CO2 gas shielded welding wire, which is made of excellent steel by drawing, straightening and copper coating.
In accordance with GB ER50-6 Equivalent to AWS ER70S-6
The product is a CO2 gas shielded welding wire, which is made of excellent steel by drawing, straightening and copper coating .It has various characteristic such as open arc, slag-free, good weld ability, high efficiency, beautiful bead, little spatter. It can not be welded in all positions. The product has high precision size. It is winded in spool,so that it can be welded automatically or semiautomatically.
Application:
Used for welding low carbon steel and low alloy steel structures, especially for welding of thin plates.
Chemical composition of the deposited weld metal (%)
C
Mn
Si
Cr
Ni
Cu
P
S
≤0.11
1.80-2.10
0.65-0.95
≤0.2
≤0.3
≤0.35
≤0.03
≤0.03
Typical mechanical properties of the deposited weld metal :
Tensile Strength
Yield point
Elongation
Charpy Vlmpacl Value
Mpa
Mpa
(Kgf/m)
(Kgf/m)
%
Room tempe/temperature
≥490
≥372
≥20
≥47
Wire size and Recommended currents:
Diameter(mm)
0.80
1.00
1.2
1.60
Length(mm)
50-100
70-120
90-220
140-300
recommended current(A)
18-21
18-22
19-23
24-28
Tuesday, October 4, 2011
Monday, October 3, 2011
(DIA 0.8 0.9 1.0 1.2 1.6 2.0) Welding wire ER70S-6 (CE Approval)
DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 (CE approval)
1.Gas-shielded Welding Wire
2.DIN SG2 AWS ER70S-6
DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 15KG/SPOOL CE APPROVAL
WELDING WIRE,mig welding wire,co2 welding wire solid welding wire
Gas shielded welding wire/Flux cored welding wire
WELDING WIRES ELECTRODES
Detailed Product Description Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000
WELDING POSITION :
CONTACT WITH Ms Alice
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
1.Gas-shielded Welding Wire
2.DIN SG2 AWS ER70S-6
DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 15KG/SPOOL CE APPROVAL
WELDING WIRE,mig welding wire,co2 welding wire solid welding wire
Gas shielded welding wire/Flux cored welding wire
WELDING WIRES ELECTRODES
Detailed Product Description Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000
WELDING POSITION :
CONTACT WITH Ms Alice
CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20
1.2MM Mig welding wire E71T-1
Flux cored Welding wire (E71T-1):
1.all position capability
2.good slag removable
3.Dia :1.2mm,1.4mm,1.6mm
4.packing:15Kg
FLUX Welding wire (ET71-1)/FCAW WIRE
E71T-1 is an all-position, flux cored welding wire, which is intended for single and multiple pass welding of low-alloy and carbon steel where a minimum 70,000 psi tensile strength is required. It is an excellent general purpose welding wire. A shielding gas must be used with this wire.
Typical Applications
General-purpose flux cored welding of steel
Structural steel
Farm machinery
Construction equipment
General carbon steel fabrication
AWS Specification
AWS A5.20
AWS Classification
E71T-1
Welding Current
DCEP (Electrode Positive, Reverse Polarity)
Typical Wire Chemistry
C 0.05
Si 0.74
Mn 1.00
P 0.008
S 0.015
Typical Mechanical Properties (As Welded)
Yield Strength, psi 71,000
Tensile Strength, psi 82,800
% Elongation in 2" 25
Welding Positions
All positions
Shielding Gas
100% CO
2
or 75% Ar / 25% CO
2
mix
Available Diameters
.035”, .045”, .052”, & 1/16”
Operating Range In Amps
.030” 40 –100
.035” 100 – 130
.052” 140 – 180
1/16” 175 – 300
1.all position capability
2.good slag removable
3.Dia :1.2mm,1.4mm,1.6mm
4.packing:15Kg
FLUX Welding wire (ET71-1)/FCAW WIRE
E71T-1 is an all-position, flux cored welding wire, which is intended for single and multiple pass welding of low-alloy and carbon steel where a minimum 70,000 psi tensile strength is required. It is an excellent general purpose welding wire. A shielding gas must be used with this wire.
