welding electrodes 6013 7018
ISO 9001:2008
Dia2.0mm-5.0mm
easy to welding
Delivery time 10days
Welding Electrodes 6013 7018
AWS E6013 Welding Electrodes
Description:
AWS E6013 is a low-carbon steel electrode with a high titanium coating and can be used on AC. or D.C. It has excellent welding technological properties .The arc is stable. The spatter is small. The slag viscosity is moderate. It can be used freely. The slag is easy to clean. The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel , such as ships, vehicles, building, and general machinery.
Conform with:
GB/T 5117 E4313 E6013 AWS A5.1 ISO 2560-B-E43 13 A
Chemical Composition of Wire (%):
C
Mn
Si
S
P
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength (MPa)
Tensile Strength(MPa)
Elongation (%)
AKV(J)
Guarantee Value
≥330
≥420
≥17
-
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
40-70
50-80
80-120
150-190
180-240
AWS E7018 Welding Electrodes
AWSE7018 is low-hydrogen potassium coating carbon steel welding rod and can be used on AC. or D.C . It has excellent welding technological properties. It can be used various composition. Its evident trait is composed of Fe power and can reduce welding layer.
Application:
Suitable for welding important structures made of low alloy steel.
Conform with:
GB/T 5117 E5018 E7018 AWS A5.1 ISO 2560-B-E49 18-1A
Chemical Composition of Wire(%):
C
Mn
Si
S
P
≤0.12
≤1.6
≤0.75
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength
(MPa)
Tensile Strength
(MPa)
Elongation
(%)
AKV(J)
Guarantee Value
≥400
≥490
≥22
≥27(-30°C)
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
60-90
90-120
120-150
170-200
210-250
Saturday, October 1, 2011
welding electrodes 6013 7018
welding electrodes 6013 7018
ISO 9001:2008
Dia2.0mm-5.0mm
easy to welding
Delivery time 10days
AWS E6013 Welding Electrodes
AWS E6013 is a low carbon steel electrode with a high tianiume coating and can be used on A.C or D.C. It has excellent welding technologiacal properities. The arc is atable . The spatter is small.The slge viscosity is miderate. It can be used freely. The slag is easy to claean.The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel , such as ships, vehicles, building, and general machinery.
Conform with:
GB/T 5117 E4313 E6013 AWS A5.1 ISO 2560-B-E43 13 A
Chemical Composition of Wire (%):
C
Mn
Si
S
P
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength (MPa)
Tensile Strength(MPa)
Elongation (%)
AKV(J)
Guarantee Value
≥330
≥420
≥17
-
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
40-70
50-80
80-120
150-190
180-240
AWS E7018 Welding Electrodes
AWSE7018 is low-hydrogen potassium coating carbon steel welding rod and can be used on AC. or D.C . It has excellent welding technological properties. It can be used various composition. Its evident trait is composed of Fe power and can reduce welding layer.
Application:
Suitable for welding important structures made of low alloy steel.
Conform with:
GB/T 5117 E5018 E7018 AWS A5.1 ISO 2560-B-E49 18-1A
Chemical Composition of Wire(%):
C
Mn
Si
S
P
≤0.12
≤1.6
≤0.75
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength
(MPa)
Tensile Strength
(MPa)
Elongation
(%)
AKV(J)
Guarantee Value
≥400
≥490
≥22
≥27(-30°C)
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
60-90
90-120
120-150
170-200
210-250
ISO 9001:2008
Dia2.0mm-5.0mm
easy to welding
Delivery time 10days
AWS E6013 Welding Electrodes
AWS E6013 is a low carbon steel electrode with a high tianiume coating and can be used on A.C or D.C. It has excellent welding technologiacal properities. The arc is atable . The spatter is small.The slge viscosity is miderate. It can be used freely. The slag is easy to claean.The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel , such as ships, vehicles, building, and general machinery.
