A5.17 H08A*Submerged-Arc Welding wire with Flux

A5.17 H08A Submerged-Arc Welding Wire with Flux
1.AWS EL-8 EL12 EM12 EM12K EH14
2.size :2.0-5.0mm
3.ISO BV IEI SGS
A5.17 H08A Submerged-Arc Welding wire with Flux
flux with submerged arc welding wire
carbon Submerged arc welding wire with flux
stone bridge /hero brand

original:shijiazhuang city



SHIJIAZHUANG SHIQIAO ELECTRIC WELDING MATERIAL CO.,LTD

Model:
EL12(H08A) EM12K(H08MnA) EH14(H10Mn2) ER13K(H10MnSi) ER49-1

Wire specification:
Φ2.0mm, Φ2.4mm, Φ2.5mm, Φ3.0mm, Φ3.2mm, Φ4.0mm, Φ5.0mm Φ5.5mm

Packing form
1. 20kg plastic spool packing(for only Φ2.0mm)
2. 25kg, 50kg, 150kg, 250kg, 350kg transverse wind without core
3. 30kg, 50kg dundle
4. 250kg drum packing


Performance
Used for submerged arc weldings of carbon steel, alloy steel (e.g. 16Mn, etc.). it features excellent metal mechanics property, stable arc. convent to remove welding slag, good figuration, can use auto and semi-auto multi-times weld, double surfaces weld, single wire and multi-wire weld at high speed, etc.

Welding wire chemical Composition (%)
Trade mark \Composition
C
Mn
Si
S
P
Mo
Ni
Cu
Cr
H08A
≤0.10
0.30-0.55
≤0.03
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H08MnA
≤0.10
0.80-1.10
≤0.07
≤0.030
≤0.030
----
≤0.30
≤0.20
≤0.20
H10Mn2
≤0.12
1.50-1.90
≤0.07
≤0.035
≤0.035
----
≤0.30
≤0.20
≤0.20
Mechanical properties of deposited metal
Trade mark \Performance
Yield strength Mpa
Tensile strength Mpa
Extension rate (%)
Shock valueJ ()
H08A
≥330
≥410
≥22
≥27
H08MnA
≥330
≥410
≥22
≥27
H10Mn2
≥330
≥410
≥22
----



Specification and reference current
Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Currents(A)
300-400
350-450
425-525
475-575
550-650