co2 gas flux cored welding wire

Gas shield welding wire
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
contact us
Gas Shield Welding wire
Introduction:
Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses:
1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)

C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)

C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30°C)
General Result
558
472
27
98
Reference Current
(DC+)
Wire Size(mm)
Welding Current(A)
CO
2
Flow Rate(L/min)
φ0.8
50~100
15
φ1.0
50~220
15~20
φ1.2
80~350
15~25
φ1.6
170~550
20~25









Introduction:
It is a kind of gas-shielded flux-cored welding wire for low-carbon steel and 490MPa high strength steel. JQ.YJ501-1 is a kind of titania type CO2 gas-shielded flux-cored welding wire. It has excellent welding performance, soft and stable arc, fewer spatters, good slag detachability and beautiful appearance of weld. Suitable for downhand welding and horizontal welding. All-position welding. It has high welding efficiency. The weld metal has been given toughening treatment by microelements, so it has excellent low temperature toughness, good crack-resistance and stable and reliable inherent quality.
Uses:
Used for welding structures made of carbon steel and low-alloy structural steel with tensile strength higher than or equal to 490MPa. Most widely used for welding some key structures like shipbuilding, mechanical manufacture, pressure vessels, boilers, petroleum machinery, chemical machinery, hoisting machinery, etc.
Chemical Composition of Deposited Metal (%)
(CO
2
Shielding Gas)
Chemical Composition
C
Mn
Si
S
P
Guarantee Value
≤0.18
≤1.75
≤0.90
≤0.030
≤0.030
General Result
0.05
1.46
0.42
0.010
0.017
Mechanical Properties of Deposited Metal

Test Item
R
m
(MPa)
R
eL
R
p0.2
(Mpa)
A(%)
KV
2
(J)
Guarantee Value
≥480
≥400
≥22
≥27(-20°C)
General Result
580
480
27
128
Reference Current
(DC+)
Wire Diameter(mm)
φ1.2
φ1.4
φ1.6
Current Range(A)
Downhand Welding
120~300
150~400
180~450
Vertical Upward Welding and Overhead Position Welding
120~260
150~270
180~280
Vertical Downward Welding and Overhead Position Welding
200~300
220~300
250~300
Horizontal Welding
120~280
150~320
180~350