CO2 Mig Mag Welding Wire

CO2 Mig Wire :
(1) Good Weldability
(2) Low Residue
(3) Low Splash
(4) High Reliability
CO2 Mig Mag Welding Wire:

Description:
The product has a nice welding property, and many advantages such as fast to melt, deposit efficiently, arc stable, less spatter, beautiful weld appearance, good oxidation resistance, low gas sensitivity, easy to operate, and so on, it is suitable for automatic, semi-automatic all-position welding facilities.
Application:
Our final products are mainly used in all-position welding of carbon steel, low alloy steel and low-alloy high-strength steel, widely used in constructional engineering, bridge construction, vehicle manufacture, shipbuilding, iron, steel framework and pressure vessel industry, can also be used in pipes and sheet The high-speed welding.

Specification

GB/T
AWS
JIS
DIN
BS
ER50-6
ER70S-6
YGW12
SG2
A18

Chemical Composition of Deposited Metal (%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06-0.15
1.40-1.85
0.80-1.15
≤0.025
≤0.035


≤0.50

Mechanical Properties or Deposited Metal

Item
Tensile Strength (σb)Mpa
Yield Point
(σ0.2)Mpa
Elongation
δ5%
Akv impact(J)
Guarantee value
≥500
≥420
≥22
≥27(-29°C)
General Result
525
435
28
95

Diameter And Reference Current(DC+)
Diameter(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Current(A)
50-120
70-240
80-350
170-450

Notice
To avoid the wire rust
,the wire should be located in
dry
environments, and open the packs just when welding
Please
clean out
the oil, rust, water and other impurities from the wire surface, before welding.