC OR METAL WIRE
6. STANDARD: ER70S-6,ER49-1

0.8-1.6mm ER70S-6 welding wire (HERO BRAND)

0.8-1.6mm AWS ER70S-6 co2 welding wire Useing the advanced Electroplating copper coated technology
Package :5/15/20kg/spool

0.8-1.6MM ER70S-6 WELDING WIRE HERO BRAND

Brand name :stone bridge /Hero brand


Brand type:SQ ER70S-6
Material :ER70S-6
Ø
5.5MM
Products Specification:0.8mm-1.6mm
Classification:Recommended products
Products introduction:SQ ER70S-6
Standard :GB ER50S-6




AWS ER70S-6 co2 welding wire
Using the advanced Electroplating copper coated technology
Package :
5/15/20kg/spool


ER70S-6 Welding Wire

CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20























PLEASE CONTACT WITH ALICE

AWS E71T-1 welding wire

welding wire
AWS E71T-1 (manufacturer )
has been approved by
CCS,ABS,DNV,LR,GL,
BV,NK,KR,RINA .
welding wire AWS E71T-1 (manufacturer )
it is used for high efficiency welding in all positions.


Chemical Composition of deposited Metal(%)
C
Mn
Si
S
P
0.05
1.26
0.31
0.009
0.011

Mechanical Properties of Deposited Metal
σb (MPa)
tensile strength
σs (MPa)
yield strength
σ5(%)
elongation
Akv(J)
590
510
28
(-20
0
C)116

Dia.(mm)
Shielding Gas
polarity
1.2/1.4/1.6
Co
2
DC(+)

Mig welding wire

Mig welding wire(copper coated)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig welding wire

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Mig welding wire

AWS ER70S-6 co2 welding wire Useing the advanced Electroplating copper coated technology

Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

Mig welding wire

Mig welding wire
Dia:0.6-0.8-1.0-1.2-1.6mm
Packing: 5-15-20kg
ISO certificate!
Free Samples

MIG/CO2 WELDING WIRE AWS ER70S-6

CO2 Welding wire
MIG WIRE
MIG WELDING WIRE.
SG2 WIRE


ER70S-6



Diameter (mm) 0.8/0.9/1.0/1.2/1.6
Package 5/15/20 kg.Carton
Spool: D200 270 300 K300
70S-6 is a low carbon, high manganese, very high silicon electrode. Used where higher alloy (manganese and silicon) is needed. Allows welding over some rust and dirt. Shielding gases range from CO2 to high Argon Blends.

ADVANTAGE

Excellent Welding
•Characteristics-ER70S-6 Wire renders good wetting action, straight bead edges, excellent arc action and high resistance to rust or mill scale porosity.
•Better Wire Feeding- less down time, higher productivity consistently stiff wire, no soft spots. Unique drawing method and special lubricants provide a smooth surface appearance, less friction in the wire feeding system, and elimination of copper coating flaking during wire feeding.
•More Resistance to porosity in the weld deposit.
•Contamination on the wire surface is minimized in the manufacturing process.
•Manufactured under a quality system certified to ISO 9001 requirements.







SPOOL TYPE: WHITE/BLACK SPOOL:D200 270 300. METAL FRAME: K300

TYPICAL APPLICATION

• Construction Equipment
• Agricultural Equipment
• Automotive
• Sheetmetal Containers
• Tubular Framework
• Light to Heavy Structural Steel Fabrication

DEPOSIT COMPOSITION



Requirements:
AWS E6013(%)
%C
%Mn
%Si
%P
%S
0.06 - 0.15
1.40 - 1.85
0.80 - 1.15
0.025
0.035
Typicle Values(%)
0.080
1.13
0.60
0.010
0.011

Mig welding wire

AWS ER70S-6 co2 welding wire Useing the advanced Electroplating copper coated technology
Electroplating copper coated technology for the welding wires.
Features:
1) Our wire is copper coated solid wire for CO2 welding for general engineering and structural application
2) Gives spatter-free welding with CO2 gas and Ar + CO2gas mixtures
3) The weld deposit is free from porosities with very smooth and uniform weld bead
4) Size (diameter): 0.6 - 2.0mm
Packing:
1) 5kg / 12.5kg / 13.5kg / 15kg precision layer wound plastic spools
2) Sealed in moisture-proof air tight plastic bag and cartons with silica
gel drying agent to prevent corrosion and rust, increase shelf life of
wires and cartons on the pallet
Welding Wire
CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20

