welding wire

CmCtw founded in 1983 as "the bridge between welding and mould."We can support you weld materials, and repair it in you place.
welding wire

CMC-SKD11-3
Hardness:HRC56~58
mn 1.0 , 1.2 , 1.6 , 2.4 , 3.2 inch 3/64 , 1/16 , 3/32 , 1/8
For welding cold work steels, punch die, cut die, industrial knives, forming dies, harden surface of work piece.
This is a sort of high hardness, grinding-resisted, good toughness Argon filler rod.
CMC-SKD61-2
Hardness:HRC52~57
mn 1.0 , 1.2 , 1.6 , 2.4 , 3.2 inch 3/64 , 1/16 , 3/32 , 1/8
For welding hot forging die, hot cut die, hot punch die, hot formation die, hot work tool, steel casting die.
CMC-SKD61
Hardness:HRC42~46
mn 0.9 , 1.2 , 1.6 , 2.4 inch 3/64 , 1/16 , 3/32
For welding Aluminum & Copper casting die. Extrudsion dies.
Well heat-resisted, grinding-resisted, crack-resisted.
CMC-SKD61-42
Hardness:HRC42~48
mm 1.6 , 2.4 , 3.2 inch 1/16 , 3/32 , 1/8
For welding hot forging die, Aluminum & Copper hot forging die, Aluminum & Copper casting die.
Well heat-resisted, grinding-resisted, crack-resisted.
CMC-8407-H12
Hardness:HRC52~57
mn 1.0 , 1.2 , 1.6 , 2.4 , 3.2 inch 3/64 , 1/16 , 3/32 , 1/8
For welding hot forging die, hot cut die, hot punch die, hot formation die, hot work tool, steel casting die.
CMC-8407
Hardness:HRC40~45
mn 0.9 , 1.2 , 1.6 , 2.4 inch 3/64 , 1/16 , 3/32
For welding the die made of the alloy of Zinc, Aluminum, Stannum, etc.
CMC-M3-2
Hardness:HRC61~63
mn 1.2 , 1.6 , 2.4 inch 3/64 , 1/16 , 3/32
For welding & stretching, hot work and high hardness tool mold, hot forging general die, hot punch die, screw die, grinding-resisted hard surface, high-speed steel.
CMC-MS-3
Untreated:HRC30-32 After age hardening 2H/500 ?C:HRC48-52
mn 1.2 , 1.6 , 2.0 , 2.4 inch 3/64 , 1/16 , 5/64 , 3/32
Special hardening good toughness alloy, especially adapt to Aluminum gravity cast, gate, be able to extend product's life-span for 3-5 times afterwards. Be able to manufacture the greatly exact mold, super satin process, heat-resisted and crack-resisted when doing gating-weld.
CmC-12Cr
HRC53-57
mn 1.0 , 1.2 , 1.6 , 2.4 , 3.2 inch 3/64 , 1/16 , 3/32 , 1/8
Specially used for Cr12¡BCr12MoV series mold argon welding wire. If more than three layers need to be welded, CMC-30N can be used as the base.
When being used for Cr12 after heat treatment, no need of preheating for small area. The weld hardness is enough, it can be used for mechanical processing.
CMC-Magic1
After the hardening,HRC50-54
mn 1.0 , 1.2 , 1.6 , 2.4 inch 3/64 , 1/16 , 3/32
Very not easy to crack, suitable for high carbon content heat-treated steel.
Be used for embossing & drawing die, which can greatly reduce the scratches caused by bending and stretching between high tension steel and ordinary one.
CMC-STAVAX
HRC 50-54
0.9,1.2,1.6,2.4
Weld injection plastic die, good characteristic of erode-resisted and osmosis