Typical Applications
General-purpose flux cored welding of steel
Structural steel
Farm machinery
Construction equipment
General carbon steel fabrication
AWS Specification
AWS A5.20
AWS Classification
E71T-1
Welding Current
DCEP (Electrode Positive, Reverse Polarity)
Typical Wire Chemistry
C 0.05
Si 0.74
Mn 1.00
P 0.008
S 0.015
Typical Mechanical Properties (As Welded)
Yield Strength, psi 71,000
Tensile Strength, psi 82,800
% Elongation in 2" 25
Welding Positions
All positions
Shielding Gas
100% CO
2
or 75% Ar / 25% CO
2
mix
Available Diameters
.035”, .045”, .052”, & 1/16”
Operating Range In Amps
.030” 40 –100
.035” 100 – 130
.052” 140 – 180
1/16” 175 – 300
CO2 Gas Shielded Welding Wire 0.1mm-8mm
CO2 Gas Shielded Welding Wire
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO CERT
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
≤0.08
≤1.00
0.5-2.50
≤0.40
≤0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72
Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
≥550
≥35
--
390
570
41
39
Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO CERT
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
≤0.08
≤1.00
0.5-2.50
≤0.40
≤0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72
Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
≥550
≥35
--
390
570
41
39
Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A
welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
CO2 Gas Shielded Welding Wire 0.1mm-8mm
CO2 Gas Shielded Welding Wire
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
<=0.08
<=1.00
0.5-2.50
<=0.40
<=0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72
Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
>=550
>=35
--
390
570
41
39
Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
<=0.08
<=1.00
0.5-2.50
<=0.40
<=0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72
Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
>=550
>=35
--
390
570
41
39
Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A
welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
welding wire
welding wire ER70S-7
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
CO2 Gas Shielded Welding Wire ER70S-6
CO2 Gas Shielded Welding Wire
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO CERT
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
≤0.08
≤1.00
0.5-2.50
≤0.40
≤0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72
Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
≥550
≥35
--
390
570
41
39
Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO CERT
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
≤0.08
≤1.00
0.5-2.50
≤0.40
≤0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72
Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
≥550
≥35
--
390
570
41
39
Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A
welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
welding wire
welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550
CO2 Gas Shielded Welding Wire ER70S-6
Welding Wire AWS E70S-6:
1) 31 years history.
2) Quality approved by CE, ABS, CCS, BV, DNV, GL, LR.
3) Competitive Price.
Description: ER70S-6 is a copper carbon steel and low alloy steel welding wire, with the good hot metal mobility and the good resisting cracking quality. The components Mn and Si can stop stomas and slag, promote the resisting cracking quality and is helpful to get the good mechanical quality.
Application:Chemical composition of ER50-6 (AWS ER70S-6) :
C
Mn
Si
P
S
Cu
0.060.15
1.40---1.85
0.801.15
≤0.025
≤0.035
≤0.50
Mechanical properties of deposited metal
Type Name
GB
Equal
Tensile Strength (MPa)
Yield Strength (Mpa )
Elongation
(%)
Impact value
(J)
Tempature
ER 50-6
ER 50-6
AWS ER70S-6
≥500
≥420
≥22
≥27
-29
Diameter and reference current:
Diameter(mm)
Φ0.8
Φ1.0
Φ1.2
Φ1.6
Welding current(A)
40-140
50-220
80-350
170-550
Packaging & Delivery
Packaging Detail:
5kg, 15kg/spool
Delivery Detail
15 Days
1) 31 years history.
2) Quality approved by CE, ABS, CCS, BV, DNV, GL, LR.
3) Competitive Price.
Description: ER70S-6 is a copper carbon steel and low alloy steel welding wire, with the good hot metal mobility and the good resisting cracking quality. The components Mn and Si can stop stomas and slag, promote the resisting cracking quality and is helpful to get the good mechanical quality.