Conform with:
GB/T 5117 E4313 E6013 AWS A5.1 ISO 2560-B-E43 13 A
Chemical Composition of Wire (%):
C
Mn
Si
S
P
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength (MPa)
Tensile Strength(MPa)
Elongation (%)
AKV(J)
Guarantee Value
≥330
≥420
≥17
-
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
40-70
50-80
80-120
150-190
180-240
AWS E7018 Welding Electrodes
AWSE7018 is low-hydrogen potassium coating carbon steel welding rod and can be used on AC. or D.C . It has excellent welding technological properties. It can be used various composition. Its evident trait is composed of Fe power and can reduce welding layer.
Application:
Suitable for welding important structures made of low alloy steel.
Conform with:
GB/T 5117 E5018 E7018 AWS A5.1 ISO 2560-B-E49 18-1A
Chemical Composition of Wire(%):
C
Mn
Si
S
P
≤0.12
≤1.6
≤0.75
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength
(MPa)
Tensile Strength
(MPa)
Elongation
(%)
AKV(J)
Guarantee Value
≥400
≥490
≥22
≥27(-30°C)
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
60-90
90-120
120-150
170-200
210-250
welding electrodes 6013 7018
welding electrodes 6013 7018
ISO 9001:2008
Dia2.0mm-5.0mm
easy to welding
Delivery time 10days
welding electrodes 6013 7018
AWS E6013 Welding Electrodes
Description:
AWS E6013 is a low-carbon steel electrode with a high titanium coating and can be used on AC. or D.C. It has excellent welding technological properties .The arc is stable. The spatter is small. The slag viscosity is moderate. It can be used freely. The slag is easy to clean. The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel , such as ships, vehicles, building, and general machinery.
Conform with:
GB/T 5117 E4313 E6013 AWS A5.1 ISO 2560-B-E43 13 A
Chemical Composition of Wire (%):
C
Mn
Si
S
P
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength (MPa)
Tensile Strength(MPa)
Elongation (%)
AKV(J)
Guarantee Value
≥330
≥420
≥17
-
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
40-70
50-80
80-120
150-190
180-240
AWS E7018 Welding Electrodes
AWSE7018 is low-hydrogen potassium coating carbon steel welding rod and can be used on AC. or D.C . It has excellent welding technological properties. It can be used various composition. Its evident trait is composed of Fe power and can reduce welding layer.
Application:
Suitable for welding important structures made of low alloy steel.
Conform with:
GB/T 5117 E5018 E7018 AWS A5.1 ISO 2560-B-E49 18-1A
Chemical Composition of Wire(%):
C
Mn
Si
S
P
≤0.12
≤1.6
≤0.75
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength
(MPa)
Tensile Strength
(MPa)
Elongation
(%)
AKV(J)
Guarantee Value
≥400
≥490
≥22
≥27(-30°C)
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
60-90
90-120
120-150
170-200
210-250
ISO 9001:2008
Dia2.0mm-5.0mm
easy to welding
Delivery time 10days
welding electrodes 6013 7018
AWS E6013 Welding Electrodes
Description:
AWS E6013 is a low-carbon steel electrode with a high titanium coating and can be used on AC. or D.C. It has excellent welding technological properties .The arc is stable. The spatter is small. The slag viscosity is moderate. It can be used freely. The slag is easy to clean. The welded seam is smooth and fine and easy to restrike the arc.
Application:
Suitable for welding sheet metal structure made of low-carbon steel , such as ships, vehicles, building, and general machinery.
Conform with:
GB/T 5117 E4313 E6013 AWS A5.1 ISO 2560-B-E43 13 A
Chemical Composition of Wire (%):
C
Mn
Si
S
P
≤0.12
0.3-0.6
≤0.35
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength (MPa)
Tensile Strength(MPa)
Elongation (%)
AKV(J)
Guarantee Value
≥330
≥420
≥17
-
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
40-70
50-80
80-120
150-190
180-240
AWS E7018 Welding Electrodes
AWSE7018 is low-hydrogen potassium coating carbon steel welding rod and can be used on AC. or D.C . It has excellent welding technological properties. It can be used various composition. Its evident trait is composed of Fe power and can reduce welding layer.
