co2 welding wire E71T-1

excellent welding properties and the welding seams have very high impact resistance at low temperature.
Product Model;E501T-1, E71T-1

CO
2
is the use of titanium-based flux-cored wire welding. Deposited efficient performance of all-position welding process better, legislation can also be welded down. Applicable to ships, pressure vessels, mechanical equipment, steel bridges, such as low carbon steel and 490MPa high strength steel welding class.
Standard;
GB/T;E501T-1
AWS;E71T-1
chemical composition of welding wire(%)
C
Mn
Si
P
S

≤0.10
≤1.75
≤0.75
≤0.03
≤0.03

Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥400
≥480
≥22
≥47(0°C)
≥47(-20°C)

Wire Size(mm)
Φ1.0
φ1.2
φ1.4
φ1.6
Welding position
Welding current(A)
80~250
120~300
160~400
190~450
Please be noted:
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.Before welding please clean out the oil,rust,water etc from the work parts
3.The protection of the use of CO
2
gas, CO
2
gas purity of 99.98%.
4.CO
2
welding to protect the flow of gas should be controlled in 20-25L/min.
5.Extend the length of the wire should be controlled in the range of 15-25mm.
6.Preheating before welding to 150-300 °C, PWHT 700-740 °C tempered by the need to deal with.

Our annual exports to the world of welding material for more than 3000 tons, and our customers to establish a solid partnership, established a good reputation, product quality is our life, and sincerely look forward to working with you for your cooperation.
Packing:
5kg/spool
10kg/spool 15kg/spool
Standard:
0.6-1.6mm
Productivity:
500ton/month
Unit Price/Payment:
1270 usd/tons
HS Code:
72292000
Trademark:
UC
Origin:
China-hebei
Min. Order:
25 tons
Transportation:
by Sea
Welding Method:
Arc Welder
Assistant Appliance:
Gas Welding Glasses
Type:
Co2
flux-cored wire welding
Export Markets:
North America, South America, Eastern Europe, Southeast Asia, Africa, Oceania, Mid East, Eastern Asia, Western Europe

No comments:

Post a Comment