Mig welding wire

1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550

Mig welding wire

Mig weld wire
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.STANDARD: ER70S-6;ER49-1
3.SURFACE:COPPER COAT
4.SPOOL: WHITE OR BLACK
Mig weld wire
1.SIZE:0.8,0.9,1.0,1.2,1.6MM
2.SURFACE TREATMENT:COPPER COATED
3.PACKING: AS PER CUSTOMER REQUEST
4.SPOOL: WHITE OR BLACK ETC
5. KIND OF SPOOL: PLASTIC OR METAL WIRE
6. STANDARD: ER70S-6,ER49-1

Mig welding- ER70S-6

1.welding wire, Application building,ships,briges,ect
2.good weldability
3.low residue
4.low splash
5.high reliability
1.welding wire AWS A5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2.Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3.

Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4.0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5.15kg, 20kg iron spool layer wind
6.100kg, 250kg, 350kg drum packing

Mig wire (0.8-1.6mm)

MIG WELDING WIRE
1Low welding costs.
2High productivity and low electricity consumption
3Easy to operate. All-position weld


CO2 WELDING WIRE/MIG WELDING WIRE

Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates



CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300

AWS E71T-11 Self sheilded Flux-Cored Welding Wire

Self sheilded Flux-Cored Welding Wire
AWS E71T-11
GB E501T-11
Self sheildedFlux-Cored Welding Wire
AWS
E71T-11
GB
E501T-11


Self sheilded Flux-Cored Welding Wire E71T-11 is
good in crack resistance suitable for all positions especialy in vertical up welding.

Diameter: 0.8-1.6mm Self sheilded
Certificate of Approval:
CCS, ABS,GL,BV,LR,NK,DNV,KR,RINA
Packing: spool+ppbag+carto

Mig wire - ER70S-6

1.welding wire, Application building,ships,briges,ect
2.good weldability
3.low residue
4.low splash
5.high reliability
1.welding wire - AWS A5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2.Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3.

Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4.0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5.15kg, 20kg iron spool layer wind
6.100kg, 250kg, 350kg drum packing

Mig wire 0.8mm

0.8mm:our annual production is about 5000tons
1)good weldability
2)low residue
3)low splash
4)high reliability
0.8mm:

We offer the items of the welding wire by the brand of ER50-6,ER70s-6,E501T-1,E711T, H08A,H08MnA,which has the specification of 0.8~φ5.0mm for your choosing.In addition,we also supply welding rod of J501Fe18,J422,J502,J506,J507 and stainless steel electrode A102 and 431 welding flux.our final products are with homogeneous coating and good anti-rust properties and also with the advantages such as stablity in the arc, little spatter, beautiful shape and strong weldability. The products are applied to vehicles, buildings, bridges, shipbuilding, Iron, Steel and pressure vessel industries, and can also be applied to high-speed welding for sheet metal and piping.
.


Trade Mank
Diameter
Lot No
Mfg Date
Executive Standard
Type
Date of lssue
ER 70S-6 (ER 50-6)
Φ1.2mm
X020892
2010-8-30
GB/T 8110-1995
ER 70S-6 (ER 50-6)
2010-8-30
Mechanical Properties of Deposited Metal
Chemical Compositions of the welding wire
Item
Specifieation
Actual Result
Element
Specification
Actual Result
Element
Specification
Actual Result
Tensile Strength
≥500
525
C
0.06-0.15
0.07
Cr
___
0.039
σb(Mpa)
Yield Strength
≥420
435
Mn
1.40-1.85
1.56
Ni
___
0.015
60.2(Mpa)
Elongation
≥22
28
Si
0.80-1.15
0.9
Cu
≤0.50
0.018
δ5(%)
V Impact Tem
-29
-29
S
≤0.035
0.012



(°C)
Impact Yalue
≥27
94 95 73
P
≤0.025
0.01



Impact Yalue

Mig wire E71T-1

Mild steel Welding wire :
1.Dia:1.2,1.4,1.6mm
2.packing:15Kg
3.good slag removable
4.low fume&spatter
FLUX Welding wire (copper coated):

E71T-1 is an all-position, flux cored welding wire, which is intended for single and multiple pass welding of low-alloy and carbon steel where a minimum 70,000 psi tensile strength is required. It is an excellent general purpose welding wire. A shielding gas must be used with this wire.
Typical Applications
General-purpose flux cored welding of steel
Structural steel
Farm machinery
Construction equipment
General carbon steel fabrication
AWS Specification