Application:
Suitable for welding important structures made of low alloy steel.
Conform with:
GB/T 5117 E5018 E7018 AWS A5.1 ISO 2560-B-E49 18-1A
Chemical Composition of Wire(%):
C
Mn
Si
S
P
≤0.12
≤1.6
≤0.75
≤0.035
≤0.040
Mechanical Properties of Deposited Metal:
Test Item
Yield Strength
(MPa)
Tensile Strength
(MPa)
Elongation
(%)
AKV(J)
Guarantee Value
≥400
≥490
≥22
≥27(-30°C)
Recommended Welding Current:
Electrode Diameter(mm)
2.0
2.5
3.2
4.0
5.0
Current Range(A)
60-90
90-120
120-150
170-200
210-250
welding electrodes
Summary Table of Gas-shielded Solid Welding Wire
Model GB AWS Current Main Applications
Summary Table of Gas-shielded Solid Welding Wire
Model
GB
AWS
Current
Main Applications
DC+
Used for welding atmospheric corrosion-resistant steel structures with corresponding strength, such as locomotive vehicles, offshore engineering, bridges, etc.
ER49-1
DC+
Used for welding low-carbon steel and some low-alloy steel structures.
ER50-3
ER70S-3
DC+
1. Used for welding low-carbon steel thin plates.
2. Used for welding low-carbon steel parts with thorough surface treatment.
ER50-4
ER70S-4
DC+
1. Used for welding sheet metal and thin plates.
2. Used for welding steel pipes.
ER50-6
ER70S-6
DC+
1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
ER50-G
ER70S-G
DC+
1. Used for welding all kinds of 500MPa structural steel parts, thick plates and thick pipelines.
2. Used for high speed welding on 500MPa base metals.
ER60-G
ER90S-G
Suitable for welding 600MPa high strength steel structures, such as construction machinery, pipelines, ships, pressure vessels, etc.
ER60-G
ER90S-G
Suitable for welding 600MPa high strength steel structures, such as construction machinery, etc.
ER70-G
ER100S-G
Suitable for welding 700MPa high strength steel structures, such as construction machinery, hoisting machinery, bridges, pipelines, ships, pressure vessels, etc.
ER80-G
ER110S-G
DC+
Suitable for welding high strength structures with tensile strength of 790MPa. It can be used for welding some key structures, such as pressure vessels, construction machinery, hoisting machinery, ships, mining machinery, etc.
ER55-G
DC+
Model GB AWS Current Main Applications
Summary Table of Gas-shielded Solid Welding Wire
Model
GB
AWS
Current
Main Applications
DC+
Used for welding atmospheric corrosion-resistant steel structures with corresponding strength, such as locomotive vehicles, offshore engineering, bridges, etc.
ER49-1
DC+
Used for welding low-carbon steel and some low-alloy steel structures.
ER50-3
ER70S-3
DC+
1. Used for welding low-carbon steel thin plates.
2. Used for welding low-carbon steel parts with thorough surface treatment.
ER50-4
ER70S-4
DC+
1. Used for welding sheet metal and thin plates.
2. Used for welding steel pipes.
ER50-6
ER70S-6
DC+
1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
ER50-G
ER70S-G
DC+
1. Used for welding all kinds of 500MPa structural steel parts, thick plates and thick pipelines.
2. Used for high speed welding on 500MPa base metals.
ER60-G
ER90S-G
Suitable for welding 600MPa high strength steel structures, such as construction machinery, pipelines, ships, pressure vessels, etc.
ER60-G
ER90S-G
Suitable for welding 600MPa high strength steel structures, such as construction machinery, etc.
ER70-G
ER100S-G
Suitable for welding 700MPa high strength steel structures, such as construction machinery, hoisting machinery, bridges, pipelines, ships, pressure vessels, etc.
ER80-G
ER110S-G
DC+
Suitable for welding high strength structures with tensile strength of 790MPa. It can be used for welding some key structures, such as pressure vessels, construction machinery, hoisting machinery, ships, mining machinery, etc.
