co2 solid metal ARC mig welding wire AWS ER70s-6

co2 ARC mig welding wire ER70s-6
as fast melting rate,high depositing efficiency,stable arc,little spatter,beautiful seam
CO2 gas-shielded welding wire ER70s-6
has excellent mechanical performance such as welding depositing speed and high efficiency,stable arc,little splash ,good welding seam.This series of welding wires are suitable for the low carbon steel and low alloy structure,vehicle,bridge,container,construction machinery,boilers and construction etc.
- AWS : ER70S-6
- Diameter : 0.8mm,0.9mm, 1.0mm, 1.2mm,1.6mm
Chemical composition: C 0.06-0.15, Mn 1.40-1.85, Si 0.80-1.15, P <=0.025, S <=0.035, Cu <=0.35, Ni <=0.30, Cr <=0.20
- Weight of spool : 5kg,15kg,12.5kg and 20kg.
- Packing: cartons lined with plastic spool
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg

chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)

Wire Size
(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position

Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just
when welding to avoid the wire rust.
Before welding please clean out the
oil,rust,water etc from the work parts