AWS A5.20
AWS Classification

E71T-1
Welding Current
DCEP (Electrode Positive, Reverse Polarity)
Typical Wire Chemistry
C 0.05
Si 0.74
Mn 1.00
P 0.008
S 0.015
Typical Mechanical Properties (As Welded)
Yield Strength, psi 71,000
Tensile Strength, psi 82,800
% Elongation in 2" 25
Welding Positions
All positions
Shielding Gas

100% CO
2
or 75% Ar / 25% CO
2
mix
Available Diameters
.035”, .045”, .052”, & 1/16”
Operating Range In Amps
.030” 40 –100
.035” 100 – 130
.052” 140 – 180
1/16” 175 – 300

Mig wire/SG2 Welding Wire AWS ER70S-6

Mig wire/SG2 Welding Wire AWS ER70S-6
Dia:0.8-1.6mm
Spool: D200 270 300 K300
Free Samples
ISO CERTIFIED
CO2 gas Welding Wire AWS ER70S-6
MIG WIRE/SG2 Welding wire AWS ER70S-6


Co2 gas shielded welding wire/mig welding wire AWS ER70S-6

CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300

Mig wire/co2 welding wire (0.8-1.6mm)

MIG WELDING WIRE
1Low welding costs.
2High productivity and low electricity consumption
3Easy to operate. All-position weld


CO2 WELDING WIRE/MIG WELDING WIRE

Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates



CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300

Mig wire

1 Low welding costs.
2 High productivity and low electricity consumption.
3 On time delivery
This wire is engineered to provide porosity-free, x-ray quality welds at the highest tensile strength (as welded) of all the plain carbon steel wires. This product requires a shielding gas: CO2 and/or CO2 mix.

Typical Wire Chemistry:

C: 0.09
Mn: 0.98
Si: 0.59
P: 0.01
S: 0.012

Welding Positions
:
All Positions

Typical Mechanical Properties (As Welded):
Yield Strength, Mpa: ≥420
Tensile Strength, Mpa: ≥510
% Elongation: ≥22

Available Diameters:
0.6mm,

0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.4mm & 1.6mm

Available Spools:
plastic spool and metal basket

Available Weight per Unit:
0.9kg, 1kg, 5kg, 12.5kg, 15kg, 20kg, 27kg, 250kg and 350kg.

Mig wire

1.Diameter: 0.8-1.6mm;
2.Packing: 15/20kgs spools.
3,Good Quality,Best Price.
4,Welcome to our company.
CO2 welding wire WS-AS.18,ER70S-6
Dia:0.8-1.6
suitable for thin plates
For AWS-AS.18,ER70S-6

FEATURE:Good project result and high quality weld can be obtained .The arc has stable burning and shallow penetration ,which is quite suitable for thin plates ,easy to operate.All position welding one side welding with back formation,beautiful oppearance of weld and no spatter.


Chemical composition of AWS ER70S-6 welding wire
(
%
)

C
Mn
Si
S
P
Cu
0.06
~
0.15
1.40
~
1.85
0.85
~
1.15
≤
0.025
≤
0.025
≤
0.30


Metal mechanical property of welding seam
σ
b
(MPa)
σ
s
(MPa)
δ
5
(%)
A
KV
(J) -30°C
≥500

≥420

≥22

-29
≥27



ER70S-6 welding wire
Er70s-6 Welding

Wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.



At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.


Introduction
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min)
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550

Above Please Reference,any question Please contact us as following contACT INFORMATION.

Mig wire

Mig welding wire(copper coated)
1.Dia :0.8-1.6mm
2.packing:5Kg,15Kg
3.high quality and lower price
4.ISO9001:2000
Mig welding wire

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Mig/ co2 Welding Wire (ER70S-6)

Mig/co2 welding wire ER70S-6
carbon steel welding wire/
CO2 gas shielded welding wire/ER50-6/ER70s-6
Mig/ co2 Welding Wire (ER70S-6)
co2 gas shielded welding wire
carbon steel welding wire

Performance
This product adapts advanced copper electroplating technology. The surface of welding wire is smooth and level and the copper layer is uniform and firm. Being adapted cisarrangement technique. it has excellent weld technology property and many advantages such as stable arc. small splashing, smooth and beautiful weld line, convenient to send welding wire and high work efficiency,etc. It is suitable for auto and semi-auto omniberaing weld.

