"Uniflower" Welding wires

CO2 gas shielded welding wire, which is made of excellent steel by drawing, straightening and copper coating.
In accordance with GB ER50-6 Equivalent to AWS ER70S-6

The product is a CO2 gas shielded welding wire, which is made of excellent steel by drawing, straightening and copper coating .It has various characteristic such as open arc, slag-free, good weld ability, high efficiency, beautiful bead, little spatter. It can not be welded in all positions. The product has high precision size. It is winded in spool,so that it can be welded automatically or semiautomatically.
Application:
Used for welding low carbon steel and low alloy steel structures, especially for welding of thin plates.
Chemical composition of the deposited weld metal (%)
C
Mn
Si
Cr
Ni
Cu
P
S
≤0.11
1.80-2.10
0.65-0.95
≤0.2
≤0.3
≤0.35
≤0.03
≤0.03
Typical mechanical properties of the deposited weld metal :
Tensile Strength
Yield point
Elongation
Charpy Vlmpacl Value
Mpa
Mpa


(Kgf/m)
(Kgf/m)
%
Room tempe/temperature
≥490
≥372
≥20
≥47
Wire size and Recommended currents:
Diameter(mm)
0.80
1.00
1.2
1.60
Length(mm)
50-100
70-120
90-220
140-300
recommended current(A)
18-21
18-22
19-23
24-28

(DIA 0.8 0.9 1.0 1.2 1.6 2.0) Welding wire ER70S-6 (CE Approval)

DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 (CE approval)
1.Gas-shielded Welding Wire
2.DIN SG2 AWS ER70S-6
DIA 0.8 0.9 1.0 1.2 1.6 2.0mm Welding wire ER70S-6 15KG/SPOOL CE APPROVAL
WELDING WIRE,mig welding wire,co2 welding wire solid welding wire
Gas shielded welding wire/Flux cored welding wire
WELDING WIRES ELECTRODES

Detailed Product Description Material:CO2 Gas Shielded Welding Wire (AWS ER70S-6) is made from excellent Ho8Mn2SiA steel by drawing, straightening and copper coating..
Features: Stable electric arc, low splashing, high deposition efficiency and good anti pore property, It can be welded automatically or semi-automatical.
Application: low carbon steel and low alloy steel, rolling stock, container, engineering machinery, and pressure container, etc.
Specification: 0.8mm, 0.9mm, 1.0mm, 1.2mm, 1.6mm
Packing : 10kg, 15kg or 20kg packed in pallet
Certificate:ISO 9001 :2000
WELDING POSITION :

CONTACT WITH Ms Alice

CO2 GAS SHIELDED WELDING WIRE
Type
China National Standard (GB)
International
Standard
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
ER50-6
ER50-6
AWS ER70S-6
0.06-0.15
1.40-1.85
0.80-1.15
≤0.035
≤0.025
≤0.50
Mechanical Properties of Deposited Metal
Tensile Strength Mpa
Yield Strength
Mpa
Elongation
%
Temperature
TensileNum KAV
≥500
≥420
≥22
-29°C
≥27
Specifications /Reference Electric Current and Voltdge Packing Weight
Diameter
0.8
0.9
1.0
1.2
1.6
Current
40 - 140
50 - 200
70 - 250
80 - 350
170 - 450
Voltage
16 - 21
17 - 25
17 - 27
18 - 30
23 - 43
Weight(Kg)
5/15/20
5/15/20
5/15/20
5/15/20
5/15/20

1.2MM Mig welding wire E71T-1

Flux cored Welding wire (E71T-1):
1.all position capability
2.good slag removable
3.Dia :1.2mm,1.4mm,1.6mm
4.packing:15Kg
FLUX Welding wire (ET71-1)/FCAW WIRE

E71T-1 is an all-position, flux cored welding wire, which is intended for single and multiple pass welding of low-alloy and carbon steel where a minimum 70,000 psi tensile strength is required. It is an excellent general purpose welding wire. A shielding gas must be used with this wire.
Typical Applications
General-purpose flux cored welding of steel
Structural steel
Farm machinery
Construction equipment
General carbon steel fabrication
AWS Specification