Application:Chemical composition of ER50-6 (AWS ER70S-6) :
C
Mn
Si
P
S
Cu
0.060.15
1.40---1.85
0.801.15
≤0.025
≤0.035
≤0.50
Mechanical properties of deposited metal
Type Name
GB
Equal
Tensile Strength (MPa)
Yield Strength (Mpa )
Elongation
(%)
Impact value
(J)
Tempature
ER 50-6
ER 50-6
AWS ER70S-6
≥500
≥420
≥22
≥27
-29
Diameter and reference current:
Diameter(mm)
Φ0.8
Φ1.0
Φ1.2
Φ1.6
Welding current(A)
40-140
50-220
80-350
170-550
Packaging & Delivery
Packaging Detail:
5kg, 15kg/spool
Delivery Detail
15 Days
welding Material ER49-1
ER49-1 welding wire
For welding low carbon steel and some low alloy steel structures
Description
ER49-1 a kind of mild steel copper coated welding wire with excellent welding properties and the welding seams have very high impact resistance at low temperature.
Application
ER49 welding wire is Used to weld ship building steel(A32E32D32A36E36D36) and mild steel products with strength at 490N/mm2 degree,such as mild alloy steel 16Mn15Mn ect to produce furnace,tubes for vessel,container building etc.
Conform with
GB/T
ER49-1 H08Mn2SiA
Appoved by CCS,ABS,LR
For welding low carbon steel and some low alloy steel structures
Description
ER49-1 a kind of mild steel copper coated welding wire with excellent welding properties and the welding seams have very high impact resistance at low temperature.
Application
ER49 welding wire is Used to weld ship building steel(A32E32D32A36E36D36) and mild steel products with strength at 490N/mm2 degree,such as mild alloy steel 16Mn15Mn ect to produce furnace,tubes for vessel,container building etc.
Conform with
GB/T
ER49-1 H08Mn2SiA
Appoved by CCS,ABS,LR
welding alloy
welding alloy
1)welding high temperature
2)in the market for years
welding alloy
You can have a look at below. Any questions, please let me know.
C
Cr
Ni
W
Mo
Al
Ti
Fe
Mn
Si
P
S
Cu
rest
HGH1035
0.060.12
20.023.0
35.040.0
2.503.50
≤0.50
0.700.12
≤0.70
≤0.80
≤0.020
≤0.020
≤0.20
Ce≤0.05
HGH1040
≤0.10
15.017.5
24.027.0
5.507.00
1.002.00
0.501.00
≤0.030
≤0.020
≤0.20
N:0.100.20
HGH1068
≤0.10
14.016.0
21.023.0
7.008.00
2.003.00
5.006.00
≤0.20
≤0.010
≤0.010
Ce≤0.02
HGH1131
≤0.10
19.022.0
25.030.0
4.86.00
2.803.50
≤0.12
≤0.80
≤0.020
≤0.020
Nb:0.71.3 N:0.150.30 B:≤0.005
HGH1139
≤0.12
23.026.0
14.018.0
5.007.00
≤1.00
≤0.030
≤0.025
≤0.20
N:0.250.45 B:≤0.01
HGH1140
0.060.12
20.023.0
35.040.0
1.401.80
2.002.50
0.200.60
0.701.20
≤0.70
≤0.80
≤0.020
≤0.015
HGH2036
0.340.40
11.513.5
7.09.0
1.101.40
≤0.12
7.509.50
0.300.80
≤0.035
≤0.030
Nb:0.250.50 V:1.251.55
HGH2038
≤0.10
10.012.5
18.021.0
≤0.50
2.302.80
≤1.00
≤1.00
≤0.030
≤0.020
≤0.20
B:≤0.008
HGH2042
≤0.05
11.513.0
34.536.5
0.901.20
2.703.20
0.801.30
≤0.60
≤0.020
≤0.020
≤0.20
HGH2132
≤0.08
10.012.5
18.021.0
≤0.35
1.752.35
1.002.00
0.401.00
≤0.020
≤0.015
V:0.100.50 B:0.0010.010
HGH2135
≤0.06
14.016.0
33.036.0
1.702.20
1.702.20
2.402.80
2.102.50
≤0.40
≤0.50
≤0.035
≤0.030
B:≤0.015 Ce≤0.003
HGH3030
≤0.12
19.022.0
rest
≤0.12
2.302.80
≤0.70
≤0.80
≤0.015
≤0.010
≤0.20
HGH3039
≤0.08