ER55-G
DC+
welding filler wire ER70S-6/sg2
MIG CO2 WELDING WIRE SG2
1.Copper coated welding wire
2.Dia:0.8mm-1.6mm
3.Packing:5Kg,15Kg,250Kg
4.ISO9001:2000
welding wire
sg2 ER70S-6/
Mig welding wire/CO2 welding wire
Specification:
1)Size: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
2)Application: Suitable to single or multiple weld welding of carbon steel and low alloy steel with strength grade of 500MPa (e.g. the welding of vehicle, bridge, construction, and mechanical structure etc), also applicable to high speed welding of thin plates and pipes etc.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
/
1.Copper coated welding wire
2.Dia:0.8mm-1.6mm
3.Packing:5Kg,15Kg,250Kg
4.ISO9001:2000
welding wire
sg2 ER70S-6/
Mig welding wire/CO2 welding wire
Specification:
1)Size: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
2)Application: Suitable to single or multiple weld welding of carbon steel and low alloy steel with strength grade of 500MPa (e.g. the welding of vehicle, bridge, construction, and mechanical structure etc), also applicable to high speed welding of thin plates and pipes etc.
Feature:
1. stable arc
2. low splashing
3. high deposited effeciency
4. suitable for all position
Packing:
net weight_1kg, 5kg, 15kg
precision layer wound on plastic spool, each spool in a box, then boxes on wooden pallets.
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Application:
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Conform with:
GB/T ER50-6 DIN SG2 JIS YGW12
AWS ER70S-6 BS A18 EN G3Si1
Wire Size
Spool Size
Net Weight
0.8mm
1.0mm
1.2mm
1.6mm
D100mm D200mm
D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition
of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties
or
Deposited Metal
Yield strengthσ0.2(Mpa)
Tensile strengthσb(Mpa)
Elongationδ5(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
/
welding filler wire e71t-1
welding filler wire
RD-YJ502(Q) AWS A5.20 E71T-1
1.2mm-1.4mm-1.6mm 100%CO2
approved by ABS BV CCS DNV GL LR KR
15kg/spooL
Flux-cored wires for Mild Stee
Gas-Shielded Arc Welding Wires for Hardfacing
Flux-cored Wires for Low Temperature Service Steel
Flux-Cored wires for Corrosion Resistance Steel
Flux-cored Wires for Heat resistance Steel
Flux-cored Wires With High tensile and High toughness
RD-YJ502(Q) AWS A5.20 E71T-1
1.2mm-1.4mm-1.6mm 100%CO2
approved by ABS BV CCS DNV GL LR KR
15kg/spooL
Flux-cored wires for Mild Stee
Gas-Shielded Arc Welding Wires for Hardfacing
Flux-cored Wires for Low Temperature Service Steel
Flux-Cored wires for Corrosion Resistance Steel
Flux-cored Wires for Heat resistance Steel
Flux-cored Wires With High tensile and High toughness
welding filler wire
welding filler wire
RD-YJ502(Q) AWS A5.20 E71T-1
1.2mm-1.4mm-1.6mm 100%CO2
approved by ABS BV CCS DNV GL LR KR
15kg/spooL
Flux-cored wires for Mild Stee
Gas-Shielded Arc Welding Wires for Hardfacing
Flux-cored Wires for Low Temperature Service Steel
Flux-Cored wires for Corrosion Resistance Steel
Flux-cored Wires for Heat resistance Steel
Flux-cored Wires With High tensile and High toughness
RD-YJ502(Q) AWS A5.20 E71T-1
1.2mm-1.4mm-1.6mm 100%CO2
approved by ABS BV CCS DNV GL LR KR
15kg/spooL
Flux-cored wires for Mild Stee
Gas-Shielded Arc Welding Wires for Hardfacing
Flux-cored Wires for Low Temperature Service Steel
Flux-Cored wires for Corrosion Resistance Steel
Flux-cored Wires for Heat resistance Steel
Flux-cored Wires With High tensile and High toughness