Welding wire chemical Composition(%)
Trade mark \Composition
C
Mn
Si
S
P
Ni
Mo
Cr
Cu
ER49-1
≤0.11
1.80-2.10
0.65-0.95
≤0.030
≤0.030
≤0.30
----
≤0.20
≤0.50
ER50-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025

----

≤0.50
Mechanical properties of deposited metal

Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ()
Protect gas
ER49-1
≥372
≥490
≥20
≥47(Room temperature)
CO2
ER50-6
≥420
≥500
≥22
≥27(-29)
CO2

Specification and reference current
Diameter(mm)
0.80
1.00
1.20
1.60
Currents(A)
40-140
70-250
80-350
170-550
Voltage(V)
16-21
17-27
18-30
23-43
Use
Apply to the alloy steel of low carbon mainly, is extensively used in the vehicle, the science of bridge buliding, engineering machinery, steel construction, shipping making, trade container, etc

Mig/CO2 welding wire 0.8mm

CO2 Mig Welding wire:
1.CO2 wire/SG2 wire/Mig wire
2.copper coated
3.Dia :0.8mm-1.6mm
4.packing:5Kg,15Kg
CO2 Mig wire:
ER70S-6-Mild steel(copper coated):

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel ,such as container building,construction machine,railway construction,pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

AWS E71T-1

flux-cored wire welding material
used for shipbuilding, machinery, vehicles. Buildings and bridges all-position welding
Description: is a new flux-cored wire welding material, the current can be used for automatic welding, semi-automatic welding, gas shielded arc welding, welding, or with self-shielded flux, such as automatic welding.
Characteristics: CO2 gas or flux-cored wire is Ar +20-50% Co2 gas mixture of all-position welding wire. Compared with solid wire, the less spatter, weld forming beautiful, gentle arc stability, slag coverage even slag off a good performance. A wide range of uses flux-cored wire, weld are mostly good quality and adaptability of the base metal, and welding of high productivity
Application: used for shipbuilding, machinery, vehicles. Buildings and bridges all-position welding

Mig/CO2 welding wire 1.0mm

CO2 Mig Welding wire:
1.CO2 wire/SG2 wire/Mig wire
2.copper coated
3.Dia :0.8mm-1.6mm
4.packing:5Kg,15Kg,250Kg
CO2 Mig wire:
ER70S-6-Mild steel(copper coated):

Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel ,such as container building,construction machine,railway construction,pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Mig/CO2 welding wire

Mig /CO2 WELDING WIRE
1.Copper coated welding wire
2.Dia:0.8mm-1.6mm
3.Packing:5Kg,15Kg,250Kg
4.ISO9001:2000
welding wire
sg2 ER70S-6/
Mig welding wire/CO2 welding wire
Specification:
1)Size: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
2)Application: Suitable to single or multiple weld welding of carbon steel and low alloy steel with strength grade of 500MPa (e.g. the welding of vehicle, bridge, construction, and mechanical structure etc), also applicable to high speed welding of thin plates and pipes etc.

Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position

Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)


/

Mig/Co2 Welding wire (0.8-1.6mm)

MIG WELDING WIRE
1Low welding costs.
2High productivity and low electricity consumption
3Easy to operate. All-position weld


CO2 WELDING WIRE/MIG WELDING WIRE

Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates



CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300

Mig/Co2 Welding wire

MIG WELDING WIRE
1Low welding costs.
2High productivity and low electricity consumption
3Easy to operate. All-position weld


CO2 WELDING WIRE/MIG WELDING WIRE

Product Description
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates



CO2 GAS SHIELDED WELDING WIRE
Type
China Natinal Standard (GB)
Internatinal
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temper ature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/18
5/15/18
5/15/20
5/15/20
5/15/20
Packing: 5kg/15kg/20kg per spool with pallet
spool size: D200/270/300 K300

Mig/Co2 gas welding wire AWS ER70S-6 (ISO)

welding wire
used for plain steel in carbon and low metal alloy steel constructions, used for many layers welding ,double the
welding wire
Detailed Product Description:
Material:co2 gas Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..

Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.

Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.

Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm

Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.

Certificate: ISO 9001:2000

Mig/Co2 gas welding wire

welding wire
used for plain steel in carbon and low metal alloy steel constructions, used for many layers welding ,double the
welding wire
Detailed Product Description:
Material:Subermerged Arc Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..

Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.

Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.

Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm

Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.