19.022.0
rest
1.802.30
0.350.75
0.350.75
≤3.0
≤0.40
≤0.80
≤0.020
≤0.012
≤0.20
Nb:0.901.30
HGH3041
≤0.25
20.023.0
72.078.0
≤0.06
≤1.7
≤0.201.50
≤0.60
≤0.035
≤0.030
≤0.20
HGH3044
≤0.10
23.526.5
rest
13.016.0
≤0.50
0.300.70
≤4.0
≤0.50
≤0.80
≤0.013
≤0.013
≤0.20
HGH3113
≤0.08
14.516.5
rest
3.004.00
15.017.0
4.0-7.0
≤1.00
≤1.00
≤0.015
≤0.015
≤0.20
V:≤0.35
HGH3128
≤0.05
19.022.0
rest
7.509.00
7.509.00
0.400.80
0.400.80
≤2.0
≤0.50
≤0.80
≤0.013
≤0.013
≤0.013
B:≤0.005 Zr:≤0.06 Ce:≤0.05
HGH4033
≤0.06
19.022.0
rest
0.601.00
2.402.80
≤1.0
≤0.35
≤0.65
≤0.015
≤0.007
≤0.007
B:≤0.001 Ce:≤0.001
HGH4145
≤0.08
14.017.0
rest
0.401.00
2.252.75
5.0-9.0
≤1.00
≤0.50
≤0.020
≤0.010
≤0.20
Nb:0.701.20
HGH4169
≤0.08
17.021.0
50.055.0
2.83.3
0.200.60
0.651.15
≤0.30
≤0.015
≤0.015
Nb:4.755.50 B:≤0.006
1)welding high temperature
2)in the market for years
welding alloy
You can have a look at below. Any questions, please let me know.
C
Cr
Ni
W
Mo
Al
Ti
Fe
Mn
Si
P
S
Cu
rest
HGH1035
0.060.12
20.023.0
35.040.0
2.503.50
≤0.50
0.700.12
≤0.70
≤0.80
≤0.020
≤0.020
≤0.20
Ce≤0.05
HGH1040
≤0.10
15.017.5
24.027.0
5.507.00
1.002.00
0.501.00
≤0.030
≤0.020
≤0.20
N:0.100.20
HGH1068
≤0.10
14.016.0
21.023.0
7.008.00
2.003.00
5.006.00
≤0.20
≤0.010
≤0.010
Ce≤0.02
HGH1131
≤0.10
19.022.0
25.030.0
4.86.00
2.803.50
≤0.12
≤0.80
≤0.020
≤0.020
Nb:0.71.3 N:0.150.30 B:≤0.005
HGH1139
≤0.12
23.026.0
14.018.0
5.007.00
≤1.00
≤0.030
≤0.025
≤0.20
N:0.250.45 B:≤0.01
HGH1140
0.060.12
20.023.0
35.040.0
1.401.80
2.002.50
0.200.60
0.701.20
≤0.70
≤0.80
≤0.020
≤0.015
HGH2036
0.340.40
11.513.5
7.09.0
1.101.40
≤0.12
7.509.50
0.300.80
≤0.035
≤0.030
Nb:0.250.50 V:1.251.55
HGH2038
≤0.10
10.012.5
18.021.0
≤0.50
2.302.80
≤1.00
≤1.00
≤0.030
≤0.020
≤0.20
B:≤0.008
HGH2042
≤0.05
11.513.0
34.536.5
0.901.20
2.703.20
0.801.30
≤0.60
≤0.020
≤0.020
≤0.20
HGH2132
≤0.08
10.012.5
18.021.0
≤0.35
1.752.35
1.002.00
0.401.00
≤0.020
≤0.015
V:0.100.50 B:0.0010.010
HGH2135
≤0.06
14.016.0
33.036.0
1.702.20
1.702.20
2.402.80
2.102.50
≤0.40
≤0.50
≤0.035
≤0.030
B:≤0.015 Ce≤0.003
HGH3030
≤0.12
19.022.0
rest
≤0.12
2.302.80
≤0.70
≤0.80
≤0.015
≤0.010
≤0.20
HGH3039
≤0.08
19.022.0
rest
1.802.30
0.350.75
0.350.75
≤3.0
≤0.40
≤0.80
≤0.020
≤0.012
≤0.20
Nb:0.901.30
HGH3041
≤0.25
20.023.0
72.078.0
≤0.06
≤1.7
≤0.201.50
≤0.60
≤0.035
≤0.030
≤0.20
HGH3044
≤0.10
23.526.5
rest
13.016.0
≤0.50
0.300.70
≤4.0
≤0.50
≤0.80
≤0.013
≤0.013
≤0.20
HGH3113
≤0.08
14.516.5
rest
3.004.00
15.017.0
4.0-7.0
≤1.00
≤1.00
≤0.015
≤0.015
≤0.20
V:≤0.35
HGH3128
≤0.05
19.022.0
rest
7.509.00
7.509.00
0.400.80
0.400.80
≤2.0
≤0.50
≤0.80
≤0.013
≤0.013
≤0.013
B:≤0.005 Zr:≤0.06 Ce:≤0.05
HGH4033
≤0.06
19.022.0
rest
0.601.00
2.402.80
≤1.0
≤0.35
≤0.65
≤0.015
≤0.007
≤0.007
B:≤0.001 Ce:≤0.001
HGH4145
≤0.08
14.017.0
rest
0.401.00
2.252.75
5.0-9.0
≤1.00
≤0.50
≤0.020
≤0.010
≤0.20
Nb:0.701.20
HGH4169
≤0.08
17.021.0
50.055.0
2.83.3
0.200.60
0.651.15
≤0.30
≤0.015
≤0.015
Nb:4.755.50 B:≤0.006
welding and MIG torch/ tips
Welding Wires AWS 5.18 ER70S-6
WELDING WIRE Size: 0.8mm/1.0mm/1.2mm/1.6mm..
