Flux Cored Wire

Flux cored E70T-1 Welding Wire,
1. Diameter:0.8mm-1.6mm;
2. vacuum packing;
3. Model no.: AWS A5.20 E71T-1;
Flux Cored Welding Wire
Flux Cored Welding Wire
E71T Flux-cored weldinwire
The surface and inside of welding wires have stable and reliable quality and welding wires have big stiffness, providing stable wire feed and high welding efficiency.
Purpose:
This product is applicable to welding of low carbon steel and low alloy structural steel with a tensile strength of not less than 500mpa. It is widely used in such industrial sectors as metallurgy, heavy machinery, petrochemical processing, vehicles, ships, containers, bridges, buildings, nuclear power plants, pressure vessels and steel beams.
Diameter: 0.8-1.6mm
packing: 15kgs /spool+
waterproof

paper
+
vacuum bag+
carton

chemical composition of welding wire(%)
C
Mn
Si
P
S
≤0.10
≤1.75
≤0.75
≤0.03
≤0.03
Mechanical Properties or Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%
AKV impact(J)
≥400
≥480
≥22
≥47(0°C)

Wire Size(mm)
φ1.2
φ1.4
φ1.6
Welding position

Welding current(A)
120~300
160~400
190~450
Please be noted:
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.Before welding please clean out the oil,rust,water etc from the work parts
3.The protection of the use of CO2 gas, CO2 gas purity of 99.98%.
4.CO2 welding to protect the flow of gas should be controlled in 20-25L/min.
5.Extend the length of the wire should be controlled in the range of 15-25mm.
6.Preheating before welding to 150-300 °C, PWHT 700-740 °C tempered by the need to deal with.