AWS A5.20
AWS Classification

E71T-1
Welding Current
DCEP (Electrode Positive, Reverse Polarity)
Typical Wire Chemistry
C 0.05
Si 0.74
Mn 1.00
P 0.008
S 0.015
Typical Mechanical Properties (As Welded)
Yield Strength, psi 71,000
Tensile Strength, psi 82,800
% Elongation in 2" 25
Welding Positions
All positions
Shielding Gas

100% CO
2
or 75% Ar / 25% CO
2
mix
Available Diameters
.035”, .045”, .052”, & 1/16”
Operating Range In Amps
.030” 40 –100
.035” 100 – 130
.052” 140 – 180
1/16” 175 – 300

CO2 Gas Shielded Welding Wire 0.1mm-8mm

CO2 Gas Shielded Welding Wire
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO CERT
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)
Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
≤0.08
≤1.00
0.5-2.50
≤0.40
≤0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72

Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
≥550
≥35
--
390
570
41
39

Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A

welding wire

welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550

welding wire

welding wire ER70S-6
1 stable arc
2 low splashing
3 high deposited effeciency
4 suitable for all position...
1.Diameter: 0.6-1.6mm;
2.Packing: 25kgs spools,250 drum;
3.good quality and best price
CO2 gas-shielded flux cored welding wire
E71T-1 welding wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.
At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,
1. Low welding costs.
2. High productivity and low electricity consumption.
3. Easy to operate. All-position welding.
4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.
5. Little deformation after welding.
6. Wide applicability. Suitable for welding thin, medium and thick plates.
Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.
Uses: 1. Used for welding all kinds of 500MPa structural steel parts.
2.Used for welding all kinds of 500MPa plates and pipes.
Chemical Composition of Welding Wire(%)
C
Mn
Si
S
P
Cu
0.06~0.15
1.4~1.85
0.8~1.15
≤0.035
≤0.025
≤0.50
Examples of Chemical Composition of Deposited Metal (%)
C
Mn
Si
S
P
Cu
0.07
1.27
0.76
0.014
0.015
0.15
Mechanical Properties of Deposited Metal
Test Item
Rm(MPa)
ReLRp0.2(Mpa)
A(%)
KV2(J)
Guarantee Value
≥500
≥420
≥22
≥27(-30)
General Result
558
472
27
98
Reference Current (DC+)
Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min)
φ0.8 50~100 15
φ1.0 50~220 15~20
φ1.2 80~350 15~25
φ1.6 170~550

CO2 Gas Shielded Welding Wire 0.1mm-8mm

CO2 Gas Shielded Welding Wire
1,Dia:0.8mm, 1.0mm, 1.2mm
2,Packing:15kg/spool
3,Excellent quality, lowest price
4,ISO
1.Manufacturer on our own.
2.Smooth appearance
3.LR,GL,ABS,CCS,NK,BV,KR,IRNA,DNV.
CO2 Gas Shielded Welding Wire SPecification:
It is suitable for downhand welding and horizontal position welding.
Shielding Gas:CO2 or Ar+CO2
Polarity:DC:wire(+)

Typical Chemical Composition of Deposited Metal(%)
C
Si
Mn
P
S
Ni
Cr
<=0.08
<=1.00
0.5-2.50
<=0.40
<=0.030
9.00-11.00
18.00-21.00
0.050
0.57
1.52
0.020
0.009
9.68
19.72

Typical Mechanical Properties of Deposited Metal
Yield Strength(Mpa)
Tensile(Mpa)
Elongation(%)
Charpy V-notch Impact Energy 0°C(J)
--
>=550
>=35
--
390
570
41
39

Size and Recommend Current Range
Wire Dia(mm)
0.9
1.2
1.6
F,HF
80~150A
130~270A
190~340A
H
90~130A
150~220A
220~270A