Certificate:ABS,SGS,EWC,AOV,LR,TUV,DB,GL
WELDING WIRE AWS 5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4. 0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5. 15kg, 20kg iron spool layer wind
6. 100kg, 250kg, 350kg drum packing
7,welding torch:
WELDING WIRE Size: 0.8mm/1.0mm/1.2mm/1.6mm..
Certificate:ABS,SGS,EWC,AOV,LR,TUV,DB,GL
WELDING WIRE AWS 5.18 ER70S-6 is a kind of mild steel copper coated welding wire, suitable for 100% CO2 and Argon& CO2 mixed gas protective welding with stable feasibility, good welding seams, less spatters and excellent welding process properties.
2,Used to weld ship building steel(A,B,D,E,A36,D36,E36)and equivalent mild steel or 550Mpa grade mild alloy steel, such as container building, construction machine, railway construction, pressure vessel for semi-auto or automatic gas shielded welding.
3,
Packaging
Wire Size
Spool Size
Net Weight
φ0.8~1.6(mm)
D100mm D200mm D270mm D300mm K300mm
1kg,5kg,15kg,18kg,20kg
chemical composition of welding wire(%)
C
Mn
Si
P
S
Cr
Ni
Cu
0.06~0.15
1.40~1.85
0.80~1.15
≤0.025
≤0.035
-
-
≤0.50
Mechanical Properties or Deposited Metal
Yield strengthσ
0.2
(Mpa)
Tensile strengthσ
b
(Mpa)
Elongationδ
5
(%)
AKV impact(J)
≥420
≥500
≥22
≥27(-29)
Wire Size(mm)
φ0.8
φ1.0
φ1.2
φ1.6
Welding position
Welding current(A)
40~140
50~220
80~350
120~550
Please be noted
Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts
4. 0.9kg, 4.5kg, 5kg, 15kg, 20kg, 27kg plastic spool layer wind
5. 15kg, 20kg iron spool layer wind
6. 100kg, 250kg, 350kg drum packing
7,welding torch:
welding cable PVC insulation CCA COPPER conductor
weld
best price
best quality
short time delivery
welding cable PVC insulation CCA COPPER conductor
Application :
The cables are suitable for use in household electrical appliances , tools ,movable appliances and power distribution network for rated voltage 450 750 V AC and below
best price
best quality
short time delivery
welding cable PVC insulation CCA COPPER conductor
Application :
The cables are suitable for use in household electrical appliances , tools ,movable appliances and power distribution network for rated voltage 450 750 V AC and below
welding cable double PVC insulation 16 MM2
welding cable double PVC insulation
good quality
short time delivery
welding cable double PVC insulation
orange colour
plain annealed copper wire conductor
double pvc sheath
cross section 16.1 MM2
good quality
short time delivery
welding cable double PVC insulation
orange colour
plain annealed copper wire conductor
double pvc sheath
cross section 16.1 MM2
welding cable35mm2 70mm2 95mm2
welding cable
1 it is approved by ISO,CCC,CB,CE,RoHS
2 jacket:PVC,rubber for option
3 conductor:copper,CCA for option
welding cable
1 also named welding cable/rubber welding cable/electrical welding cable/welding machine cable
2 Welder apply to the secondary side wiring and connecting welding clamp dedicated cables, the exchange does not exceed the rated voltage 200 V DC and pulse of 400 V peak.