Certificate: ISO 9001:2000

AWS E71T-1

flux cord wire AWS E71T-1 GB E501T-1
1.Certificate:ISO 9001:2000
2.Used for high effciency welding in all position
flux cord wire E71T-1

is a self-shielding flux cored wire used for welding carbon steels. This product does not require a shielding gas and can be used in limited multi-pass welding operations. The bead appearance is not equal to a gas-shielded product, but the benefits of not having to use gas makes this product popular. E71T-11 operates on straight polarity only (DCEN).
Typical Applications

Butt, lap and fillet welds on steel 16 gauge through ½”
Assembly and maintenance welding
Welding Current

DCEN (Electrode Negative, Straight Polarity)

Mig/co2 gas welding wire ER70S-6

welding wire
used for plain steel in carbon and low metal alloy steel constructions, used for many layers welding ,double the
welding wire
Detailed Product Description:
Material:Subermerged Arc Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..

Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automaticall.

Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.

Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm

Packing : 5kg,10kg, 15kg or 20kg packed in plastic spool.

Certificate: ISO 9001:2000

Mig/mag Welding wire ER70S-6

Mig/mag Welding wire ER70S-6
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price

Welding Wire ER70S-6,
Mig/mag Welding wire ER70S-6
, SG2 welding

wire, CO2 welding wire


Application

Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts
Mig welding wire ER70S-6

AWS E71T-7 Flux-Cored Welding Wire

Flux-Cored Welding Wire
AWS E71T-7
GB E501T-7
Flux-Cored Welding Wire
AWS

E71T-7

GB
E501T-7


Flux-Cored Welding Wire E71T-7 is
used in open air for welding pipe laying and gas pipeline which has higher requirments on low temperature and high toughness

Diameter: 1.6-2.4mm
Certificate of Approval:
CCS, ABS,GL,BV,LR,NK,DNV,KR,RINA
Packing: spool+ppbag+carto

Mild Steel Flux Cored Welding Wire E71T-1

Flux Cored Wedling Wire:
1.all position capability
2.Low fume&spatter.
3.good slag removabilty
4.less operater skills.
Description:
Flux Cored Wedling wire: E71T-1
it reduces production costs through higher deposition rates with excellent high integrity deposits. Superb weld profiles with low spatter and fume levels result in good operator appeal.

Applications:
Flux Cored Wedling wire is recommended for general purpose all positional welding of mild, carbon and carbon-manganese steels where excellent weld profile and penetration is required. Suitable for applications such as storage tanks, structural fabrication, machinery, earth moving equipment and fatigue loaded structures.

Packing:
All spools of wire are level layer wound on plastic spool.
The spools are then vacuum-packed with silica gel in moisture proof, foil-poly bags.
The spools of wire are boxed and securely stacked on wooden pallets with shrink-wrap plastic.

Chemical compostiton of deposited metal (shield gas:co2):
C
Mn
Si
P
S
0.036
1.40
0.52
0.013
0.011

Mechanical properties of deposited metal (shield gas:co2)
Yield Strength
Mpa(σb)
Tensile Strength
Mpa(σb)
Elongation
%(δ5)
Impact Value
-20°C(J)
505
570
26
120

Shipping Approvals:
ABS,LR,GL,BV,DNV,KR,CCS.

Mild Steel Flux Cored Welding Wire

Flux Cored Wedling Wire:
1.all position capability
2.Low fume&spatter.
3.good slag removabilty
4.less operater skills.
Description:
Flux Cored Wedling wire: E71T-1
it reduces production costs through higher deposition rates with excellent high integrity deposits. Superb weld profiles with low spatter and fume levels result in good operator appeal.

Applications:
Flux Cored Wedling wire is recommended for general purpose all positional welding of mild, carbon and carbon-manganese steels where excellent weld profile and penetration is required. Suitable for applications such as storage tanks, structural fabrication, machinery, earth moving equipment and fatigue loaded structures

Packing:
All spools of wire are level layer wound on plastic spool.
The spools are then vacuum-packed with silica gel in moisture proof, foil-poly bags.
The spools of wire are boxed and securely stacked on wooden pallets with shrink-wrap plastic.

Chemical compostiton of deposited metal (shield gas:co2):
C
Mn
Si
P
S
0.036
1.40
0.52
0.013
0.011

Mechanical properties of deposited metal (shield gas:co2)
Yield Strength
Mpa(σb)
Tensile Strength
Mpa(σb)
Elongation
%(δ5)
Impact Value
-20°C(J)
505
570
26
120

Shipping Approvals:
ABS,LR,GL,BV,DNV,KR,CCS.

Diameter:
1.2/1.4/1.6mm.