copper brazing wire

Have good wetting ability, good mechanical strength and toughness with low melting point
Phos-Copper-silver brazing alloys have good wettability, higher strength and toughness of brazing seam and lower melting point. The heating speed should be as quick as possible while brazing. The joint is to be bright grey and will return to the original color of bronze while dipped into 10% sulphuric acid.

Product Number
Correlative Noumber
Chemical Analysis
Melting range
Application
Ag
P
Cu
Solidus°C
Liquidus°C
GWY-6P
L-CuP6

6.0
bal
710
890
Good capillary flow and ductibility,Capillary brazing of cooper,brass and bronze,No flux is required for copper
Gwy-7P
BCu93P

6.8-7.5
bal
710
790
L-CuP7

7.0
bal
710
790
BCuP-2

7.0-7.5
bal
710
793
GWY-8P
BCu92P

7.5-8.5
bal
710
780
L-CuP8

8.0
bal
710
770
GWY-7PSn
L-CuSnP7
Sn:6.8-7.2
6.6-7.0
bal
650
700
GWY-2B
BCu91PAg
1.8-2.2
6.8-7.2
bal
645
788
For brazing copper parts in airconditioners ,freezers,refrigerators and motors.The brazing perfomance is excellent.
BCuP-6
1.8-2.2
6.8-7.2
bal
645
788
L-Ag2P
2.0
6.2
bal
645
825
GWY-5B
BCu89PAg
4.8-5.2
5.8-6.7
bal
645
815
BCuP-3
4.8-5.2
5.8-6.2
bal
645
815
BCuP-7
4.8-5.2
6.5-7.0
bal
645
785
L-Ag5P
5.0
6.0
bal
645
815
GWY-6B
BCu87PAg
5.8-6.2
7.0-7.5
bal
645
724
BCuP-4
5.8-6.2
7.0-7.5
bal
645
724
GWY-15B
BCu80PAgP
14.5-15.5
4.8-5.2
bal
645
800
BCuP-5
14.5-15.5
4.8-5.2
bal
645
800
L-Ag15P
15.0
5.0
bal
645
800
GWY-18B
BCu75PAg
17.5-18.5
6.0-6.5
bal
645
680
For brazing copper and copper alloys in motors,transformation equipment and spectacles.
18M
18.0
6.3
bal
645
680
L-Ag18P
18.0
7.05
bal
645
645