3 Single core structure, a multi-unit complex cutter made of soft wire. Conductive wire core heat-resistant polyester film used outside insulation wrap packages, with the outermost layer of insulation made of rubber sheathing as a protective layer.
Instruction
Cables are suitable for the secondary side voltage exchange does not exceed 200 V and 400 V peak pulsating DC welding machine with secondary side wiring and connecting welding clamp purposes. Cable allows long-term temperature: ≤ +65
Type:
Type
Name
YH
Welder natural rubber sheathing cables
YHF
Chloroprene or elastomer sheathe cable welder
Cable main technical performance
section
Core structure cores/mm
20 conductive wire core DC resistance Ω/km
No Tinning
Tinning
10
322/0.20
≤1.19
≤1.95
16
513/0.20
≤1.16
≤1.19
25
798/0.20
≤0.758
≤0.780
35
1121/0.20
≤0.536
≤0.552
50
1596/0.20
≤0.346
≤0.390
70
2214/0.20
≤0.268
≤0.276
95
2997/0.20
≤0.198
≤0.204
120
3702/.0.20
≤0.161
≤0.164
Note: Finished drills immersion in water 1 hour at room temperature, withstood 50Hz, 200V AC voltage of 5 min no breakdown.
1 it is approved by ISO,CCC,CB,CE,RoHS
2 jacket:PVC,rubber for option
3 conductor:copper,CCA for option
welding cable
1 also named welding cable/rubber welding cable/electrical welding cable/welding machine cable
2 Welder apply to the secondary side wiring and connecting welding clamp dedicated cables, the exchange does not exceed the rated voltage 200 V DC and pulse of 400 V peak.
3 Single core structure, a multi-unit complex cutter made of soft wire. Conductive wire core heat-resistant polyester film used outside insulation wrap packages, with the outermost layer of insulation made of rubber sheathing as a protective layer.
Instruction
Cables are suitable for the secondary side voltage exchange does not exceed 200 V and 400 V peak pulsating DC welding machine with secondary side wiring and connecting welding clamp purposes. Cable allows long-term temperature: ≤ +65
Type:
Type
Name
YH
Welder natural rubber sheathing cables
YHF
Chloroprene or elastomer sheathe cable welder
Cable main technical performance
section
Core structure cores/mm
20 conductive wire core DC resistance Ω/km
No Tinning
Tinning
10
322/0.20
≤1.19
≤1.95
16
513/0.20
≤1.16
≤1.19
25
798/0.20
≤0.758
≤0.780
35
1121/0.20
≤0.536
≤0.552
50
1596/0.20
≤0.346
≤0.390
70
2214/0.20
≤0.268
≤0.276
95
2997/0.20
≤0.198
≤0.204
120
3702/.0.20
≤0.161
≤0.164
Note: Finished drills immersion in water 1 hour at room temperature, withstood 50Hz, 200V AC voltage of 5 min no breakdown.
Subscribe to:
Posts (Atom)